Method for improving deodorization effect by polyacrylic-acid-series water-absorbent resin component

A technology of polyacrylic acid series and super absorbent resin, applied in the field of absorbent articles, can solve the problems of deodorizing effect discount and the like

Inactive Publication Date: 2018-05-18
宜兴丹森科技有限公司
View PDF23 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, general physical adsorption systems, such as activated carbon, are usually not compatible with fragrances, which greatly reduces the deodorizing effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for improving deodorization effect by polyacrylic-acid-series water-absorbent resin component
  • Method for improving deodorization effect by polyacrylic-acid-series water-absorbent resin component
  • Method for improving deodorization effect by polyacrylic-acid-series water-absorbent resin component

Examples

Experimental program
Comparison scheme
Effect test

manufacture example 1

[0184] The acrylic acid / sodium acrylate mixed monomer solution (the molar ratio of acrylic acid / sodium acrylate is 2.2 / 7.8) was transported through pipelines, the monomer concentration of acrylic acid / sodium acrylate was 44.0wt%, and the flow rate of the monomer solution was 8689kg / h. The temperature of the monomer solution is 80-90°C. Polyethylene glycol diacrylate (molecular weight: 522) with a concentration of 11.3 wt% was transported at the branch of the monomer solution pipeline, and the flow rate was 72 kg / h. In addition, the azobisisobutylamidine hydrochloride aqueous solution (flow 50kg / h) and the sodium persulfate aqueous solution (flow 60kg / h) with a concentration of 4wt% were mixed by a delivery pump to form an initiator mixed turbidity. Liquid, and the mixed turbid liquid is transported to the monomer through the branch of the monomer solution pipeline to carry out the polymerization reaction. The reaction solution is sprayed onto the reaction bed to form a monome...

manufacture example 2

[0189] The acrylic acid / sodium acrylate mixed monomer solution (the molar ratio of acrylic acid / sodium acrylate is 2.2 / 7.8) was transported through pipelines, the monomer concentration of acrylic acid / sodium acrylate was 44.0wt%, and the flow rate of the monomer solution was 8689kg / h. The temperature of the monomer solution is 80-90°C. Polyethylene glycol diacrylate (molecular weight: 522) with a concentration of 11.3 wt% was transported at the branch of the monomer solution pipeline, and the flow rate was 72 kg / h. In addition, the azobisisobutylamidine hydrochloride aqueous solution (flow 50kg / h) and the sodium persulfate aqueous solution (flow 60kg / h) with a concentration of 4wt% were mixed by a delivery pump to form an initiator mixed turbidity. Liquid, and the mixed turbid liquid is transported to the monomer through the branch of the monomer solution pipeline to carry out the polymerization reaction. The reaction solution is sprayed onto the reaction bed to form a monome...

Embodiment 1

[0193] Reference sample 1:

[0194] The reference sample used was Powder A.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for improving deodorization effect by a polyacrylic-acid-series water-absorbent resin component. The method includes that (a), a deodorization combination comprisinga plant component and a chemical component is provided; (b), the deodorization mode of the plant component can be physical smell neutralization or covering, or chemical reaction; (c), the plant component can obviously reduce initial foul smell of body fluids when being used individually; (d), the plant component in the combination is bamboo powder; (e), the grain diameter of the bamboo powder in the combination is below 800 micrometers. By the deodorization combination, the initial foul smell of the body fluids can be removed, and the deodorization state can continue 24 hours or above.

Description

technical field [0001] The present invention relates to a method for improving the deodorizing effect using a polyacrylic acid-based water-absorbing resin component. Specifically, it is suitable for absorbent articles, such as paper diapers (disposable diapers), sanitary napkins, incontinence pads, mattresses, pet pads, wound care materials, building materials, soil water retention materials and other products, and has fast liquid absorption [0002] The polyacrylic acid-based water-absorbent resin with high performance, the composition and the production method of other absorbent articles. Background technique [0003] Super absorbent polymer (SAP), also known as super absorbent resin, is a cross-linked polymer containing strong hydrophilic groups that is insoluble in water but can absorb tens, hundreds or even thousands of times its own weight. polymer. Superabsorbent resins are now widely used in various fields such as diapers, sanitary napkins, adult incontinence produ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L51/00C08L97/02C08K13/02C08K3/36C08K3/30C08K5/053C08K5/1515C08J9/28C08J3/24C08F283/06C08F220/06
CPCC08L51/003C08F283/065C08J3/246C08J9/28C08J2201/0504C08J2351/00C08J2497/02C08K2003/3081C08K2201/003C08K2201/014C08L2205/16C08L97/02C08K13/02C08K3/36C08K3/30C08K5/053C08K5/1515C08F220/06
Inventor 顾子旭王招弟徐亮徐科峰杭渊胡健
Owner 宜兴丹森科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com