A kind of hypereutectic aluminum-silicon alloy modification agent and application

An aluminum-silicon alloy and modifier technology, which is applied in the field of hypereutectic aluminum-silicon alloy modifiers, can solve problems such as coarse primary silicon, and achieve the effects of dense organization, gas reduction, and size reduction.

Active Publication Date: 2018-11-09
福建祥鑫股份有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to solve the problem of coarse primary silicon in hypereutectic aluminum-silicon alloys, the present invention provides a novel modifier for hypereutectic aluminum-silicon alloys and its application method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of hypereutectic aluminum-silicon alloy modification agent and application
  • A kind of hypereutectic aluminum-silicon alloy modification agent and application
  • A kind of hypereutectic aluminum-silicon alloy modification agent and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] The technical solutions of the present invention are further specifically described below through examples. It should be noted that the following examples and comparative examples are only used to explain the present invention, and should not be regarded as limiting the scope of the claims of the present invention.

[0035] Examples and comparative examples

[0036] In the present invention, the prepared hypereutectic aluminum-silicon alloy raw materials are sequentially melted in a resistance furnace, then the melt is overheated to 750-850° C., and then the Cu-2Be master alloy modifier (containing 2wt% of Be) is pressed Put it into the overheated hypereutectic aluminum-silicon alloy melt, stir it well, and keep it warm for 30-60 minutes; then add conventional refining agents for degassing and refining, and keep it warm for 10-15 minutes; finally, pour the hypereutectic aluminum-silicon alloy melt into castings or For ingot casting, the pouring temperature is 740-800°C...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of nonferrous metal materials and particularly relates to a hypereutectic aluminium-silicon alloy alterant and application. The hypereutectic aluminium-silicon alloy alterant contains Be. A better application technology of the hypereutectic aluminium-silicon alloy alterant is as follows: overheating hypereutectic aluminium-silicon alloy melt to 750-850 DEG C, pressing a Be alterant into the overheated alloy melt, fully stirring, preserving heat for 30-60 minutes, refining for degassing, standing and preserving heat for 10-15 minutes, and pouring into casting or cast ingot, wherein the pouring temperature is 740-800 DEG C and the cooling rate is 50-100 DEG C / s. The hypereutectic aluminium-silicon alloy alterant enables the average size of primary silicon in hypereutectic aluminium-silicon alloy containing 15-25% of silicon to be refined to below 30 microns, is uniform in distribution, remarkably improves the comprehensive mechanical property, and effectively promotes application of hypereutectic aluminium-silicon alloy.

Description

technical field [0001] The invention belongs to the technical field of non-ferrous metal materials, and in particular relates to a hypereutectic aluminum-silicon alloy modifier and its application. Background technique [0002] Due to its good wear resistance, corrosion resistance, low expansion coefficient, excellent mechanical properties and castability, hypereutectic aluminum-silicon alloy is an ideal material for manufacturing wear-resistant and heat-resistant parts such as motorcycles and automobile engine pistons. However, the hypereutectic aluminum-silicon alloy structure without modification often contains coarse and flaky primary silicon, which will severely split the matrix and significantly reduce the strength and toughness of the alloy, especially the plasticity of the alloy is very poor, and the elongation is generally 1%. Below, it is difficult to meet the requirements of production and use. Therefore, effective modifiers and treatment processes must be adopte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/04C22C1/03
CPCC22C1/026C22C1/03C22C21/04
Inventor 林高用李坤谭鑫陈昭
Owner 福建祥鑫股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com