Self-adhesive and preparation method thereof and anti-pollution self-adhesive asphalt waterproofing membrane

A technology of bituminous waterproofing membrane and self-adhesive, which is applied in the direction of bituminous material adhesive, adhesive type, chemical instrument and method, etc. problems such as performance, to achieve excellent bonding effect, improve efficiency, and save energy.

Active Publication Date: 2018-05-08
YUEYANG ORIENTAL YUHONG WATERPROOF TECH
View PDF8 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, none of the above technical solutions solves the problem that the adhesive surface of the self-adhesive modified asphalt coil is easily polluted by materials such as dust and cement powder on the construction site during the construction process, resulting in low surface energy of the self-adhesive surface, loss of adhesion and loss of adhesion. The failure of bonding with the base layer may easily lead to waterproof problems such as water channeling in the later stage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Self-adhesive and preparation method thereof and anti-pollution self-adhesive asphalt waterproofing membrane
  • Self-adhesive and preparation method thereof and anti-pollution self-adhesive asphalt waterproofing membrane
  • Self-adhesive and preparation method thereof and anti-pollution self-adhesive asphalt waterproofing membrane

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] This embodiment proposes a self-adhesive rubber material for anti-pollution self-adhesive waterproof membrane, and its raw material formula weight components are as follows:

[0041]

[0042]

[0043] Petroleum asphalt is grade 110# asphalt; the aniline point of aromatic oil is 23°C, and the content of aromatic hydrocarbon is 86%; the freezing point of naphthenic oil is -26°C, and the content of saturated hydrocarbon is 91%; the molecular weight of synthetic wax is 2000, and the melting point is 100~ 103 polyethylene wax; styrene-isoprene-styrene grade is SIS 1105; styrene-butadiene-styrene grade is SBS 792; tackifier is C9 petroleum resin; stabilizer is elemental sulfur; The coupling agent is silane coupling agent DL602; the inorganic filler is fly ash.

[0044] The preparation steps of the self-adhesive of the present embodiment are as follows:

[0045]Heat petroleum asphalt to 130°C; add aromatic oil and naphthenic oil, heat and stir until the temperature rise...

Embodiment 2

[0049] This embodiment proposes a self-adhesive rubber material for anti-pollution self-adhesive waterproof membrane, and its raw material formula weight components are as follows:

[0050]

[0051] Petroleum asphalt is a mixture of 90# asphalt and 220# asphalt, the weight fraction ratio of 90# asphalt and 220# asphalt is 1:1.5; the aniline point of aromatic oil is 21°C, and the aromatic content is 90%; the freezing point of naphthenic oil is -28 ℃, the content of saturated hydrocarbons is 93%; the molecular weight of the synthetic wax is 3000, and the melting point is 105-110 ℃ polyethylene wax; the grade of styrene-isoprene-styrene is SIS 1100; styrene-butadiene-styrene The grade of ethylene is SBS 6302; the tackifier is C5 petroleum resin; the stabilizer is zinc oxide; the coupling agent is titanate coupling agent isopropyl tris (dioctyl pyrophosphate acyloxy) titanate; inorganic filler For light calcium carbonate.

[0052] The preparation steps of the self-adhesive tha...

Embodiment 3

[0057] This embodiment proposes a self-adhesive rubber material for anti-pollution self-adhesive waterproof membrane, and its raw material formula weight components are as follows:

[0058]

[0059] Petroleum asphalt is a mixture of 70# asphalt and 160# asphalt, the weight fraction ratio of 70# asphalt and 160# asphalt is 1:2; the aniline point of aromatic oil is 21°C, and the aromatic content is 90%; the freezing point of naphthenic oil is -30 ℃, the content of saturated hydrocarbons is 95%; the molecular weight of the synthetic wax is 4000, and the melting point is 110-115 ℃ polyethylene wax; the grade of styrene-isoprene-styrene is SIS1100; styrene-butadiene-styrene The grade is SBS 791; the tackifier is C9 petroleum resin; the stabilizer is zinc oxide; the coupling agent is titanate coupling agent isopropyl tris (dioctyl pyrophosphate acyloxy) titanate; the inorganic filler is Light calcium carbonate.

[0060] The preparation steps of the self-adhesive that the present...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
aniline pointaaaaaaaaaa
freezing pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a self-adhesive and a preparation method of the self-adhesive and an anti-pollution self-adhesive asphalt waterproofing membrane. The self-adhesive comprises the following components: petroleum asphalt, aromatic oil, naphthenic oil, synthetic wax, styrene-isoprene-styrene, styrene-butadiene-styrene, a tackifier, a stabilizer, a coupling agent and an inorganic filler. The anti-pollution self-adhesive asphalt waterproofing membrane comprises three layers which are a reinforced layer, a self-adhesive layer and an isolation layer successively; or five layers which are an isolation layer, a self-adhesive layer, a reinforced layer, a self-adhesive layer, and an isolation layer successively. According to the anti-pollution self-adhesive asphalt waterproofing membrane prepared by the invention, physical properties can meet product standard requirements in GB 23441-2009 Self-adhesive Polymer Modified Asphalt Waterproofing Membrane, and the peel strength of the membrane and an aluminum plate reaches 2.8 N / mm, and is higher than the standard by 1.5 N / mm.

Description

technical field [0001] The invention belongs to the field of waterproof materials, and more specifically relates to a self-adhesive, a preparation method thereof, and an anti-pollution self-adhesive asphalt waterproof coiled material. Background technique [0002] Self-adhesive modified asphalt waterproofing membranes do not require hot-melt heating during construction, and have the advantages of safety and environmental protection compared with hot-melt modified asphalt waterproofing membranes. Therefore, the application of self-adhesive modified asphalt waterproofing membranes has increased rapidly in the past two years. [0003] Chinese patent application CN 201010541459.4 discloses a modified asphalt composition with creep characteristics and its preparation method. The patent has the characteristics of strong bonding ability and continuous bonding ability, high elongation, and good low-temperature flexibility; Chinese patent application CN 200910013774.7 discloses a pre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J195/00C09J11/08B32B27/36B32B27/06B32B27/32B32B7/12B32B7/08
CPCC09J11/08C09J195/00B32B7/08B32B7/12B32B27/06B32B27/08B32B27/32B32B27/36C08L2205/035B32B2323/04B32B2367/00C08L53/02C08L91/00C08L23/06C08L93/04C08L57/02C08L61/06
Inventor 刘欢
Owner YUEYANG ORIENTAL YUHONG WATERPROOF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More