A kind of aluminum-wood composite decorative board and preparation method thereof
A technology of aluminum-wood composite and decorative panels, which is applied in the field of material chemistry, can solve the problems of high energy consumption, long cold pressing cycle, and low production efficiency, and achieve the effects of high bonding strength, high stability, and high adhesion
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0023] An aluminum-wood composite decorative board, in parts by weight, the decorative board includes 30 parts of kraft base paper, 25 parts of aluminum foil, 19 parts of phenolic resin, 11 parts of sodium hydroxide, 13 parts of absolute ethanol, 8 parts of pectin, poly 20 parts of vinyl alcohol, 12 parts of polyvinyl acetate emulsion, 12 parts of polyvinyl butyral, 7 parts of starch, 8 parts of kaolin, 12 parts of deionized water.
[0024] A method for preparing an aluminum-wood composite decorative panel, the method comprising the following steps:
[0025] (1) Disperse the phenolic resin in anhydrous ethanol, stir magnetically for 30 minutes, and stir at 25°C until completely dissolved, then add polyvinyl acetate emulsion and polyvinyl butyral, and continue magnetically stirring until completely dissolved;
[0026] (2) dissolving starch in deionized water to form a paste, then adding sodium hydroxide, and reacting at a temperature of 45°C for 1 hour to obtain modified starch...
Embodiment 2
[0032] An aluminum-wood composite decorative board, in parts by weight, said decorative board comprises 42 parts of kraft base paper, 40 parts of aluminum foil, 35 parts of phenolic resin, 18 parts of sodium hydroxide, 16 parts of absolute ethanol, 18 parts of pectin, poly 30 parts of vinyl alcohol, 19 parts of polyvinyl acetate emulsion, 18 parts of polyvinyl butyral, 14 parts of starch, 17 parts of kaolin, 21 parts of deionized water.
[0033] A method for preparing an aluminum-wood composite decorative panel, the method comprising the following steps:
[0034] (1) Disperse the phenolic resin in absolute ethanol, stir magnetically for 45 minutes, and stir at a temperature of 30°C until completely dissolved, then add polyvinyl acetate emulsion and polyvinyl butyral, and continue magnetically stirring until completely dissolved;
[0035] (2) dissolving starch in deionized water to form a paste, then adding sodium hydroxide, and reacting at a temperature of 55° C. for 2.5 hours...
Embodiment 3
[0041] An aluminum-wood composite decorative board, in parts by weight, said decorative board comprises 55 parts of kraft base paper, 55 parts of aluminum foil, 40 parts of phenolic resin, 19 parts of sodium hydroxide, 19 parts of absolute ethanol, 22 parts of pectin, poly 34 parts of vinyl alcohol, 23 parts of polyvinyl acetate emulsion, 22 parts of polyvinyl butyral, 18 parts of starch, 22 parts of kaolin, 25 parts of deionized water.
[0042] A method for preparing an aluminum-wood composite decorative panel, the method comprising the following steps:
[0043] (1) Disperse the phenolic resin in absolute ethanol, stir magnetically for 60 minutes at a temperature of 35°C, add polyvinyl acetate emulsion and polyvinyl butyral after complete dissolution, and continue magnetic stirring until completely dissolved;
[0044](2) dissolving starch in deionized water to form a paste, then adding sodium hydroxide, and reacting at a temperature of 65°C for 3 hours to obtain modified star...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction