Nesting type mosaic tile and preparing method thereof
A mosaic and nested technology, applied in the field of building decoration materials, can solve the problems of difficulty in ensuring the flatness of the mosaic wall, low mosaic pattern combination efficiency, and small mosaic size, etc., so as to improve the laying efficiency and flatness, reduce Paving difficulty, improving the effect of flatness
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0044] Figure 1 to Figure 4 Shown is the embodiment one of a kind of nested mosaic tile of the present invention, as figure 1 As shown, it is composed of a frame body 1 and an inner core 2; the size of the inner core 2 is the size of a mosaic monomer, and it is a square whose side length A2 is 52mm (see image 3 ); frame body 1 is a square whose side length A1 is 98mm, such as figure 2 As shown, there is a hollow space 1a matching the shape and size of the inner core, and the hollow space 1a is 13mm away from the edge of the frame body 1; the inner core 2 is embedded in the hollow space 1a of the frame body 1 (see figure 1 ).
[0045] The preparation method of above-mentioned nested type mosaic tile, its steps are as follows:
[0046] (1) Preparation of frame 1
[0047] The frame material is made of ceramic powder, the main component of which is SiO 2 65%~75%, Al 2 o 3 19%~24%, MgO 0.1%~0.4%, CaO 1%~11%, R 2 O 4%~7%, Fe 2 o 30.1% to 1.5%; use the middle mold core ...
Embodiment 2
[0054] Figure 5 , Figure 6 Shown is the embodiment two of a kind of nested mosaic tile of the present invention and preparation method thereof, differs from embodiment one in that:
[0055] (1) Both the inner core 2 and the frame body 1 are hexagonal, and the movable pressing mold is a hexagonal mold; the frame body 1 is composed of inner and outer layers nested in the direction of the plane (see Figure 5 ). The inner and outer two-layer frames 1 are respectively prepared by the step (1).
[0056] Such as Figure 5 As shown, the size L1×W1 of the outer frame 1 is 98×150 mm, and the inner angle α is 108°; the size L2×W2 of the inner frame 1 is 40×115 mm, and the inner angle α is 108°. The dimensions L3×W3 of the inner core 2 are 11.6×31.8 mm, and the inner angle α is 108°. Based on the short side, the distance from the left edge of the inner core 2 to the left edge of the inner frame 1 is 65 mm, and the distance from the edge of the inner frame to the edge of the outer ...
Embodiment 3
[0060] Figure 7 , Figure 8 Shown is a third embodiment of a nested mosaic tile of the present invention and its preparation method, which differs from embodiment one in that:
[0061] (1) Both the inner core 2 and the frame body 1 are fan-shaped, and the movable pressing mold is a fan-shaped mold.
[0062] Such as Figure 7 As shown, the size B1×H1 of the frame body 1 is 80×100 mm, and the size B2×H2 of the inner core 2 is 28×36 mm. The distance between the arc tangent of frame 1 and the handle of the small fan is 23mm, and the distance between the tangents of the fan is 23mm.
[0063] (2) The preparation of the inner core 2 in the step (2) is as follows: cutting the glass material according to requirements, and performing cold spray coloring on the obtained product to obtain the inner core 2 .
[0064] The nested mosaic tiles of this embodiment can be combined according to a certain pattern, such as Figure 8 As shown, a large-area mosaic pattern is formed.
PUM
| Property | Measurement | Unit |
|---|---|---|
| water absorption | aaaaa | aaaaa |
| water absorption | aaaaa | aaaaa |
| shrinkage | aaaaa | aaaaa |