Method for preparing asphalt regenerating agent based on discarded tires

A technology of asphalt reclaimer and waste tires, which is applied in building components, building insulation materials, buildings, etc. It can solve the problems of inability to restore the properties of asphalt, low utilization rate of waste tires, and pollute the environment, so as to increase solubility and activity , Improve the effect of rapidity

Inactive Publication Date: 2017-07-21
雷春生
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention: Aiming at the problems that the utilization rate of waste tires is not high and pollutes the environment, at the same time, it is difficul

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0024] Example 1, preparation of asphalt regenerant

[0025] Firstly, take the waste tires and wash the surface, put them into the ring cutting machine for cutting, collect the cut waste tire rings, and put them into the cutting machine for cutting, set the cutting length to 8cm, and then cut the Put it into the jaw crusher for crushing, set the diameter of the discharge port to 15mm, collect the discharge material and put it into the ball mill, then add steel balls with a diameter of 50mm five times the discharge material, and ball mill at 800r / min to obtain particles The particle size is 0.15 mm, and the ball mill is collected to obtain waste tire particles; the rubber bark is stripped from a rubber tree with an age of 8 years, put into a pulverizer and crushed, and the 100-mesh sieve is passed to collect the sieved rubber bark particles, press In parts by weight, get 80 parts of distilled water, 35 parts of glucose, 25 parts of peptone, 21 parts of sieved rubber bark partic...

example 2

[0026] Example 2, preparation of asphalt regenerant

[0027]Firstly, take the waste tires and wash the surface, put them into the ring cutting machine for cutting, collect the cut waste tire rings, and put them into the cutting machine for cutting, set the cutting length to 6cm, and then cut the Put it into the jaw crusher for crushing, set the diameter of the discharge port to 10mm, collect the discharge material and put it into the ball mill, then add steel balls with a diameter of 3 times the discharge material and 50mm in diameter, and ball mill at 800r / min to obtain particles The particle size is 0.08mm, and the ball mill is collected to obtain waste tire particles; the rubber bark is stripped from a rubber tree with a age of 6 years, put into a pulverizer and crushed, and the 100-mesh sieve is passed to collect the sieved rubber bark particles, press In parts by weight, get 70 parts of distilled water, 30 parts of glucose, 22 parts of peptone, 19 parts of sieved rubber b...

example 3

[0028] Example 3, preparation of asphalt regenerant

[0029] Firstly, take the waste tires and wash the surface, put them into the ring cutting machine for cutting, collect the cut waste tire rings, and put them into the cutting machine for cutting, set the cutting length to 7cm, and then cut the Put it into the jaw crusher for crushing, set the diameter of the discharge port to 12mm, collect the discharge material and put it into the ball mill, then add steel balls with a diameter of 4 times the discharge material and 50mm in diameter, and ball mill at 800r / min to obtain particles The particle size is 0.10 mm, and the ball mill is collected to obtain waste tire particles; the rubber bark is stripped from a rubber tree with a age of 7 years, put into a pulverizer for crushing, and the 100-mesh sieve is passed to collect the sieved rubber bark particles, press In parts by weight, get 75 parts of distilled water, 32 parts of glucose, 24 parts of peptone, 20 parts of sieved rubbe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of road engineering materials and particularly relates to a method for preparing an asphalt regenerating agent based on discarded tires. The discarded tires are used as raw materials firstly and are processed to obtain discarded tire granules, then the discarded tire granules and a home-made biological fluid are put in a fermentation tank for fermentation, a fermentation mixture is obtained, then platinum tetrachloride is used as a catalyst, splitting decomposition is conducted on the fermentation mixture through high temperature and high pressure, a discharged substance is filtered, filtrate and amino cyclopropane carboxylic acid are mixed, distillation is performed to obtain a fraction, finally the fraction is mixed with sodium sulfamate and other substances, and the asphalt regenerating agent can be obtained. The discarded tires are used as raw materials, the cost is reduced, waste recycling is achieved, microbes in rubber barks are screen and cultured and then are filtered, a target culture solution is obtained and is used for conducting biological decomposition and modification on the discarded tire granules, the activity is increased, and further the rapidity of the asphalt regenerating agent permeating into an asphalt inside layer is improved.

Description

technical field [0001] The invention belongs to the technical field of road engineering materials, and in particular relates to a method for preparing asphalt regeneration agent from waste tires. Background technique [0002] With the rapid development of the automobile industry, the amount of waste tires is also increasing day by day. On the one hand, most waste tires cannot be recycled, and the utilization rate is very low, resulting in a serious waste of resources. On the other hand, the long-term exposed stacking of waste tires not only occupies a large amount of land, but also is prone to breeding mosquitoes and spreading diseases after being exposed to the sun and rain, and it is also easy to cause fires, causing serious environmental problems. Therefore, how to recycle waste tires and prevent them from polluting the environment is an outstanding problem that people are facing today. [0003] Asphalt rejuvenator refers to a kind of asphalt rejuvenator that needs to b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L95/00C08K5/435C08K5/17C08K5/32C08J11/28C08L19/00
CPCC08J11/28C08J2319/00C08K5/17C08K5/32C08K5/435C08L95/00Y02W30/62
Inventor 刘丹薛洋宋昊
Owner 雷春生
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap