A kind of two-dimensional zinc coordination polymer and its preparation method

A zinc coordination polymer and two-dimensional layered technology, which is applied in the field of coordination polymer preparation, can solve the problems of inconvenient detection and expensive detection instruments, and achieve a good effect of fluorescence recognition and sensing

Active Publication Date: 2021-08-31
安徽锦圣新材料有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These detection methods have high sensitivity, but there are also some shortcomings, mainly because some detection instruments are too expensive and the detection is not convenient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of two-dimensional zinc coordination polymer and its preparation method
  • A kind of two-dimensional zinc coordination polymer and its preparation method
  • A kind of two-dimensional zinc coordination polymer and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0034] to combine figure 1 , a method for preparing a two-dimensional zinc coordination polymer, comprising the following steps:

[0035] S1, choose soluble zinc salt, 3-nitrophthalic acid, 1,2,4-triazole, the soluble zinc salt, 3-nitrophthalic acid, 1,2,4-triazole Select according to the molar ratio of 1:1:1~2;

[0036] S2. Dissolve the selected soluble zinc salt, 3-nitrophthalic acid, and 1,2,4-triazole in 500-1000 parts of deionized water, stir at room temperature for 1 hour, and then add 10-15 Part of organic base, stirred at room temperature for 1 hour;

[0037] S3, after stirring the solution in step S2 evenly, add it into a stainless steel reaction kettle with polytetrafluoroethylene as the inner liner;

[0038]S4. Put the reaction kettle into a blast drying oven and heat up to 160-170°C, react for 72-96 hours, turn off the oven and cool to room temperature naturally to obtain light yellow needle-shaped crystals, filter, wash with deionized water several times, and b...

Embodiment 1

[0040] A method for preparing a two-dimensional zinc coordination polymer, comprising the following steps:

[0041] S1, select zinc nitrate hexahydrate (0.1mmol), 3-nitrophthalic acid (0.1mmol) 1,2,4-triazole (0.2mmol), zinc nitrate hexahydrate, 3-nitrophthalic acid Formic acid and 1,2,4-triazole are selected according to the molar ratio of 1:1:2;

[0042] S2. Dissolve zinc nitrate hexahydrate, 3-nitrophthalic acid, and 1,2,4-triazole in 500 to 1,000 parts of deionized water, stir for 1 hour at room temperature, and then add triethyl Amine (1.0mmol), stirred at room temperature for 1 hour;

[0043] S3. After the solution in step S2 was stirred evenly, it was added to a 30 mL stainless steel reactor with polytetrafluoroethylene as a lining, and 10 mL of deionized water was added;

[0044] S4. Put the reaction kettle into a blast drying oven and heat up to 160°C, react for 72 hours, turn off the oven and cool to room temperature naturally to obtain light yellow needle-shaped c...

Embodiment 2

[0046] A method for preparing a two-dimensional zinc coordination polymer, comprising the following steps:

[0047] S1, choose zinc sulfate heptahydrate (0.1mmol), 3-nitrophthalic acid (0.1mmol) 1,2,4-triazole (0.2mmol), zinc sulfate heptahydrate, 3-nitrophthalate Formic acid and 1,2,4-triazole are selected according to the molar ratio of 1:1:1;

[0048] S2. Dissolve zinc sulfate heptahydrate, 3-nitrophthalic acid, and 1,2,4-triazole in 500 to 1,000 parts of deionized water, stir for 1 hour at room temperature, and then add triethyl Amine (1.5mmol), stirred at room temperature for 1 hour;

[0049] S3. After the solution in step S2 was stirred evenly, it was added to a 30 mL stainless steel reactor with polytetrafluoroethylene as a lining, and 10 mL of deionized water was added;

[0050] S4. Put the reaction kettle into a blast drying oven and heat up to 170°C, react for 96 hours, turn off the oven and cool to room temperature naturally to obtain light yellow needle-shaped cr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a two-dimensional zinc coordination polymer, the zinc coordination polymer has a two-dimensional layered structure, and the zinc coordination polymer is composed of soluble zinc salt, 1,2,4-triazole, 3-nitrate The chemical formula of the zinc coordination polymer is [Zn(3‑NBA)(trz)] n , wherein, 3‑NBA is 3‑nitrobenzoic acid anion, trz is 1,2,4‑triazole anion, and n is the degree of polymerization. The invention adopts soluble zinc salt to add organic ligand 3-nitrophthalic acid, and high-temperature hydrothermal reaction 3-nitrophthalic acid is prepared by in-situ decomposition reaction of C-C bond breaking; zinc complex It is a two-dimensional layered structure and has a good fluorescence recognition and sensing effect on p-nitrobenzene, and has important potential application prospects in environmental detection.

Description

technical field [0001] The invention relates to the technical field of preparation of coordination polymers, in particular to a two-dimensional zinc coordination polymer capable of detecting nitrobenzene and a preparation method thereof. Background technique [0002] Nitrobenzene (NB) is an important organic intermediate, which is widely used in the production of dyes, pesticides, medicines, and fluorescent whitening agents. A large amount of pollutants may be produced during production, which may cause serious harm to the environment and organisms function and is potentially explosive. In recent years, the rapid and effective detection of nitro compounds has become one of the research hotspots in the field of materials. The current methods for detecting various nitro compounds mainly include gas chromatography-mass spectrometry, surface-enhanced Raman spectroscopy, cyclic voltammetry, and ion mobility spectrometry. These detection methods have high sensitivity, but there ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More