Biologically treated light-coated glassine paper and preparation method thereof

A glassine base paper and biological treatment technology, which is applied in pulp beating/refining methods, special paper, fiber raw material treatment, etc., can solve the problems of glassine paper surface lint and powder, high production cost, low transparency, etc., to achieve Excellent paper performance, improve transparency, and solve the effect of lint and powder falling

Active Publication Date: 2017-11-28
浙江哲丰新材料有限公司
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to overcome the disadvantages of glassine base paper in the prior art, such as insufficient strength, low transparency and high production cost, to provide a biologically treated light-coated glassine base paper and its preparation method. Larch, cheap and easy-to-obtain domestic eucalyptus wood, and glass wool fiber that can improve the strength of paper are used as raw materials. The transparency of glassine base paper is significantly improved through alkali treatment combined with biological enzyme treatment. The problem of lint and powder falling on the paper surface has excellent paper performance and high market value

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0024] A method for preparing biologically treated light-coated glassine base paper, which is characterized in that it comprises the following steps:

[0025] (1) Material selection: Russian larch, North Sea fast-growing eucalyptus and glass wool fiber are selected as raw materials for production;

[0026] (2) Pulp preparation: After the Russian larch is cooked into pulp by the kraft method, it is pre-soaked in a sodium hydroxide solution with a mass concentration of 8.5-16.5 percent for 30-60 minutes, and then transferred to the trough-type pulping along with the lye Beating in the machine, the beating degree is controlled at 25-35°SR, and then washed with pure water for use;

[0027] After the eucalyptus is pulped by the CTMP method, it is pre-soaked in a sodium hydroxide solution with a mass concentration of 6.8-13.5% for 20-40 minutes, and transferred to a double disc mill along with the lye for beating. The beating degree is controlled at 38 -42°SR, then wash with pure water fo...

Embodiment 1

[0043] A method for preparing biologically treated light-coated glassine base paper, which is characterized in that it comprises the following steps:

[0044] (1) Material selection: Russian larch, North Sea fast-growing eucalyptus and glass wool fiber are selected as raw materials for production;

[0045] (2) Pulp preparation: After the Russian larch is cooked into pulp by the kraft method with a ratio of sodium sulfate and sodium hydroxide of 1:4.5, it is pre-soaked in a sodium hydroxide solution with a mass concentration of 11.6% for 60 minutes. It is transferred to the trough-type beater along with the lye for beating, the beating degree is controlled at 32°SR, and then washed with pure water for use;

[0046] After the eucalyptus is pulped by the CTMP method, it is pre-soaked in a sodium hydroxide solution with a mass concentration of 11.6% for 40 minutes, and transferred to a double disc mill along with the lye for beating. The beating degree is controlled at 38°SR, and then W...

Embodiment 2

[0055] A method for preparing biologically treated light-coated glassine base paper, which is characterized in that it comprises the following steps:

[0056] (1) Material selection: Russian larch, North Sea fast-growing eucalyptus and glass wool fiber are selected as raw materials for production;

[0057] (2) Pulp preparation: After the Russian larch is cooked into pulp by the kraft method with a ratio of sodium sulfate and sodium hydroxide of 1.5:5.5, it is pre-soaked in a sodium hydroxide solution with a mass concentration of 14.5% for 40 minutes, It is transferred to the trough-type beater along with the lye for beating, the beating degree is controlled at 30°SR, and then washed with pure water for use;

[0058] After the eucalyptus is pulped by the CTMP method, it is pre-soaked in a sodium hydroxide solution with a mass concentration of 14.5% for 30 minutes, and then transferred to a double disc mill along with the lye for beating. The beating degree is controlled at 41°SR. Was...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses biologically treated light-coated glassine paper and a preparation method thereof. The method comprises the steps of material selection of selecting russia larix gmelini, fast-growing eucalyptus in the north sea and glass wool fiber as production materials; slurry preparation of larix gmelini, eucalyptus and wool fiber; and slurry preparation, biological treatment, papermaking and final paper forming operation. According to the preparation method of the biologically treated light-coated glassine paper, the transparency of the glassine paper is significantly improved by combining alkali treatment with bioenzyme treatment by selecting imported larix gmelini with excellent performance, cheap and available domestic eucalyptus and the glass wool fiber capable of improving the paper forming strength as the raw materials; meanwhile, the problems of linting and dusting of the surface of the glassine paper in the using process is solved through light coating; and the biologically treated light-coated glassine paper has excellent paper performance and relatively high market value.

Description

Technical field [0001] The invention relates to the technical field of papermaking, in particular to a biologically treated light-coated glassine base paper and a preparation method thereof. Background technique [0002] As a kind of industrial paper with uniform texture, glassine paper can be used to make bar codes, tapes, oil-proof packaging, etc. The glassine base paper in the prior art is mostly made directly from chemical wood pulp, so it is limited by the properties of natural fibers, the strength of the finished paper is insufficient, the transparency is low, and the paper surface is prone to lint and powder during use. Such circumstances make it difficult to meet the requirements of large-scale industrial use. At the same time, because all high-quality chemical wood pulp is used, its high price and high production cost. Based on this, the present invention selects imported larch with excellent performance, cheap and easily available domestic eucalyptus, and glass wool fi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H27/00D21H15/12D21H17/64D21D1/30D21H15/02D21H17/00D21F11/02D21H21/54D21C3/02
CPCD21C3/022D21D1/303D21F11/02D21H15/02D21H15/12D21H17/005D21H17/64D21H21/54D21H27/00
Inventor 张顺根史君齐张诚章琚珩程义桃
Owner 浙江哲丰新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap