Al4O4C enhanced silicon carbide honeycomb ceramic and preparation method thereof

A technology of silicon carbide honeycomb and silicon carbide powder, which is applied in the field of honeycomb ceramics, can solve the problems of uneven micropore size and distribution in the wall, poor mechanical properties of the product, and high thermal expansion coefficient, and achieve good microstructure and strong thermal fatigue resistance , the effect of high mechanical strength

Active Publication Date: 2018-03-20
JIANGSU GAOCHUN CERAMICS
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The wall-flow silicon carbide honeycomb ceramics obtained by the current preparation method of wall-flow silicon carbide honeycomb ceramics has high thermal expansion coefficient, high firing temperature, uneven micropore size and distribution in the wall, poor mechanical properties of the product, and high production cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Al4O4C enhanced silicon carbide honeycomb ceramic and preparation method thereof
  • Al4O4C enhanced silicon carbide honeycomb ceramic and preparation method thereof
  • Al4O4C enhanced silicon carbide honeycomb ceramic and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] In order to better understand the present invention, the content of the present invention will be further clarified below in conjunction with the embodiments, but the content of the present invention is not limited to the following embodiments.

[0025] In the following examples, Al 4 O 4 The raw material components of the C-reinforced silicon carbide honeycomb ceramic include: 75 to 85 parts of silicon carbide powder, 5 to 15 parts of silicon carbide powder, Al 4 O 4 5-10 parts of C, 2-6 parts of sintering aid, 12.5-22.5 parts of binder and 12.5-22.5 parts of water. The parts are parts by mass. The purity of silicon carbide powder one is 99wt%, and the particle size is 5~50μm, the manufacturer is Anyang Jinsheng Metallurgical Materials Co., Ltd.; the purity of silicon carbide powder II is 99wt%, and the particle size is 0.05~0.5μm, and the manufacturer is Anyang Jinsheng Metallurgical Materials Co., Ltd.; 4 O 4 The purity of C is 99 wt%, and the particle size is 30-80 μm.

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses Al4O4C enhanced silicon carbide honeycomb ceramic and a preparation method thereof. The Al4O4C enhanced silicon carbide honeycomb ceramic is prepared from raw material ingredients in parts by mass: 75 to 85 parts of first silicon carbide powder, 5 to 15 parts of second silicon carbide powder, 5 to 10 parts of Al4O4C, 2 to 6 parts of sintering aid, 12.5 to 22.5 parts of binding agent and 12.5 to 22.5 parts of water, wherein the purity of the first silicon carbide powder is 85 to 99.9wt%, the granularity of the first silicon carbide is 5 to 50mu m, the purity of the second silicon carbide is 85 to 99.9wt%, and the granularity of the second silicon carbide is 0.05 to 0.5mu m. The Al4O4C enhanced silicon carbide honeycomb ceramic disclosed by the invention has the characteristics of high raw material utilization rate and high production efficiency; furthermore, a product structure is in a wall flow type, so that purifying capacity to waste gas is improved; the product is easy to form, and a process is easy to control; the Al4O4C enhanced silicon carbide honeycomb ceramic prepared by the method has the advantages of good microstructure, even micropore distribution, high mechanical strength and low thermal expansion coefficient.

Description

Technical field [0001] The present invention relates to an Al 4 O 4 C-reinforced silicon carbide honeycomb ceramics and a preparation method thereof belong to the technical field of honeycomb ceramics. Background technique [0002] Developed countries began to control vehicle exhaust in the 1970s and formulated emission standards. In order to reduce the hazards of exhaust pollutants from gasoline and diesel vehicles, honeycomb ceramic filters are mainly used. With the economic construction and the continuous increase in the exhaust emissions of gasoline and diesel vehicles used by residents, my country's environmental protection requirements are gradually increasing, and higher emission reduction technologies are needed. [0003] The wall-flow silicon carbide honeycomb ceramic obtained by the current preparation method of the wall-flow silicon carbide honeycomb ceramic has high thermal expansion coefficient, high firing temperature, uneven size and distribution of micropores in th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/00C04B35/565C04B35/622C04B35/636C04B35/632C04B35/634
CPCC04B35/565C04B35/622C04B35/632C04B35/63488C04B35/6365C04B38/0006C04B38/0041C04B2235/3217C04B2235/3232C04B2235/3895C04B2235/9607C04B38/0054
Inventor 余超吴郑敏邓承继孔秋民陈明祥祝洪喜丁军
Owner JIANGSU GAOCHUN CERAMICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products