Sewage treating agent
A technology of sewage treatment agent and chelating agent, which is applied in water/sewage treatment, adsorption water/sewage treatment, water/sludge/sewage treatment, etc. Toxicity and other problems, to achieve the effect of heat conduction, low production cost, strong adsorption capacity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0017] A sewage treatment agent, which consists of the following components in parts by weight: 16 parts of polyaluminum chloride, 5 parts of bentonite, 10 parts of sodium polyacrylate, 1.2 parts of lignosulfonate, 1.8 parts of sodium sulfate, and 15 parts of activated carbon. The above-mentioned bentonite is organic-inorganic modified bentonite, lignosulfonate is lignosulfonate-based amphoteric chelating agent, lignosulfonate calcium phosphonate quaternary ammonium salt modified product or activated carbon is nano-copper and 8-hydroxy Copper quinoline modified activated carbon.
[0018] The preparation method of above-mentioned modified bentonite is: be that 10mmol / g, organic modifier and bentonite mass ratio are 1.8:100 to get each raw material according to aluminum / bentonite ratio, organic modifier and aluminum chloride are added deionized water, material The liquid ratio is 0.05:1, fully dissolved, then add bentonite calcined at 200°C for 3h, stir and react at a stirring r...
Embodiment 2
[0022] A sewage treatment agent, which consists of the following components in parts by weight: 8 parts of polyaluminum chloride, 10 parts of bentonite, 6 parts of sodium polyacrylate, 1.6 parts of lignosulfonate, 1.2 parts of sodium sulfate, and 25 parts of activated carbon. The above-mentioned bentonite is organic-inorganic modified bentonite, lignosulfonate is lignosulfonate-based amphoteric chelating agent, lignosulfonate calcium phosphonate quaternary ammonium salt modified product or activated carbon is nano-copper and 8-hydroxy Copper quinoline modified activated carbon.
[0023] The preparation method of above-mentioned modified bentonite is: be 5mmol / g according to aluminum / bentonite ratio, organic modifier and bentonite mass ratio are 2.3:100 get each raw material, organic modifier and aluminum chloride are added deionized water, material The liquid ratio is 0.03:1, fully dissolved, then add bentonite calcined at 300°C for 1 hour, stir and react at a stirring rate of...
Embodiment 3
[0027] A sewage treatment agent, which is composed of the following components in parts by weight: 12 parts of polyaluminum chloride, 7 parts of bentonite, 8 parts of sodium polyacrylate, 1.4 parts of lignosulfonate, 1.4 parts of sodium sulfate, and 10 parts of activated carbon. The above-mentioned bentonite is organic-inorganic modified bentonite, lignosulfonate is lignosulfonate-based amphoteric chelating agent, lignosulfonate calcium phosphonate quaternary ammonium salt modified product or activated carbon is nano-copper and 8-hydroxy Copper quinoline modified activated carbon.
[0028] The preparation method of above-mentioned modified bentonite is: be 8mmol / g according to aluminum / bentonite ratio, organic modifier and bentonite mass ratio are 2.0:100 get each raw material, organic modifier and aluminum chloride are added deionized water, material The liquid ratio is 0.04:1, fully dissolved, then add bentonite calcined at 250°C for 2 hours, stir and react at a stirring rat...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com