Polyethylene water supply pipe material and preparation method thereof

A polyethylene and water supply pipe technology, applied in the polymer field, can solve the problems of poor heat resistance and aging resistance, improve heat resistance and aging resistance, enhance heat resistance and aging resistance, improve The effect of dispersibility and UV absorption effect

Inactive Publication Date: 2018-05-29
长沙善道新材料科技有限公司
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The invention provides a PE composition; the pipe prepared by the PE composition has high tensile yield strength, good rigidity, excellent impac

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyethylene water supply pipe material and preparation method thereof
  • Polyethylene water supply pipe material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] The preparation method of above-mentioned polyethylene water supply pipe material, comprises the following steps:

[0026] (1) Preparation of composite filler: bake the superfine white carbon black at 100°C for 10h, then mix and stir with maleic anhydride grafted polyethylene, after cooling, mix with calcium sulfate whiskers, silane coupling agent, paraffin, Mix talcum powder, stir at 80-120°C for 30-40 minutes, cool to room temperature, and granulate with a particle size of 2-4 μm;

[0027] (2) Preparation of polyethylene water supply pipe material: mix high-density polyethylene, metallocene linear low-density polyethylene, composite filler, hydrogen-terminated silicone oil, hydroxyethyl acrylate, nano-manganese dioxide, and allyl glycidyl ether, Carry out high-speed kneading and kneading, raise the temperature to 110-130°C, and knead for 8-12 minutes, then put it into a cold mixer and stir until the temperature is 40-50°C, melt and extrude, cool, and shape to obtain. ...

Embodiment 1

[0030] The polyethylene water supply pipe material is composed of the following raw materials calculated in parts by mass: high-density polyethylene 80, metallocene linear low-density polyethylene 10, composite filler 10, hydrogen-terminated silicone oil 10, hydroxyethyl acrylate 8, nano-manganese dioxide 8. Allyl glycidyl ether 3; the composite filler is composed of the following raw materials calculated in parts by mass: calcium sulfate whisker 45, silane coupling agent 3, paraffin wax 3, talcum powder 35, superfine white carbon black 45 , Maleic anhydride grafted polyethylene 5. The particle diameter of the superfine white carbon black is 40nm, and the high-density polyethylene is polyethylene P6006N.

[0031] The preparation method of above-mentioned polyethylene water supply pipe material, comprises the following steps:

[0032] (1) Preparation of composite filler: bake the superfine white carbon black at 100°C for 10h, then mix and stir with maleic anhydride grafted pol...

Embodiment 2

[0035]A polyethylene water supply pipe material, which is composed of the following raw materials calculated in parts by mass: high-density polyethylene 85, metallocene linear low-density polyethylene 10, composite filler 15, hydrogen-terminated silicone oil 5, hydroxyethyl acrylate 10, nano Manganese dioxide 5, allyl glycidyl ether 1; wherein, the composite filler is composed of the following raw materials calculated in parts by mass: calcium sulfate whisker 35, silane coupling agent 3, paraffin wax 1, talcum powder 35, super Fine silica 35, maleic anhydride grafted polyethylene 5; the particle diameter of the superfine silica is 10nm, and the high-density polyethylene is polyethylene P6006N.

[0036] The preparation method of above-mentioned polyethylene water supply pipe material, comprises the following steps:

[0037] (1) Preparation of composite filler: bake the superfine white carbon black at 100°C for 10h, then mix and stir with maleic anhydride grafted polyethylene, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a polyethylene water supply pipe material and a preparation method thereof. The polyethylene water supply pipe material comprises the following raw materials: high density polyethylene, metallocene linear low density polyethylene, composite fillers, hydrogen-terminated silicone oil, hydroxyethyl acrylate, nano-manganese oxide and allyl glycidyl ether, wherein the mass ratioof the hydrogen-terminated silicone oil, the hydroxyethyl acrylate, the nano-manganese oxide to the allyl glycidyl ether is 5-15: 5-10: 5-10: 1-5. The preparation method comprises the following steps: preparation of the raw materials, mixing, molding and the like. Compared with the prior art, a product disclosed by the invention is further improved in the aspects of aging resistance and heat resistance.

Description

【Technical field】 [0001] The invention belongs to the technical field of polymers, and in particular relates to a polyethylene water supply pipe material and a preparation method thereof. 【Background technique】 [0002] Polyethylene pipes are more and more widely used in gas pipes due to their outstanding chemical corrosion resistance, low temperature resistance, heat resistance, wear resistance and welding performance, no pollution to the conveying medium, low manufacturing and installation costs, and long service life. Transportation, water supply, sewage, heat supply, agricultural irrigation and mine fine particle solid transportation and other fields. In addition to the above-mentioned properties, the most basic requirement for pressure pipelines is to have excellent hydrostatic resistance. [0003] For polyethylene pressure pipes, there are two forms that affect pipe damage, long-term creep damage and rapid crack growth damage. Among them, resistance to long-term cree...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/06C08L23/08C08L83/05C08L51/06C08K13/04C08K7/08C08K3/34C08K3/36C08K3/22C08K5/103C08K5/1515
CPCC08L23/06C08K2003/2262C08K2201/011C08L2201/08C08L2203/18C08L2205/035C08L2207/062C08L2312/00C08L23/0815C08L83/04C08L51/06C08K13/04C08K7/08C08K3/34C08K3/36C08K3/22C08K5/103C08K5/1515
Inventor 不公告发明人
Owner 长沙善道新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap