Rhinestone piece and preparation method thereof

A technology of rhinestones and antioxidants, applied in the field of decorative product raw materials, can solve the problems of poor dimensional stability, loss, hot beads, hot drills or hot stamping scraps, etc., to improve stability performance, improve antioxidant performance, and improve dimensional stability. Effects of Sexuality and Structural Strength

Inactive Publication Date: 2017-07-21
温州市隆昌塑料有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since hot beads, hot drills or iron sheets are placed on the rhinestone sheet, if the dimensional stability of the PVC rhinestone sheet is poor, the hot beads, hot drills or hot sheets placed on the rhinestone sheet will be scrapped, resulting in greater losses

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rhinestone piece and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A rhinestone sheet, comprising the following components in parts by weight:

[0043] 80 parts of polyvinyl chloride, 4 parts of MBS, 2 parts of methyl tin mercaptide, 1 part of lubricant, 5 parts of P201, 0.1 part of HMC-710, 5 parts of NSR-100, 0.5 parts of antioxidant, 0.1 part of stearic acid Calcium, 0.05 parts of ultramarine blue, 0.3 parts of bis(2-ethylhexyl) phthalate.

[0044] Wherein, the lubricant includes SG-16 and SG-70s, and according to the weight ratio, SG-16:SG-70s=8:3. The antioxidant includes antioxidant 1010 and antioxidant 168, and according to the weight ratio, antioxidant 1010:168=1:1.

[0045] A preparation method of a rhinestone sheet, comprising the following preparation steps:

[0046] Step 1: According to parts by weight, weigh 80 parts of polyvinyl chloride, 4 parts of MBS, 2 parts of methyl tin mercaptide, 1 part of lubricant, 5 parts of P201, 0.1 part of HMC-710, 5 parts of NSR-100, 0.5 parts Antioxidant, 0.1 part of calcium stearate, 0...

Embodiment 2

[0050] A rhinestone sheet, comprising the following components in parts by weight:

[0051] 70 parts of polyvinyl chloride, 1 part of MBS, 1 part of methyl tin mercaptide, 0.5 part of lubricant, 4 parts of P201, 0.05 part of HMC-710, 2 parts of NSR-100, 0.1 part of antioxidant, 0.2 part of stearic acid Calcium, 0.08 part of ultramarine blue, 0.1 part of bis(2-ethylhexyl) phthalate.

[0052] Wherein, the lubricant includes SG-16 and SG-70s, and according to the weight ratio, SG-16:SG-70s=8:3. The antioxidant includes antioxidant 1010 and antioxidant 168, and according to the weight ratio, antioxidant 1010:168=1:1.

[0053] A preparation method of a rhinestone sheet, comprising the following preparation steps:

[0054]Step 1: According to parts by weight, weigh 70 parts of polyvinyl chloride, 1 part of MBS, 1 part of methyl tin mercaptide, 0.5 part of lubricant, 4 parts of P201, 0.05 part of HMC-710, 2 parts of NSR-100, 0.1 part Antioxidant, 0.2 part of calcium stearate, 0.08...

Embodiment 3

[0058] A rhinestone sheet, comprising the following components in parts by weight:

[0059] 72 parts of polyvinyl chloride, 2 parts of MBS, 0.5 parts of methyl tin mercaptide, 0.75 parts of lubricant, 2 parts of P201, 0.07 parts of HMC-710, 3 parts of NSR-100, 0.2 parts of antioxidant, 0.4 parts of stearic acid Calcium, 0.1 part of ultramarine blue, 0.2 part of bis(2-ethylhexyl) phthalate.

[0060] Wherein, the lubricant includes SG-16 and SG-70s, and according to the weight ratio, SG-16:SG-70s=8:3. The antioxidant includes antioxidant 1010 and antioxidant 168, and according to the weight ratio, antioxidant 1010:168=1:1.

[0061] A preparation method of a rhinestone sheet, comprising the following preparation steps:

[0062] Step 1: According to parts by weight, weigh 72 parts of polyvinyl chloride, 2 parts of MBS, 0.5 parts of methyl tin mercaptide, 0.75 parts of lubricant, 2 parts of P201, 0.07 parts of HMC-710, 3 parts of NSR-100, 0.2 parts Antioxidant, 0.4 part of calci...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a rhinestone piece and preparation method thereof. The rhinestone piece comprises the following components in parts by weight: 70-80 parts of polyvinyl chloride, 1-4 parts of MBS, 0.5-2 parts of methyl tin mercaptide, 0.5-1.5 parts of a lubricant, 1-5 parts of processing additives, 0.05-0.1 part of an anti-sticking agent, 1-5 parts of a foaming regulator and 0.1-0.5 parts of an antioxidant, wherein the lubricant comprises SG-16 and SG-70s; a weight ratio of SG-16 to SG-70s is equal to 8: 3. The invention has the beneficial effect that the rhinestone piece has high dimensional stability, so as to avoid occurrence of scraping of beads placed on the rhinestone piece due to change in dimension of the rhinestone piece.

Description

technical field [0001] The invention relates to decorative product raw materials, in particular to a rhinestone sheet and a preparation method thereof. Background technique [0002] As a clothing accessory, hot stamping can increase the beauty of clothing and increase the value of clothing. Ironing diamonds, also known as rhinestones, are the main components of ironing pictures. [0003] The Chinese patent with the publication number CN101961969A discloses a method for sticking hot beads, hot drills and hot sheets. The method includes the following steps: stick hot beads, hot drills or hot sheets with an adhesive pen and place them on a sheet made of soft rubber materials such as PVC, PU, ​​silica gel, vinyl, etc., and then use silicone heat-fixing tape Stick the whole pattern of hot beads, hot drills or hot sheets that have been placed and paste them on the surface of the product that needs to be pasted with patterns, and use electric ironing or electric heating equipment...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L51/04C08L33/04C08K13/02C08K5/58C08K5/134C08K5/526
CPCC08L27/06C08L2203/14C08L2205/025C08L2205/035C08L51/04C08L33/04C08K13/02C08K5/58C08K5/1345C08K5/526
Inventor 张建胜唐元亮邹雪克
Owner 温州市隆昌塑料有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com