Polyformaldehyde thin film and preparation method thereof

A polyoxymethylene and polyoxymethylene resin technology, which is used in flat products, other household appliances, household appliances, etc., to achieve the effect of fast crystallization rate, expansion of application fields, and excellent performance

Active Publication Date: 2018-02-23
TANGSHAN KAILUAN CHEM TECH CO LTD
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the technology of preparing polyoxymethylene film with high mechanical strength in both horizontal and vertical directions by bidirectional synchronous film drawing method has not been reported yet.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The mass ratio of raw materials of the polyoxymethylene film of the present invention is: 94 parts of polyoxymethylene resin, 5 parts of novolak resin, and 1 part of antioxidant.

[0015] Preparation process: weigh polyoxymethylene resin, novolac resin and antioxidant with a melt index of 3 g / 10min according to the mass ratio, mix them evenly in a high-speed mixer, and then put them into a screw extruder for melt blending Finally, it is extruded through a mold, and the extruded melt is shaped by a cooling roller to make a polyoxymethylene film; then the polyoxymethylene film is placed on the stretching mold frame and fixed, and the hot air is blown to the film for preheating. Longitudinal and transverse two-way synchronous stretching, heat setting after stretching to the set draft ratio, and finally edge trimming, thickness measurement, and winding.

[0016] Process parameters: The temperature of the feeding section of the main extruder is 170~175°C, the temperature of ...

Embodiment 2

[0019] The mass ratio of raw materials of the polyoxymethylene film of the present invention is: 96 parts of polyoxymethylene resin, 3 parts of novolak resin, and 1 part of antioxidant.

[0020] Preparation process: Weigh polyoxymethylene resin, novolac resin and antioxidant with a melt index of 9 g / 10min according to the mass ratio, mix them evenly in a high-speed mixer, and then put them into a screw extruder for melt blending Finally, it is extruded through a mold, and the extruded melt is shaped by a cooling roller to make a polyoxymethylene film; then the polyoxymethylene film is placed on the stretching mold frame and fixed, and the hot air is blown to the film for preheating. Longitudinal and transverse two-way synchronous stretching, heat setting after stretching to the set draft ratio, and finally edge trimming, thickness measurement, and winding.

[0021] Process parameters: The temperature of the feeding section of the main extruder is 170~175°C, the temperature of ...

Embodiment 3

[0024] The mass ratio of raw materials of the polyoxymethylene film of the present invention is: 97 parts of polyoxymethylene resin, 2.5 parts of novolac resin, and 0.5 part of antioxidant.

[0025] Preparation process: weigh polyoxymethylene resin, novolac resin and antioxidant with a melt index of 3 g / 10min according to the mass ratio, mix them evenly in a high-speed mixer, and then put them into a screw extruder for melt blending Finally, it is extruded through a mold, and the extruded melt is shaped by a cooling roller to make a polyoxymethylene film; then the polyoxymethylene film is placed on the stretching mold frame and fixed, and the hot air is blown to the film for preheating. Longitudinal and transverse two-way synchronous stretching, heat setting after stretching to the set draft ratio, and finally edge trimming, thickness measurement, and winding.

[0026] Process parameters: The temperature of the feeding section of the main extruder is 170~175°C, the temperature...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
thicknessaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polyformaldehyde thin film and a preparation method thereof. The polyformaldehyde thin film comprises the following components by weight: 94-98 parts of a polyformaldehyde resin, 1-5 parts of a linear phenolic resin, and 0.5-1 part of an anti-oxidant. In allusion to the problem that the film formation is difficult because the crystallization speed of the polyformaldehydeis rapid and the crystallinity degree is high, the linear phenolic resin is introduced as a crystallization interference agent, the crystallization speed is reduced, and the crystallization time is prolonged, so the film-forming property of the polyformaldehyde is improved. In addition, a synchronous two-way stretching method is used, so the problem that the crosswise stretching film-formation isdifficult because of the rapid crystallization after the longitudinal stretching is prevented. In the raw material and technology aspect, the problem that the uniformity is bad because fracture and afine neck are easily generated in the stretching process of the polyformaldehyde thin film is overcome, and the high-strength polyformaldehyde thin film is prepared.

Description

technical field [0001] The invention belongs to the field of film preparation, in particular to a polyoxymethylene film and a preparation method thereof. Background technique [0002] As a highly crystalline polymer, polyoxymethylene has excellent mechanical properties, wear resistance, dimensional stability, chemical corrosion resistance and self-lubricating properties. Its raw materials and modified materials are widely used in automobiles, mechanical parts, electronic appliances, etc. There are applications in all fields. For example, if polyoxymethylene is used as raw material to stretch longitudinally and horizontally in a certain temperature range, the molecules can be rearranged, the degree of orientation can be improved, and the performance of the polyoxymethylene material can be further improved, so that the polyoxymethylene film has the characteristics of high strength and smooth surface. , can be widely used in packaging, construction, interior decoration, medici...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L59/02C08L61/06C08J5/18B29C55/16B29L7/00
CPCB29C55/16B29L2007/00C08J5/18C08J2359/02C08J2461/06
Inventor 王亚涛李建华马小丰刘莉莉郭学华
Owner TANGSHAN KAILUAN CHEM TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com