Passivating anticorrosion treatment method for surface of stainless steel sieving plate

An anti-corrosion treatment, stainless steel technology, applied in the direction of metal material coating process, etc., can solve the problems of reduced service life of the sieve plate, prolonging the production cycle of the sieve plate, and wear of the edge of the sieve hole, so as to improve corrosion resistance, inhibit corrosion reaction, The effect of increasing binding force

Inactive Publication Date: 2018-03-20
安徽屹翔滤材有限公司
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Stainless steel sieve plate has high rigidity and bearing capacity, and can be used as a rigid screening and filtering device of various shapes. It is widely used in various industries for screening, filtering, dehydration, desliming and other filtering functions. The sieve plates used in grading, screening and filtration operations in quarry, chemical, food and other industries, when screening, filtering materials, and filter bodies, the movement of granular materials will cause serious wear and corrosion to the sieve plate, often causing the surface of the sieve plate to be damaged. The edge of the sieve hole is severely worn, which affects the accuracy of material screening, which significantly reduces the service life of the sieve plate, and the replacement of the sieve plate will prolong the production cycle, increase production costs, and reduce production efficiency.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A kind of surface passivation anticorrosion treatment method of stainless steel sieve plate, comprises the following steps:

[0019] (1) Cleaning: Soak the stainless steel sieve plate in acetone for 30 minutes, then take it out, clean it with clean water, then soak the stainless steel sieve plate in an ethanol solution with a mass fraction of 75% for 25 minutes, then take it out, and wash it with clean water After cleaning, dry to constant weight;

[0020] (2) Vacuum impregnation: Put the stainless steel sieve plate treated in step (1) into the glycosylamide-modified polysiloxane solution and vacuum impregnate at 80°C for 1 hour, and then add the glycosylamide-modified polysiloxane Add 0.5% phosphoric acid in the solution, ultrasonically disperse evenly, keep warm at 75°C for 30min, then cool down to room temperature naturally, take out the stainless steel sieve plate, wash it with clean water, and dry it to constant weight;

[0021] (3) Surface irradiation treatment: ...

Embodiment 2

[0030] A kind of stainless steel sieve plate surface passivation anticorrosion treatment method, comprises the following steps:

[0031] (1) Cleaning: Soak the stainless steel sieve plate in acetone for 40 minutes, then take it out, clean it with clean water, then put the stainless steel sieve plate in an ethanol solution with a mass fraction of 75% for 30 minutes, then take it out, and wash it with clean water After cleaning, dry to constant weight;

[0032] (2) Vacuum impregnation: Put the stainless steel sieve plate treated in step (1) into the glycosylamide-modified polysiloxane solution and vacuum impregnate at 90°C for 1 hour, and then add the glycosylamide-modified polysiloxane Add phosphoric acid with a mass of 0.8% to the solution, ultrasonically disperse it evenly, keep it warm at 75°C for 30 minutes, then cool it down to room temperature naturally, take out the stainless steel sieve plate, wash it with clean water, and dry it to constant weight;

[0033] (3) Surfac...

Embodiment 3

[0042] A kind of surface passivation anticorrosion treatment method of stainless steel sieve plate, comprises the following steps:

[0043] (1) Cleaning: Soak the stainless steel sieve plate in acetone for 35 minutes, then take it out, clean it with clean water, then soak the stainless steel sieve plate in an ethanol solution with a mass fraction of 75% for 28 minutes, then take it out, and wash it with clean water After cleaning, dry to constant weight;

[0044] (2) Vacuum impregnation: Put the stainless steel sieve plate treated in step (1) into the glycosylamide-modified polysiloxane solution and vacuum impregnate at 85°C for 1 hour, and then add the glycosylamide-modified polysiloxane Add phosphoric acid with a mass of 0.6% to the solution, ultrasonically disperse it evenly, keep it warm at 75°C for 30 minutes, then cool it down to room temperature naturally, take out the stainless steel sieve plate, wash it with clean water, and dry it to constant weight;

[0045] (3) Su...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention discloses a passivation and anticorrosion treatment method for the surface of stainless steel sieve plate, which relates to the technical field of stainless steel sieve plate, including: (1) cleaning; (2) vacuum impregnation; (3) surface irradiation treatment; (4) passivation: The surface passivation anticorrosion treatment method of the stainless steel sieve plate of the present invention can not only form a corrosion-resistant passivation film on the surface of the stainless steel sieve plate, but also make the surface of the passivation film smoother, and effectively improve the contact angle of the surface of the passivation film , thereby significantly improving the fouling resistance of the passivation film surface.

Description

technical field [0001] The invention belongs to the technical field of stainless steel sieve plates, and in particular relates to a passivation and anticorrosion treatment method for the surface of stainless steel sieve plates. Background technique [0002] Stainless steel sieve plate has high rigidity and bearing capacity, and can be used as a rigid screening and filtering device of various shapes. It is widely used in various industries for screening, filtering, dehydration, desliming and other filtering functions. The sieve plates used in grading, screening and filtration operations in quarry, chemical, food and other industries, when screening, filtering materials, and filter bodies, the movement of granular materials will cause serious wear and corrosion to the sieve plate, often causing the surface of the sieve plate to be damaged. The edge of the sieve hole is severely worn, which affects the accuracy of material screening and significantly reduces the service life of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/73C23C22/08
CPCC23C22/73C23C22/08
Inventor 丁好奇韩同清李金成王体亚
Owner 安徽屹翔滤材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com