Prefabricated concrete pavement structure

A concrete pavement, prefabricated assembly technology, applied to pavement, roads, roads and other directions paved with prefabricated blocks, can solve the problems of long construction period, low production efficiency, long seasonal downtime, etc., and achieve rapid assembly paving, installation Fast speed, good shear stress effect

Active Publication Date: 2017-12-22
湖北广盛建筑产业化科技有限公司
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Low production efficiency, consume a lot of human resources, long construction period
On-site construction mainly adopts manual work, and product quality is not easy to guarantee
Great environmental pollution, on-site concrete pouring produces noise, sewage, waste and other environmental pollution
When the pavement is demolished or abandoned, the pavement materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Prefabricated concrete pavement structure
  • Prefabricated concrete pavement structure
  • Prefabricated concrete pavement structure

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0026] Example 1

[0027] A method for preparing high-strength antifreeze concrete, characterized in that the method includes the following steps:

[0028] Add 300 parts of cement, 60 parts of quicklime, 600 parts of aggregate, 2.5 parts of activator and 5.8 parts of amphoteric dispersant into 300 parts of water and stir and mix well, control the dispersion of the slurry at 18cm, the temperature at 45℃, and the stirring rate 650r / min;

[0029] Pour the material obtained in the above steps, and then send it to a static shutdown room with a temperature of 50°C and a humidity of 60°C for 3 hours after casting;

[0030] After the thickening, the material is demoulded and cut to obtain the required size of the green body, and then the green body

[0031] It is sent to the autoclave for steam curing for 2 hours, after leaving the autoclave, natural curing for one week to obtain the final high-strength anti-freeze concrete.

[0032] The preparation method of the amphoteric dispersant is as fol...

Example Embodiment

[0045] Example 2

[0046] Add 300 parts of cement, 60 parts of quicklime, 600 parts of aggregate, 1 part of activator and 8 parts of amphoteric dispersant to 300 parts of water and stir and mix, control the dispersion of the slurry at 18cm, the temperature at 45℃, and the stirring rate 650r / min;

[0047] Pour the material obtained in the above steps, and then send it to a static shutdown room with a temperature of 50°C and a humidity of 60°C for 3 hours after casting;

[0048] After the thickening, the material is demoulded and cut to obtain the required size of the green body, and then the green body is sent to the autoclave for steam curing for 2 hours, after leaving the autoclave, natural curing for one week to obtain the final high-strength antifreeze Concrete

[0049] The rest of the preparation is the same as in Example 1.

Example Embodiment

[0050] Example 3

[0051] Add 400 parts of cement, 10 parts of quicklime, 500 parts of aggregate, 2.5 parts of activator and 5.8 parts of amphoteric dispersant to 300 parts of water and stir and mix well, control the dispersion of the slurry at 18cm, the temperature at 45℃, and the stirring rate 650r / min;

[0052] Pour the material obtained in the above steps, and then send it to a static shutdown room with a temperature of 50°C and a humidity of 60°C for 3 hours after casting;

[0053] After the thickening, the material is demoulded and cut to obtain the required size of the green body, and then the green body is sent to the autoclave for steam curing for 2 hours, after leaving the autoclave, natural curing for one week to obtain the final high-strength antifreeze Concrete

[0054] The rest of the preparation is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a prefabricated concrete pavement structure. The prefabricated concrete pavement structure comprises a plurality of concrete road modules; a square notch is reserved in each of four corners of each concrete road module; each corner forms a rabbet; a through hole is formed between the adjacent two rabbets; one concrete road module forms four through holes comprising two transverse through holes and two longitudinal through holes; and the concrete road modules are used cooperatively with a transverse connecting shaft and a longitudinal connecting shaft. The prefabricated concrete pavement structure is formed by assembling the concrete road modules, in particular, rapid assembling paving can be realized and the mounting speed is high.

Description

technical field [0001] The invention relates to a prefabricated assembled concrete pavement structure. Background technique [0002] At present, the society builds a large number of roads of various grades, a large part of which is concrete roads. At present, domestic concrete roads mainly adopt cast-in-place concrete construction technology, which requires on-site support formwork, binding steel bars, pouring concrete, concrete curing and other construction processes. The disadvantages of the cast-in-place concrete production process are mainly as follows: [0003] The production efficiency is low, a large amount of human resources are consumed, and the construction period is long. The on-site construction mainly adopts manual operation, and the product quality is not easy to guarantee. Great environmental pollution, on-site pouring of concrete produces noise, sewage, waste and other environmental pollution. When the pavement is demolished or abandoned, the pavement mat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): E01C5/06C04B28/00C04B24/26C04B24/16C04B103/40C04B111/20C08F283/06C08F285/00C08F220/06C08F220/34C08F222/06C08F220/14C08F220/56C08F220/38
CPCC04B24/165C04B24/2694C04B28/00C04B2103/408C04B2111/29C04B2201/50C04B2201/52C08F283/065C08F285/00E01C5/065C04B22/064C04B18/08C04B14/106C04B18/141C04B18/064C04B18/04C08F220/06C08F220/34C08F222/06C08F220/14C08F220/56
Inventor 赵蕊赵然
Owner 湖北广盛建筑产业化科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap