Rubber compound of high-tensile-modulus high-wear-resistance tread rubber, and preparation method of rubber compound

A rubber compound, high wear-resistant technology, applied in the rubber field, can solve the problems of easy cracking, high air permeability, poor rubber adhesion, etc., and achieve the effect of improving physical and mechanical properties, good compactness, and poor air permeability.

Active Publication Date: 2017-10-20
QINGDAO UNIV OF SCI & TECH
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention mainly solves the technical problems that the single SBR formula in the prior art is prone to cracks, punctures, the more ordinary fibers there are, the greater its air permeability, and the poorer degree of adhesion with rubber, and it provides a high specific elongation and high wear resistance. The rubber compound of tread rubber and its preparation method, the rubber compound can achieve the effect of high constant elongation and high wear resistance through the synergistic effect between the components

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rubber compound of high-tensile-modulus high-wear-resistance tread rubber, and preparation method of rubber compound
  • Rubber compound of high-tensile-modulus high-wear-resistance tread rubber, and preparation method of rubber compound

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0027] The technical solutions in the embodiments of the present invention will be clearly and completely described below in conjunction with the embodiments of the present invention. Apparently, the described embodiments are only some of the embodiments of the present invention, not all of them. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0028] Below in conjunction with embodiment the present invention will be further described:

[0029] Table 1: Rubber compound formula table (unit is weight part)

[0030]

[0031] Various rubbers and compounds in Table 1 are described below.

[0032] NR: Use Thai smoked sheet glue 3#.

[0033] Carbon Black: Cabot Carbon Black.

[0034] Aramid staple fiber: Twaron produced by DuPont.

[0035] All other complexes are commercially available.

[0036] Table 2: Physical p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a rubber compound of high-tensile-modulus high-wear-resistance tread rubber, and a preparation method of the rubber compound. The rubber compound comprises 100 parts of natural rubber, 55 parts of carbon black, 6 parts of an environmentally-friendly peptizer, 2 parts of stearic acid, 5 parts of zinc oxide, 2 parts of an anti-ageing agent 4010NA, 1.5 parts of protective wax, 1.5 parts of tackifying resin, 3 parts of aramid short fiber, 2 parts of an adhesive, 5 parts of sulfur, 1.8 parts of an accelerant NS, 1 part of shredded ginger fiber and 2 parts of potato fiber. After the potato fiber is added, the three-dimensional fiber net-like structure locks up the shredded ginger fiber, so that the performance of the rubber product is integrally enhanced, the shredded ginger fiber is wrapped with the potato fiber, and the potato fiber active free radical can promote adhesion with a rubber matrix; the waste is utilized, so that environmental protection is benefited.

Description

technical field [0001] The invention relates to the technical field of rubber, in particular to a rubber compound of high constant elongation and high wear-resistant tread rubber and a preparation method thereof. technical background [0002] As people have more and more requirements for cars, tires have become a very important research object in addition to the interior functions and safety of cars. Tires support the entire weight of the car and bear the load, transmit traction and braking force, and ensure the adhesion between the wheel and the road surface; they can also absorb and slow down the impact and vibration generated by the car during driving, which can not only slow down the vibration of car parts Destroying and improving ride comfort, it can also reduce the noise generated by the car at high speeds, ensuring the safety, stability and comfort of the car. The outermost layer of the tire is called the tread. Through a specific pattern, the tire has traction and b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L91/06C08L77/10C08L3/02C08L1/02C08K13/02C08K3/22C08K5/09C08K3/04C08K3/06B60C1/00
CPCC08L7/00B60C1/0016C08K2003/2296C08K2201/014C08L2205/035C08L2205/16C08L91/06C08L77/10C08L3/02C08L1/02C08K13/02C08K3/22C08K5/09C08K3/04C08K3/06
Inventor 汪传生李海涛刘洁李泽汉张鲁琦
Owner QINGDAO UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products