PVC (polyvinyl chloride) calcium plastic floor material and preparation method thereof

A technology of floor materials and PVC resin powder, applied in the field of PVC calcium-plastic floor materials and its preparation, can solve problems such as poor texture and poor anti-skid performance, and achieve the effect of solving poor texture

Inactive Publication Date: 2018-03-09
徐伟权
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The technical problem to be solved by the present invention is to provide a PVC calcium-plastic floor material and its preparation method, which can solve the problems of poor texture and poor anti-skid performance of existing calcium-plastic floor materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0012] A PVC calcium-plastic floor material, made of the following components in parts by weight: 30 parts of PVC resin powder, 30 parts of PVC recycled resin powder, 30 parts of orthoclase, 20 parts of 100 mesh borax, ethyl methacrylate 8 parts, barium ferrite 3 parts, calcium stearate 3 parts, saturated octadecylamide 2 parts.

[0013] The preparation method of this PVC calcium-plastic floor material comprises the following steps:

[0014] (1) Ingredients: according to the ratio of raw materials, add PVC resin powder, PVC recycled resin powder, orthoclase, 100 mesh borax, ethyl methacrylate, barium ferrite, calcium stearate, saturated octadecylamide Mix in a mixer, the speed is 1200 rpm, the time is 20 minutes, the temperature is 100 ° C, and the mixture is obtained for later use;

[0015] (2) Granulation: adding the mixture obtained in step (1) to a granulator at a temperature of 130°C for granulation, and cooling the obtained granules to obtain a PVC calcium plastic floor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a PVC (polyvinyl chloride) calcium plastic floor material and a preparation method thereof. The PVC calcium plastic floor material is prepared from the following raw materials in parts: 30 parts of PVC resin powder, 30 to 50 parts of PVC regenerated resin powder, 30 to 50 parts of orthoclase, 20 to 40 parts of 100-mesh borax, 8 to 12 parts of ethyl methacrylate, 3 to 5 partsof barium ferrite, 3 to 5 parts of calcium stearate, and 2 parts of saturated stearamide. The PVC calcium plastic floor material and the preparation method have the advantages that by adopting the formula, the problems of poor texture, and poor anti-skid property in the existing calcium plastic floor material are solved.

Description

Background technique [0001] Calcium-plastic materials are a type of composite material that is made of inorganic calcium salt as the main raw material and mixed with synthetic resins such as polyolefins. It has chemical stability, high and low temperature resistance, good heat insulation, water resistance, good flame retardancy, slow burning speed, less smoke, and is not easy to cause fire and public nuisance. Widely used as building materials, home improvement materials, furniture and daily necessities materials, etc., the existing calcium-plastic floor materials have the above-mentioned advantages, but also have the problems of poor texture and poor anti-skid performance. Contents of the invention [0002] The technical problem to be solved by the present invention is to provide a PVC calcium-plastic floor material and a preparation method thereof, which can solve the problems of poor texture and poor anti-skid performance of existing calcium-plastic floor materials. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K13/02C08K3/34C08K3/38C08K5/098C08K5/20
CPCC08L27/06C08L2205/025C08L2207/20C08K13/02C08K3/34C08K2003/387C08K5/098C08K5/20
Inventor 徐伟权
Owner 徐伟权