Anti-fouling self-cleaning blended fiber fabric for curtains and preparation method of fabric

A blended fiber, self-cleaning technology, applied in the direction of anti-coloring pollution/anti-fouling fiber, fiber type, fiber treatment, etc. Cleaning effect, excellent targeting, effect of increasing effective working life

Inactive Publication Date: 2017-09-08
马鞍山市永运家纺有限公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to long-term use, due to ventilation problems, furniture adhesives, decoration materials, smoking, etc., on the one hand, the environmental humidity is not easy to control, which makes the curtains easy to breed mold. On the other hand, it contains formaldehyde, cresol, benzene, nicotine, and nitrogen oxides. The release of other gases affects the health of people in the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] An antifouling self-cleaning blended fiber fabric for curtains, which is made of the following parts by mass: 90 parts of functional fibers, 4 parts of nano-chitosan, 4 parts of nano-maya blue, 4 parts of sodium anthraquinone-2-sulfonate, poly 4 parts of ethylene glycol oleate, 4 parts of sodium silicate, 4 parts of isopropanol, 8 parts of N,N-dimethylformamide, 2 parts of silane coupling agent.

[0017] It also includes 4 parts of plant extracts, which are chamomile and arborvitae with a mass ratio of 1:2.

[0018] Among them, the functional fiber is composed of polyester fiber, acrylic fiber, bamboo charcoal fiber, and viscose staple fiber. The mass percentages of the four are 20% acrylic fiber, 20% viscose staple fiber, and 15% bamboo charcoal fiber. , polyester fiber balance, nano chitosan particle size of 5-10nm, nano maya blue particle size of 5-15nm, silane coupling agent is a mixture of KH-590 and Si-602 with a mass ratio of 1:1.5.

[0019] Antifouling self-cle...

Embodiment 2

[0021] An antifouling self-cleaning blended fiber fabric for curtains, which is made of the following parts by mass: 95 parts of functional fibers, 5 parts of nano-chitosan, 3 parts of nano-maya blue, 4 parts of sodium anthraquinone-2-sulfonate, poly 5 parts of ethylene glycol oleate, 6 parts of sodium silicate, 3 parts of isopropanol, 10 parts of N,N-dimethylformamide, 2 parts of silane coupling agent.

[0022] It also includes 3 parts of plant extracts, which are chamomile and arborvitae with a mass ratio of 1:2.

[0023] Among them, the functional fiber is composed of polyester fiber, acrylic fiber, bamboo charcoal fiber, and viscose staple fiber. The mass percentages of the four are 30% of acrylic fiber, 25% of viscose staple fiber, and 30% of bamboo charcoal fiber. , polyester fiber balance, nano chitosan particle size of 5-10nm, nano maya blue particle size of 5-15nm, silane coupling agent is a mixture of KH-590 and Si-602 with a mass ratio of 1:1.5.

[0024] Antifoulin...

Embodiment 3

[0026] An antifouling self-cleaning blended fiber fabric for curtains, comprising the following parts by mass: 80 parts of functional fiber, 6 parts of nano chitosan, 3 parts of nano Maya blue, 4.5 parts of sodium anthraquinone-2-sulfonate, poly 5 parts of ethylene glycol oleate, 2 parts of sodium silicate, 2 parts of isopropanol, 6 parts of N,N-dimethylformamide, and 1 part of silane coupling agent.

[0027] It also includes 5 parts of plant extracts, which are chamomile and arborvitae with a mass ratio of 1:2.

[0028] Among them, the functional fiber is composed of polyester fiber, acrylic fiber, bamboo charcoal fiber, and viscose staple fiber. The mass percentages of the four are 25% of acrylic fiber, 20% of viscose staple fiber, and 25% of bamboo charcoal fiber. , polyester fiber balance, nano chitosan particle size of 5-10nm, nano maya blue particle size of 5-15nm, silane coupling agent is a mixture of KH-590 and Si-602 with a mass ratio of 1:1.5.

[0029] The anti-foul...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides an anti-fouling self-cleaning blended fiber fabric for curtains and a preparation method of the fabric. The fiber fabric comprises, by weight, 80-100 parts of functional fiber, 3-6 parts of nano chitosan, 3-5 parts of nano maya blue, 4-6 parts of sodium anthraquinone-2-sulfonate, 3-6 parts of polyethylene glycol oleate, 2-10 parts of sodium silicate, 2-5 parts of isopropyl alcohol, 3-10 parts of N,N-dimethyl formamide and 1-3 parts of silane coupling agent. By reasonable modification on fibers, toughness, adsorption, antifouling and dyeing properties and the like of the fiber fabric are improved effectively; by means of photocatalysis, the capability of the fiber of adsorbing and decomposing foreign flavor, odor and hazardous substances is enhanced, the fabric has self-cleaning effect and is green and environment friendly, and service life is prolonged.

Description

technical field [0001] The invention relates to the technical field of chemical fiber preparation, in particular to an antifouling self-cleaning blended fiber fabric for curtains and its preparation. Background technique [0002] Curtains are floor coverings made of cotton, hemp, wool, silk, grass and other natural fibers or chemical synthetic fiber materials that are braided, tufted or woven by hand or mechanically. Covering the ground of residences, hotels, gymnasiums, exhibition halls, vehicles, ships, aircraft, etc. With its tight and breathable structure, the curtain can absorb and isolate sound waves, and has a good sound insulation effect. The fluff on the surface of the curtain can capture and absorb dust particles floating in the air, effectively improving indoor air quality. Curtains are a kind of soft paving material, which is different from hard floor paving materials such as marble and ceramic tiles. Curtains have rich patterns, gorgeous colors, and diverse s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/03D06M11/79D06M13/256D06M15/53D06M101/32D06M101/28D06M101/06
CPCD06M11/79D06M13/256D06M15/03D06M15/53D06M2101/06D06M2101/28D06M2101/32D06M2200/01
Inventor 卫必兵
Owner 马鞍山市永运家纺有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com