Processing method of silver ornament

A processing method and technology of silver jewelry, applied in clothing, jewelry, applications, etc., can solve the problems of silver jewelry processing technology confusion, poor gloss of silver jewelry, unsightly welding, etc., and achieve beautiful silver jewelry, smooth surface, and high wear resistance Effect

Active Publication Date: 2017-12-22
GUIZHOU YIHUAZHUANG DEV CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the improvement of living standards, people buy more and more silver ornaments, and the requirements for the appearance and quality of silver ornaments are constantly improved. Due to the higher demand, the processing technology of silver ornaments in the prior art is relatively chaotic, resulting in processed silver ornaments. Defects such as poor gloss of jewelry and unsightly welding have caused many defective products to be re-melted, causing unnecessary losses to the manufacturer.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A processing method for silver jewellery, comprising the steps of:

[0021] (1) Rolling: the silver block is sent into the tablet press and rolled into a silver wire with a width of 1 cm and a thickness of 0.5 cm;

[0022] (2) Modification: put the silver wire into the modification solution and soak for 25 minutes, and the soaking temperature is 60°C;

[0023] (3) High temperature: Send the soaked silver wire into a high-temperature furnace at 150°C for 10 minutes, and place it in a ventilated place to cool naturally to 40°C;

[0024] (4) Production of messy silk: rub the high-temperature-treated silver silk on a flat object with a wooden pressing tool to form silver filigree, wind the twisted silver filigree on an iron rod with a diameter of 3 cm, and put it in an oven for 120 minutes , then cool naturally to normal temperature, remove the silver filigree from the iron bar, squeeze the spiral silver filigree by hand, and then use an iron hammer to slightly beat on bot...

Embodiment 2

[0033] A processing method for silver jewellery, comprising the steps of:

[0034] (1) Rolling: the silver nugget is sent into the tablet press and rolled into a silver wire with a width of 1.5cm and a thickness of 1cm;

[0035] (2) Modification: soak the silver wire in the modification solution for 35 minutes, and the soaking temperature is 70°C;

[0036] (3) High temperature: Send the soaked silver wire into a high-temperature furnace at 220°C for 20 minutes, and place it in a ventilated place to cool naturally to 60°C;

[0037] (4) Production of messy silk: rub the high-temperature-treated silver silk on a flat object with a wooden pressing tool to form silver filigree, wind the twisted silver filigree on an iron rod with a diameter of 5 cm, and put it in an oven for 180 minutes , then cool naturally to normal temperature, remove the silver filigree from the iron bar, squeeze the spiral silver filigree by hand, and then use an iron hammer to slightly beat on both sides to ...

Embodiment 3

[0046] A processing method for silver jewellery, comprising the steps of:

[0047] (1) Rolling: the silver block is sent into the tablet press and rolled into a silver wire with a width of 1.2cm and a thickness of 0.8cm;

[0048] (2) Modification: put the silver wire into the modification solution and soak for 30 minutes, and the soaking temperature is 68°C;

[0049] (3) High temperature: Send the soaked silver wire into a 180°C high-temperature furnace for 15 minutes, and place it in a ventilated place to cool naturally to 48°C;

[0050] (4) Making of messy silk: rub the high-temperature-treated silver thread on a flat object with a wooden pressing tool to form silver filigree, wind the twisted silver filigree on an iron rod with a diameter of 3 to 5 cm, and put it in an oven Process for 150 minutes, then cool naturally to room temperature, remove the silver filigree from the iron rod, squeeze the spiral silver filigree by hand, and then lightly beat both sides with an iron ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of silver ornament processing, in particular to a processing method of a silver ornament. The method comprises the following six steps to finish the silver ornament processing: rolling, modifying, processing under high temperature, manufacturing entangled threads, welding the silver threads subjected to modifying and high-temperature processing are high in tensile strength, wearing resistance, toughness and glossiness, so that the silver threads can be effectively prevented from breaking and deforming during the entangled thread manufacturing process; moreover, the plasticity of the silver threads in processing can be improved. The silver ornament processed through the abovementioned scheme is nice in appearance, smooth in surface, glossy, high in wearing resistance, and hard to damage.

Description

technical field [0001] The invention belongs to the technical field of silver jewelry processing, in particular to a processing method of silver jewelry. Background technique [0002] With the improvement of living standards, people buy more and more silver ornaments, and the requirements for the appearance and quality of silver ornaments are constantly improved. Due to the higher demand, the processing technology of silver ornaments in the prior art is relatively chaotic, resulting in processed silver ornaments. Defects such as poor gloss of jewelry and unsightly welding have caused many defective products to be re-melted, causing unnecessary losses to manufacturers. Contents of the invention [0003] In order to solve the above technical problems, the present invention provides a processing method for silver ornaments. [0004] Specifically, it is achieved through the following technical solutions: [0005] A processing method for silver jewellery, comprising the steps...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A44C27/00B23P15/00
CPCA44C27/00B23P15/00
Inventor 李开琼李开元张喜
Owner GUIZHOU YIHUAZHUANG DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com