Transparent resin composition for wire pipe and preparation method of transparent resin composition

A technology of resin composition and electric wire pipe, applied in the field of transparent resin composition and preparation thereof, can solve the problems of inability to accurately judge the internal condition of the pipe material, construction difficulty, etc., to ensure the corrosion resistance of acid and alkali, improve mechanical properties, Guaranteed uniformity

Inactive Publication Date: 2018-05-01
惠州法智力量法律咨询有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the pipes used for wire distribution and pipes on the market are basically PVC pipes or PPR pipes. However, PVC pipes or PPR pipes are currently opaque materials. difficulty

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Transparent resin composition for wire pipe and preparation method of transparent resin composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Example 1 is a transparent resin composition for wire and pipe, including the following components in parts by mass: polyphenylene sulfone resin 50, polyethylene terephthalate 10, sodium m-carboxybenzoate 10, Nano-titanium dioxide particles 5, emulsifier 3, accelerator 0.5, preservative 1, through the coupling agent and accelerator in the embodiment, the prepared resin composition can be made to achieve quick-drying performance, and by adding nano-titanium dioxide particles, The surface of the resin composition can be made finer and finer, further by adding polyethylene terephthalate and sodium m-carboxybenzoate, the prepared resin composition can have better transparency, and the film thickness of the resin composition is 0.5 cm, its light transmittance can reach more than 95%, the haze can reach level 5, and the service life of level 5 salt spray test can reach more than 48 months.

Embodiment 2

[0025] Example 2 is a transparent resin composition for wire and pipe, including the following components in parts by mass: polyphenylene sulfone resin 70, polyethylene terephthalate 30, sodium m-carboxybenzoate 50, Nano-titanium dioxide particles 20, emulsifier 9, coupling agent 0.5, accelerator 5, preservative 5, through coupling agent and accelerator in the embodiment, the resin composition prepared can be made to achieve quick-drying performance, and by adding There are nano-titanium dioxide particles, which can make the surface of the resin composition more delicate. Further, by adding polyethylene terephthalate and sodium m-carboxybenzoate, the prepared resin composition can have better transparency, and the resin combination When the film thickness is 0.5cm, the light transmittance can reach more than 95%, the haze can reach level 5, and the service life of level 5 salt spray test can reach more than 48 months.

Embodiment 3

[0027] Example 3 is a transparent resin composition for wire and pipe, including the following components in parts by mass: polyphenylene sulfone resin 60, polyethylene terephthalate 20, sodium m-carboxybenzoate 10, Nano-titanium dioxide particles 5, emulsifier 3, coupling agent 0.1, accelerator 0.5, preservative 1, through coupling agent and accelerator in the embodiment, the resin composition prepared can be made to achieve quick-drying performance, and by adding There are nano-titanium dioxide particles, which can make the surface of the resin composition more delicate. Further, by adding polyethylene terephthalate and sodium m-carboxybenzoate, the prepared resin composition can have better transparency, and the resin combination When the film thickness is 0.5cm, the light transmittance can reach more than 95%, the haze can reach level 5, and the service life of level 5 salt spray test can reach more than 48 months.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
thicknessaaaaaaaaaa
transmittivityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a transparent resin composition for a wire pipe and a preparation method of the transparent resin composition, wherein the transparent resin composition for the wire pipe comprises the following components in parts by mass: 50-70 parts of polyphenylene sulfone resin, 10-30 parts of polyethylene glycol terephthalate, 10-50 parts of sodium carboxyl benzoate, 5-20 parts of nanometer titania particles, 3-9 parts of emulsifier, 0-0.5 part of coupling agent, 0.5-5 parts of accelerant and 1-5 parts of preservative. When the membrane thickness of the transparent resin composition for the wire pipe, prepared by using the preparation method, is 0.5cm, the light transmittance can reach 95% or above, the fog scale can reach 5 grades, and a 5-grade salt fog test proves that thelife reaches up to 48 months or longer.

Description

technical field [0001] The invention belongs to the field of fine chemicals, and in particular relates to a transparent resin composition used for electric wires and pipes and a preparation method thereof. Background technique [0002] At present, the pipes used for wire distribution and pipes on the market are basically PVC pipes or PPR pipes. However, PVC pipes or PPR pipes are currently opaque materials. difficulty. Contents of the invention [0003] The object of the present invention is to provide a kind of transparent resin composition and preparation method thereof for electric wire pipe material, and when the film thickness of the transparent resin composition for electric wire pipe material prepared by the present invention is 0.5cm, its light transmittance can reach More than 95%, the haze can reach level 5, and the service life of level 5 salt spray test can reach more than 48 months. [0004] The present invention can be realized through the following technic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L81/06C08L67/02C08L71/02C08K13/02C08K5/098C08K3/22C08K5/41C08K5/42
CPCC08L81/06C08K2003/2241C08K2201/011C08L2201/10C08L2205/24C08L2203/18C08L2203/20C08L2205/03C08L67/02C08L71/02C08K13/02C08K5/098C08K3/22C08K5/41C08K5/42
Inventor 林妙娥
Owner 惠州法智力量法律咨询有限公司