Method for manufacturing floor

A manufacturing method and flooring technology, applied in floor coverings, chemical instruments and methods, paper/cardboard layered products, etc., can solve problems such as magnetic field radiation, high energy consumption, and excessive formaldehyde, so as to enhance floor strength and eliminate The effect of formaldehyde

Inactive Publication Date: 2018-06-12
DUYUN NUANDONG WATER HEATING FLOOR
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The production method solves the problems of excessive formaldehyde, magnetic field radiation, high energy consumption and single function existing in the current floor heating process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for manufacturing floor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Embodiment 1 of the present invention: a kind of floor making method, as attached figure 1 As shown, there is a substrate layer, the bottom of the substrate layer is provided with a plurality of open water tanks along the length direction of the floor, and the surface of the substrate layer is provided with wood grain paper; wherein the substrate layer uses the following weight component ratio Raw materials: PVC resin 40kg, wood fiber 50kg, stearic acid 1kg, calcium zinc stabilizer 3kg, epoxy soybean oil 1kg, stone powder 50kg.

[0013] When making the floor, mix PVC resin, wood fiber, stearic acid, calcium-zinc stabilizer, epoxy soybean oil, and stone powder, then sol the mixed material at a temperature of 180°C, and then extrude the sol through a mold to obtain a base After the base layer is finalized, the surface is covered with wood grain paper, and finally cut to obtain the desired floor.

[0014] The thickness ratio of wood grain paper to substrate layer is 1:18....

Embodiment 2

[0016] Embodiment 2 of the present invention: a kind of floor making method, as attached figure 1 As shown, there is a substrate layer, the bottom of the substrate layer is provided with a plurality of open water tanks along the length direction of the floor, and the surface of the substrate layer is provided with wood grain paper; wherein the substrate layer uses the following weight component ratio Raw materials: PVC resin 60kg, wood fiber 20kg, stearic acid 3kg, calcium zinc stabilizer 1kg, epoxy soybean oil 3kg, stone powder 30kg.

[0017] When making the floor, mix PVC resin, wood fiber, stearic acid, calcium-zinc stabilizer, epoxy soybean oil, and stone powder, then sol the mixed material at a temperature of 250°C, and then extrude the sol from a mold to obtain a base After the base layer is finalized, the surface is covered with wood grain paper, and finally cut to obtain the desired floor.

[0018] The thickness ratio of wood grain paper to substrate layer is: 1:25. ...

Embodiment 3

[0020] Embodiment 3 of the present invention: a kind of floor making method, as attached figure 1 As shown, there is a substrate layer, the bottom of the substrate layer is provided with a plurality of open water tanks along the length direction of the floor, and the surface of the substrate layer is provided with wood grain paper; wherein the substrate layer uses the following weight component ratio Raw materials: PVC resin 50kg, wood fiber 35kg, stearic acid 2kg, calcium zinc stabilizer 2kg, epoxy soybean oil 2kg, stone powder 40kg.

[0021] When making the floor, mix PVC resin, wood fiber, stearic acid, calcium-zinc stabilizer, epoxy soybean oil, and stone powder, then sol the mixed material at a temperature of 220°C, and then extrude the sol from a mold to obtain a base After the base layer is finalized, the surface is covered with wood grain paper, and finally cut to obtain the desired floor.

[0022] The thickness ratio of wood grain paper to substrate layer is 1:22.

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for manufacturing a floor. A base material layer is included. A plurality of open-type water tanks are arranged at the bottom of the base material layer in the lengthdirection of the floor, and wood grained paper is arranged on the surface of the base material layer. The base material layer is prepared from following raw materials of, by weight, 40-60 parts of PVCresin, 20-50 parts of wood fibers, 1-3 parts of stearic acid, 1-3 parts of calcium zinc stabilizers, 1-3 parts of epoxidized soybean oil and 30-50 parts of stone powder. PVC plastic is used as a binder and does not contain formaldehyde, the stone powder is used as a filler, and thus the strength of the floor is reinforced. The open-type water tanks are arranged at the bottom of the floor and thusthe problems brought by the situation that as for an original ground heating floor, the water tanks are designed in the middles of plates in a penetrating mode are solved, wherein the problems comprise that 1, when water pipes are mounted, penetrated and inserted, troubles are caused, the labor is consumed, the labor cost is high, and the larger is the floor area, the larger is the workload; 2, when the water pipes are penetrated, inserted and pulled, the water pipes are likely to be damaged, and thus the hidden danger of water leakage is left; and 3, the ground heating floor is likely to contain formaldehyde.

Description

technical field [0001] The invention relates to a method for making a floor, which belongs to the technical field of floors. Background technique [0002] Floors have been widely used in building decoration, and floors are divided into many types according to different uses. The floor heating floor is one of them, but there are the following problems in the commonly used floor heating floors on the market: Enhanced floor: Due to the needs of the production process, the floor must use glue as an adhesive. The glue contains formaldehyde. play small. When used as a floor heating floor, the environment is around 40°C to 50°C, so the volatilization of formaldehyde is large; heating tiles: they generate heat due to the passage of current, so there are electromagnetic fields and radiation hazards; the heating floor still needs to be covered with a floor. Not only is the installation complicated, but also the cost is high. At the same time, there is a fatal disadvantage - radiatio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04F15/10C08L27/06C08L97/02C08L91/00C08K5/09C08K3/26B32B3/30B32B27/06B32B27/18B32B27/30B32B29/00
CPCE04F15/10B32B3/30B32B27/06B32B27/18B32B27/306B32B29/002B32B2471/00C08L27/06C08L2205/03C08L2205/16E04F15/107C08L97/02C08L91/00C08K5/09C08K2003/265