High-transmittance and blue light-proof eye protection eyeglass and production method thereof

A high transmittance, anti-blue light technology, applied in glasses/goggles, optics, optical components, etc., to achieve the effect of soft and comfortable light and simple process

Active Publication Date: 2018-06-15
JIANGSU MAAT OPTICAL CO LTD
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the existing technology, the requirements of reducing blue light damage and increasing light transmittance are often incompatible. One loses the other, and one trades off. In order to reduce blue light damage, the light transmittance must be sacrificed as a price

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] High-transmittance anti-blue light goggles raw materials (parts by weight): 100 parts of resin monomer, 2 parts of ultraviolet absorber, 1 part of blue light absorber, 1 part of anti-reflection agent, and 1 part of initiator.

[0039] The resin monomer is a bisallyl diglycol dicarbonate monomer with a refractive index of 1.49.

[0040] The initiator is diisopropyl peroxydicarbonate.

[0041] The anti-reflection agent is titanium dioxide.

[0042] The blue light absorber is zirconia.

[0043] The ultraviolet absorber is a rare earth complex, and the rare earth complex is a binary rare earth complex.

[0044] The rare earth binary complex is prepared by the following method: Weigh 52.79g of europium carbonate and 134.55g of dibenzoylmethane, place it in a planetary ball mill for ball milling, select ceramic ball mill pots and ceramic balls, and the mass ratio of the ball to material is 20:1, the ball milling speed is 500 rpm, and the ball milling time is 4 hours to obt...

Embodiment 2

[0052] High-transmittance anti-blue light goggles raw materials (parts by weight): 100 parts of resin monomer, 2 parts of ultraviolet absorber, 1 part of blue light absorber, 1 part of anti-reflection agent, and 1 part of initiator.

[0053] The resin monomer is a bisallyl diglycol dicarbonate monomer with a refractive index of 1.49.

[0054] The initiator is diisopropyl peroxydicarbonate.

[0055] The anti-reflection agent is titanium dioxide.

[0056] The blue light absorber is modified zirconia.

[0057] The ultraviolet absorber is a rare earth complex, and the rare earth complex is a binary rare earth complex.

[0058] The rare earth binary complex is prepared by the following method: Weigh 52.79g of europium carbonate and 134.55g of dibenzoylmethane, place it in a planetary ball mill for ball milling, select ceramic ball mill pots and ceramic balls, and the mass ratio of the ball to material is 20:1, the ball milling speed is 500 rpm, and the ball milling time is 4 hou...

Embodiment 3

[0071] High-transmittance anti-blue light goggles raw materials (parts by weight): 100 parts of resin monomer, 2 parts of ultraviolet absorber, 1 part of blue light absorber, 1 part of anti-reflection agent, and 1 part of initiator.

[0072] The resin monomer is a bisallyl diglycol dicarbonate monomer with a refractive index of 1.49.

[0073] The initiator is diisopropyl peroxydicarbonate.

[0074] The anti-reflection agent is titanium dioxide.

[0075] The blue light absorber is modified zirconia.

[0076] The ultraviolet absorber is a rare earth complex, and the rare earth complex is a binary rare earth complex.

[0077] The rare earth binary complex is prepared by the following method: Weigh 52.79g of europium carbonate and 134.55g of dibenzoylmethane, place it in a planetary ball mill for ball milling, select ceramic ball mill pots and ceramic balls, and the mass ratio of the ball to material is 20:1, the ball milling speed is 500 rpm, and the ball milling time is 4 hou...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
hazeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-transmittance blue light-proof eye protection eyeglass and a production method thereof. The high-transmittance blue light-proof eye protection eyeglass comprises a resinmonomer, an ultraviolet ray absorber, a blue light absorbent, a transparent agent and an initiator. The high-transmittance blue light-proof eye protection eyeglass and the production method thereof have a simple process, effectively reduce damages of blue lights and ultraviolet rays to human retinas on the premise of guaranteeing the light transmittance of the eyeglass to make the lights soft andcomfortable in order to achieve eye protection.

Description

technical field [0001] The invention belongs to the field of resin lenses, in particular to a high-transmittance anti-blue light goggle lens and a preparation method thereof. Background technique [0002] At present, with the advancement of science and technology, human beings have entered the information age, and major changes have taken place in the way of learning, working and living. Among them, the dependence on vision is getting higher and higher, and the burden of vision is getting heavier and heavier. People's study, work, and entertainment are increasingly inseparable from computers, TVs, mobile phones, etc. The display screens of these electronic products have high blue light radiation components, which can cause great damage to visual cells, and are an ever-changing source of light radiation. [0003] Light wavelengths in the range of 400-700nm are visible to the human eye, those with wavelengths shorter than 400nm are ultraviolet rays, those with wavelengths lon...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F118/00C08F2/44C08K3/22C08K3/26G02C7/02G02C7/10
CPCC08F2/44C08F118/00C08K3/22C08K3/26C08K2003/2241C08K2003/2244G02C7/022G02C7/10
Inventor 彭裕民
Owner JIANGSU MAAT OPTICAL CO LTD