Antiskid, flame-retardant and antistatic wood-plastic composite material and preparation method thereof

A wood-plastic composite material, flame-retardant and anti-static technology, applied in the field of wood-plastic composite materials, can solve problems such as limiting practical application, and achieve the effects of improving stability, increasing cross-linking density, and improving adhesion

Inactive Publication Date: 2018-02-23
GUANGDONG GUOLI SCI & TECH CO LTD
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, there are few research reports on the anti-skid of wood-plastic composite materials, especially the research reports on the anti-skid effect achieved by designing components and processes, which limits the practical application.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0069] In this example, the lubricant is made by blending silicone powder and pentaerythritol ester at a weight ratio of 1:1, the initiator is azobisisobutyronitrile, the flame retardant is expandable graphite, and the coupling agent is γ-ammonia Propyltriethoxysilane, the antistatic agent is graphene oxide, the compatibilizer is polyethylene-glycidyl methacrylate with a melt index of 15g / 10min, the surface modifier is isocyanate, and the plant fiber is straw powder. The anti-sedimentation agent is organic bentonite, the leveling agent is silicone oil, and the pH regulator is citric acid.

[0070] A preparation method of a non-slip, flame-retardant and antistatic wood-plastic composite material in this embodiment comprises the following steps:

[0071] Substrate preparation steps, anti-slip agent preparation steps and mixing steps;

[0072] The substrate preparation steps include:

[0073] Step A: Polycarbonate resin, plant fibers, glass fibers, and carbon fibers are mixed i...

Embodiment 2

[0088] In this example, the lubricant is made by blending silicone powder and pentaerythritol ester at a weight ratio of 1:1, the initiator is azobisisobutyronitrile, the flame retardant is expandable graphite, and the coupling agent is γ-ammonia Propyltriethoxysilane, the antistatic agent is graphene oxide, the compatibilizer is polyethylene-glycidyl methacrylate with a melt index of 15g / 10min, the surface modifier is isocyanate, and the plant fiber is straw powder. The anti-settling agent is modified hydrogenated castor oil, the leveling agent is polydimethylsiloxane, and the pH regulator is potassium citrate.

[0089] A preparation method of a non-slip, flame-retardant and antistatic wood-plastic composite material in this embodiment comprises the following steps:

[0090] Substrate preparation steps, anti-slip agent preparation steps and mixing steps;

[0091] The substrate preparation steps include:

[0092] Step A: Polycarbonate resin, plant fibers, glass fibers, and c...

Embodiment 3

[0107] In this example, the lubricant is made by blending silicone powder and pentaerythritol ester at a weight ratio of 1:1, the initiator is azobisisobutyronitrile, the flame retardant is expandable graphite, and the coupling agent is γ-ammonia Propyltriethoxysilane, the antistatic agent is graphene oxide, the compatibilizer is polyethylene-glycidyl methacrylate with a melt index of 15g / 10min, the surface modifier is isocyanate, and the plant fiber is straw powder. The anti-settling agent is N-methylpyrrolidone solution of modified polyurea, the leveling agent is alkyl modified organosiloxane, and the pH regulator is tartaric acid.

[0108] A preparation method of a non-slip, flame-retardant and antistatic wood-plastic composite material in this embodiment comprises the following steps:

[0109] Substrate preparation steps, anti-slip agent preparation steps and mixing steps;

[0110] The substrate preparation steps include:

[0111] Step A: Polycarbonate resin, plant fiber...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of wood-plastic composite materials, and especially relates to an antiskid, flame-retardant and antistatic wood-plastic composite material and a preparation method thereof. The preparation method comprises the following steps: preparing a base material, preparing an antiskid agent, and mixing for preparing the composite material. The composite materialis prepared from polycarbonate resin, vegetable fibers, glass fibers, carbon fibers, a lubricant, an initiator, a flame retardant, a coupling agent, an antistatic agent, a compatibilizer and the antiskid agent. The composite material is formed by the base material and an antiskid layer sprayed on the surface of the base material, and the base material sequentially comprises a core latex, a shell latex and a sheath layer from the inside to the outside. The composite material has excellent antiskid, flame-retardant and antistatic properties.

Description

technical field [0001] The invention relates to the technical field of wood-plastic composite materials, in particular to an anti-slip, flame-retardant and antistatic wood-plastic composite material and a preparation method thereof. Background technique [0002] Wood-plastic composite material is a new type of environmentally friendly composite material prepared by processing a certain proportion of wood fiber material, thermoplastic polymer resin and various additives through melt extrusion, injection molding or hot pressing compounding. It has the dual advantages of both wood and plastic. It not only has the wood-like appearance of wood but also has the advantages of water resistance, corrosion resistance and insect resistance of thermoplastics. Moreover, its dimensional stability is better than that of wood, and its hardness and modulus are higher than that of wood. Thermoplastics have a flexible production process and can be reprocessed and recycled. They have outstandin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L97/02C08L83/04C08L51/06C08K13/04C08K7/06C08K7/14C08K7/24C08K3/04
CPCC08L69/00C08L97/02C08L2201/02C08L2201/04C08L2205/025C08L2205/035C08L2205/08C08L2205/16C08L83/04C08L51/06C08K13/04C08K7/06C08K7/14C08K7/24C08K3/04
Inventor 罗文平
Owner GUANGDONG GUOLI SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap