What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A preparation process, pearl white technology, applied in the field of ceramic products, can solve the problems of pearl luster, loss of firing process, etc., and achieve the effect of pearl gloss, good hiding, and lower quality and content
Active Publication Date: 2017-09-29
CERAMICS SCI & TECH RES INST QUANZHOU +1
View PDF5 Cites 10 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
The raw materials and firing process of traditional pearl white porcelain ha...
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
specific Embodiment 1
[0032] Dehua pearl white porcelain, including pearl white body and pearl white glaze,
[0033] Pearl white body, its parts by weight are as follows: 37 parts of kaolin, 28 parts of bone powder, 14 parts of Dehua quartz, 9 parts of feldspar, 8 parts of calcite, 4 parts of bentonite;
[0034] Pearl white glaze, its parts by weight are as follows: 77 parts of transparent glaze frit, 6 parts of dolomite, 4 parts of kaolin, 3 parts of bone powder, 4 parts of calcined strontium carbonate, 2 parts of fluorescent powder, 3 parts of nano-silver powder, 1 part of nano-platinum powder parts, and the chemical composition of the transparent glaze frit is as follows: SiO 2 54%, Al 2 o 3 7.5%, B 2 o 3 9.3%, CaO 10.8%, MgO 4.26%, ZnO 6.8%, Na 2 O 0.8%, K 2 O1.5%, Mn 0.04%, I.L 5%.
specific Embodiment 2
[0035] Dehua pearl white porcelain is characterized in that it includes a pearl white body and a pearl white glaze,
[0036] The pearl white body has parts by weight as follows: 34 parts of kaolin, 29 parts of bone meal, 14 parts of Dehua quartz, 9 parts of feldspar, 8 parts of calcite, and 6 parts of bentonite;
[0037] The pearl white glaze has the following parts by weight: 73 parts of transparent glaze frit, 8 parts of dolomite, 6 parts of kaolin, 3 parts of bone meal, 2 parts of calcined strontium carbonate, 4 parts of fluorescent powder, 2 parts of nano-silver powder, and 2 parts of nano-platinum Powder 2 parts, and the chemical composition of the transparent glaze frit is as follows: SiO 2 54%, Al2 o 3 7.8%, B 2 o 3 9.6%, CaO 10.2%, MgO 3.78%, ZnO 6.2%, Na 2 O0.66%, K 2 O 1.92%, Mn 0.04%, I.L 5.8%.
[0038] The preparation process of Dehua pearl white porcelain is characterized in that the above-mentioned Dehua pearl white porcelain is prepared, and the specifi...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention belongs to the field of porcelain product and relates to Dehua pearl white porcelain and a preparation technology thereof. The prepared Dehua pearl white porcelain comprises a pearl white porcelain body and pearl white glaze. The glaze surface of the prepared Dehua pearl white porcelain has milk white pearly luster, and has the artistic effect closest to that of traditional Dehua pearl white porcelain. Through detection of the glaze surface of the prepared Dehua pearl white porcelain, the refractive index of the surface of the pearl white porcelain is 1.4-1.5, the glaze surface is capable of reflecting light energy into milk white light, the light is abundant, changeable and not dull, and delicate changeable iridescence can be seen through angle transformation; the glaze surface of the Dehua pearl white porcelain is relatively thick, so that the pearl glossiness of the glaze surface can be more obvious and the thick feeling of the porcelain body can be increased; and in addition, the pearl white porcelain has good shielding property on the body and is capable of properly reducing the quality and the content of kaolin in the raw materials of the body, and the kaolin is replaced with low-price bentonite, so that the production cost is reduced.
Description
technical field [0001] The invention belongs to the field of ceramic products, in particular, the invention relates to a Dehua pearl white porcelain and its preparation process. Background technique [0002] Dehua white porcelain originated in the Song and Yuan Dynasties, was famous in the Ming Dynasty, and was extended in the early Qing Dynasty. It has a unique style in the white porcelain system in my country, occupies an important position in the history of ceramic development, and has the reputation of "Oriental Art" internationally. . Dehua white porcelain in the Ming and Qing dynasties was fired with a transparent glaze on a low-iron porcelain body. Dehua white porcelain of the Ming Dynasty has a pure white, solid and dense body bone. The technology of its body glaze strives to pursue the perfection of jade texture, which is unique in the dazzling array of porcelain altars. According to the different porcelain colors, they are lard white, ivory white, pearl white, etc...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).