Titanium alloy applied to golf club heads, and preparation method thereof

A golf club head and titanium alloy technology, which is applied to golf balls, golf clubs, sports accessories, etc., can solve the problems of large-scale golf club heads, diverse materials, small elastic deformation, and high density. , to achieve the effect of increasing alloy hardening ability and high temperature strength, increasing elastic deformation force, and improving heat resistance

Inactive Publication Date: 2018-03-02
BAOJI YONGSHENGTAI TITANIUM IND
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a titanium alloy used in golf club heads, which solves the problem of small elastic deformation and high density of titanium alloy materials in the prior art, which cannot meet the requirements of large-scale golf club heads and diversification of materials. question of needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] The above-mentioned preparation method of the titanium alloy applied to the golf club head is specifically implemented according to the following steps:

[0029] Step 1: Weigh respectively according to mass percentage: titanium powder: 87-90%, aluminum powder: 8-10.5%, bismuth powder: 1.5-3.5%, iron powder: 0.1-0.5%, molybdenum powder: 0.05-0.08%, Chromium powder: 0.01-0.03%, the sum of the mass percentages of the above components is 100%;

[0030] Step 2: Dry the raw materials weighed in step 1 in a drying room at a temperature of 85-90°C for 24-36 hours;

[0031] Step 3: Put the raw materials dried in step 2 into a mixer at a speed of 25 rpm, and mix for 9-10 minutes;

[0032] Step 4: Cool the mixed raw materials in step 3 to room temperature;

[0033] Step 5: Put the cooled raw materials in step 4 into a smelting furnace for melting to obtain the finished titanium alloy. The specific melting process is as follows:

[0034] Step 5.1: From room temperature, heat to ...

Embodiment 1

[0041] A titanium alloy used in golf club heads, consisting of the following components by mass percentage: titanium powder: 88.5%, aluminum powder: 9%, bismuth powder: 2%, iron powder: 0.4%, molybdenum powder: 0.08% , Chromium powder: 0.02%, the sum of the mass percentages of the above components is 100%.

[0042] The above-mentioned preparation method of the titanium alloy applied to the golf club head is specifically implemented according to the following steps:

[0043] Step 1: Weigh respectively according to mass percentage: titanium powder: 88.5%, aluminum powder: 9%, bismuth powder: 2%, iron powder: 0.4%, molybdenum powder: 0.08%, chromium powder: 0.02%, the mass of the above components The sum of the percentages is 100%;

[0044] Step 2: Dry the raw materials weighed in step 1 in a drying room with a temperature of 85°C for 24 hours;

[0045] Step 3: Put the raw materials dried in step 2 into a mixer at a speed of 25 rpm, and mix for 9 minutes;

[0046] Step 4: Cool...

Embodiment 2

[0055] A titanium alloy applied to the golf club head of the present invention is composed of the following components according to mass percentage: titanium powder: 88%, aluminum powder: 10%, bismuth powder: 1.5%, iron powder: 0.4%, molybdenum powder : 0.07%, chromium powder: 0.03%, the sum of the mass percentages of the above components is 100%.

[0056] The above-mentioned preparation method of the titanium alloy applied to the golf club head is specifically implemented according to the following steps:

[0057] Step 1: Weigh respectively according to mass percentage: titanium powder: 88%, aluminum powder: 10%, bismuth powder: 1.5%, iron powder: 0.4%, molybdenum powder: 0.07%, chromium powder: 0.03%, the mass of the above components The sum of the percentages is 100%;

[0058] Step 2: Dry the raw materials weighed in step 1 in a drying room with a temperature of 86°C for 30 hours;

[0059] Step 3: Put the raw materials dried in step 2 into a mixer at a speed of 25 rpm, and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a titanium alloy applied to golf club heads. The titanium alloy comprises, by mass, 87-90% of titanium powder, 8-10.5% of aluminum powder, 1.5-3.5% of bismuth powder, 0.1-0.5%of iron powder, 0.05-0.08% of molybdenum powder and 0.01-0.03% of chromium powder, and the sum of the mass percentages of the above components is 100%. A preparation method of the titanium alloy comprises the following steps: weighing the titanium powder, aluminum powder, bismuth powder, iron powder, molybdenum powder and chromium powder, drying the weighed raw materials, adding the dried raw materials into a mixer, mixing the raw materials, cooling the mixed raw materials to room temperature, adding the cooled raw materials into a smelting furnace, and melting the raw materials to obtain thefinished titanium alloy. The addition of bismuth makes the titanium alloy applied to the golf club heads have a high strength and be easy to cast, and improves the yield of the golf club heads cast byusing the titanium alloy; and the addition of aluminum increases the elastic deformation force of the titanium alloy and reduces the density of the titanium alloy.

Description

technical field [0001] The invention belongs to the technical field of titanium alloy material preparation, and relates to a titanium alloy applied to a golf club head, and also relates to a preparation method of a titanium alloy applied to a golf club head. Background technique [0002] Playing golf is an outdoor activity with special charm. In recent years, with the improvement of people's living standards, more and more people have joined golf, so the market demand for golf equipment has also increased rapidly. [0003] Titanium alloy materials are widely used in the golf equipment industry. However, although the titanium alloy materials currently on the market have greater elastic deformation force, the same strength and lower density than club heads made of stainless steel materials, However, under the premise of increasing the size and diversification of golf club heads, the existing titanium alloy materials cannot meet the needs. Therefore, it is necessary to develop ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C14/00C22C1/02A63B53/04
CPCC22C14/00A63B53/04A63B2209/00C22C1/02
Inventor 陈炳豊文锐刘宝权周辉良
Owner BAOJI YONGSHENGTAI TITANIUM IND
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com