Psychedelic pseudo-decorative surface coating and preparation method thereof

A decorative surface and coating technology, applied in camouflage coatings, polyester coatings, epoxy resin coatings, etc., can solve the problem of camouflage bunkers that are difficult to achieve high efficiency, the quality of finished raw materials in the market is uneven, and the weather resistance and crack resistance of building exterior walls Poor performance and other problems, to achieve the effect of enhancing the psychedelic illusion of visible light and near-infrared radar magnetic wave detection, increasing interference to hinder radar magnetic wave detection, and protecting the base color paint

Active Publication Date: 2018-01-12
宜昌市大棒科技有限公司
View PDF1 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] 1. Direct identification, it is difficult to achieve high-efficiency camouflage bunker effect
[0006] 2. The quality of raw materials and finished products in the market is uneven, and it is difficult to achieve an effective camouflage bunker effect
[0007] 3. Does not have the function of reflective heat insulation, multi-function, multi-purpose coating camouflage bunker
[0008] 4. Toxic or low-toxic products are not environmentally friendly and not conducive to construction and use
[0009] 5. The construction cost is high, and the weather resistance and crack resistance of the building exterior wall are poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Psychedelic pseudo-decorative surface coating and preparation method thereof
  • Psychedelic pseudo-decorative surface coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Embodiment 1: a kind of psychedelic pseudo-decorative finish paint, raw material is: 10 parts of base material water; Auxiliary (preservative agent 100g, dispersant 50g, defoamer 100g, propylene glycol 200g, film-forming agent 200g, thickener 200g , antifouling agent 100g), a total of 4.0 parts; functional filler (ceramic silicon carbide 100g, ferrite magnetic powder 50g, inorganic pigment 50g, chlorophyll 200g, hollow ceramic microspheres 500g, aluminized powder 100g, silicon dioxide 500g), A total of 0.8 parts; a total of 85 parts of water-based resin silicone acrylic emulsion.

[0035] Applicable technical parameters:

[0036]

[0037]

Embodiment 2

[0038] Embodiment 2: a kind of psychedelic pseudo-decorative finish paint, raw material is: base material water, altogether 13 parts; Auxiliary (preservative 130g, dispersant 65g, defoamer 130g, propylene glycol 230g, film-forming agent 250g, thickening 250g antifouling agent, 130g anti-fouling agent), a total of 4.5 parts; functional filler (130g ceramic silicon carbide, 80g ferrite magnetic powder, 80g inorganic pigment, 150g chlorophyll, 650g hollow ceramic microspheres, 130g aluminized powder, 650g silicon dioxide ), a total of 1.0 parts; a mixture of fluorocarbon emulsion and polyurethane emulsion with a mass ratio of 1:1 is 80 parts in total.

[0039] main performance

Embodiment 3

[0040] Embodiment 3: a kind of psychedelic pseudo-decorative topcoat, raw material is: base material water, altogether 17 parts; Auxiliary (preservative 160g, dispersant 85g, defoamer 160g, propylene glycol 260g, film-forming agent 320g, thickening 320g antifouling agent, 165g anti-fouling agent), a total of 5 parts; functional filler (ceramic silicon carbide 165g, ferrite magnetic powder 120g, inorganic pigment 150g, chlorophyll 100g, hollow ceramic microspheres 800g, aluminized powder 160g, silicon dioxide 800g ), a total of 1.2 parts; a mixture of alkyd resin and phenolic resin with a mass ratio of 1:1 is 75 parts in total.

[0041] main performance

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides psychedelic pseudo-decorative surface coating. The psychedelic pseudo-decorative surface coating comprises base material water, aids, functional fillers and water-based resin, wherein the aids comprises preservative, a dispersing agent, a defoaming agent, propylene glycol, a film-forming agent, an anti-contamination aid and a thickening agent; the functional fillers compriseceramic silicon carbonate, ferrite magnetic powder, ferric oxide inorganic pigment, chlorophyll, hollow ceramic microbeads, aluminum plating powder and silicon dioxide; and the water-based resin comprises one or two of silicone acrylic emulsion, fluorocarbon emulsion, pure acrylic emulsion, polyurethane emulsion, epoxy resin, acrylic acid emulsion, alkyd resin and phenolic resin. In the technicalscheme of the invention, all the raw materials are environmentally friendly and are water-soluble environment-friendly raw materials. The psychedelic pseudo-decorative surface coating has non-toxic,odorless and environment-friendly effects; and the product has multiple functions of realizing reflective insulation, resisting dirt and weather, enhancing visible light near infrared radar magnetic wave detective psychedelic illusion, pretending blindage, realizing floating cloud psychedelic illusion, resisting ultraviolet rays, protecting bottom color paint, prolonging service life and the like.

Description

technical field [0001] The invention belongs to the technical field of paint preparation, and in particular relates to a psychedelic pseudo-decorative paint and a preparation method thereof. It is a kind of psychedelic pseudo-decorative top coating suitable for general camouflage coating surface or conventional coating surface construction. Background technique [0002] Camouflage paint is a special paint that prevents the enemy from being reconnaissance with visible light, infrared rays, and radar waves to confuse the enemy. It is mainly used on metal facilities and equipment; the basic design idea of ​​camouflage paint is to produce an effect that is consistent with the background. Under visible light, it produces a color consistent with the background; under electromagnetic wave irradiation, it produces a reflection spectrum consistent with the background, making the camouflage target consistent with the background tone, brightness or change shape. The camouflage paint s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D127/12C09D175/04C09D167/08C09D161/06C09D163/00C09D133/00C09D5/30C09D5/33C09D5/16C09D5/32C09D7/61
Inventor 袁绪彪
Owner 宜昌市大棒科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com