High-wear resistance water-based deck paint

A deck paint, high wear-resistant technology, applied in coatings, polyurea/polyurethane coatings, etc., can solve the problems of ship personnel who are prone to slip and fall injuries, aggravate ship equipment wear, and deck cleaning difficulties, etc., to achieve excellent mechanical and physical properties, High impact strength and short construction period

Inactive Publication Date: 2018-07-20
ANHUI KAILIN ADVANCED MATERIAL CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Ships sailing on the sea are inevitably shaken and turbulent by the influence of waves and strong winds. Ship personnel are prone to slip and get injured when doing work. In order to improve the anti-skid ability of the deck, in the prior art, the Apply anti-skid paint for anti-skid, which has a certain anti-skid effect to a certain extent
In order to obtain excellent wear resistance and anti-skid properties, ship manufacturers use a large number of anti-skid fillers with high hardness and large particles. Although it can increase the anti-skid performance of the deck, it will aggravate the wear and tear of ship equipment and bring the cleaning of the deck. some difficulties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A high wear-resistant water-based deck paint. The raw materials are composed of 20 parts by weight of silicone polyurethane resin, 15 parts of vinyl acrylate, 12 parts of acrylic resin, 9 parts of xylene, 3 parts of alumina, and 7 parts of zinc oxide. , 17 parts of pigments, 48 ​​parts of ethanol, 30 parts of fillers, 16 parts of sodium lauryl sulfate, 1 part of anhydrous xylene, 40 parts of isopropanol.

[0024] The pigment is phthalocyanine blue, titanium white slurry, and carbon black slurry.

[0025] A production process of high wear-resistant water-based deck paint, the specific steps are as follows:

[0026] (1) 20 parts of silicone polyurethane resin, 15 parts of vinyl acrylate and 12 parts of acrylic resin are stirred at 100°C for 20 minutes;

[0027] (2) Add 9 parts of xylene and 3 parts of alumina, and heat the mixture to 130°C at a heating rate of 20°C / min;

[0028] (3) Add 7 parts of zinc oxide, and heat the mixture to 145°C at a heating rate of 30°C / min;

[0029] (4)...

Embodiment 2

[0037] A high wear-resistant water-based deck paint, the raw materials are composed of 25 parts by weight of silicone polyurethane resin, 10 parts of vinyl acrylate, 14 parts of acrylic resin, 6 parts of xylene, 5 parts of alumina, 4 parts of zinc oxide , 21 parts of pigments, 40 parts of ethanol, 45 parts of fillers, 13 parts of sodium lauryl sulfate, 2 parts of anhydrous xylene, 37 parts of isopropanol.

[0038] The pigment is phthalocyanine blue, titanium white slurry, and carbon black slurry.

[0039] A production process of high wear-resistant water-based deck paint, the specific steps are as follows:

[0040] (1) Stir 25 parts of silicone polyurethane resin, 10 parts of vinyl acrylate, and 14 parts of acrylic resin at 80°C for 30 minutes;

[0041] (2) Add 6 parts of xylene and 5 parts of alumina, and heat the mixture to 100°C at a heating rate of 20°C / min;

[0042] (3) Add 4 parts of zinc oxide, and heat the mixture to 160°C at a heating rate of 30°C / min;

[0043] (4) Add 40 parts...

Embodiment 3

[0051] A high wear-resistant water-based deck paint, the raw materials are composed of 24 parts by weight of silicone polyurethane resin, 13 parts of vinyl acrylate, 12 parts of acrylic resin, 9 parts of xylene, 3 parts of alumina, 7 parts of zinc oxide , 17 parts of pigments, 44 parts of ethanol, 38 parts of fillers, 15 parts of sodium lauryl sulfate, 1 part of anhydrous xylene, 39 parts of isopropanol.

[0052] The pigment is phthalocyanine blue, titanium white slurry, and carbon black slurry.

[0053] A production process of high wear-resistant water-based deck paint, the specific steps are as follows:

[0054] (1) Stir 24 parts of silicone polyurethane resin, 13 parts of vinyl acrylate and 12 parts of acrylic resin at 96°C for 27 minutes;

[0055] (2) Add 9 parts of xylene and 3 parts of alumina, and heat the mixture to 110°C at a heating rate of 20°C / min;

[0056] (3) Add 7 parts of zinc oxide, and heat the mixture to 150°C at a heating rate of 30°C / min;

[0057] (4) After adding 4...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
adhesivityaaaaaaaaaa
wear resistanceaaaaaaaaaa
wear resistanceaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-wear-resistance water-based deck paint. The high-wear-resistance water-based deck pain comprises, by weight, 20-25 parts of silicone polyurethane resin, 10-15 parts ofvinyl acrylate, 12-14 parts of acrylic resin, 6-9 parts of xylene, 3-5 parts of alumina, 4-7 parts of zinc oxide, 17-21 parts of a pigment, 40-48 parts of ethanol, 30-45 parts of a filler, 13-16 partsof sodium lauryl sulfate, 1-2 parts of anhydrous xylene and 37-40 parts of isopropyl alcohol. The high-wear resistance water-based deck paint has the advantages of outstanding anti-wear and anti-skidperformances, effectiveness in skid prevention, strong adhesion, excellent mechanical and physical performances, good flexibility, high impact strength and unique wear resistance; and the fineness ofthe deck paint produced in the invention is equal to or less than 25 [mu]m, so the deck paint can effectively prevent skid to ensure the safety of the environment, and also can effectively protect the ship devices to effectively avoiding the wearing of the devices.

Description

Technical field [0001] The invention relates to a high wear-resistant water-based deck paint, which belongs to the technical field of chemical products. Background technique [0002] Ships sailing on the sea are inevitably affected by waves and strong winds to produce sway and turbulence. Ship personnel are easy to slip and get injured while working. In order to improve the anti-skid ability of the deck, the existing technology is usually on the deck. The anti-slip paint is applied to prevent slip, which has a certain anti-slip effect to a certain extent. In order to obtain excellent wear resistance and anti-slip properties, the anti-slip coating uses a large number of anti-slip fillers with high hardness and large particles. Although it can increase the anti-slip performance of the deck, it will aggravate the abrasion of ship equipment and bring about the cleaning of the deck A certain difficulty. Summary of the invention [0003] In view of the shortcomings in the prior art, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D133/00C09D7/61C09D7/63
CPCC09D175/04C08K2003/2227C08K2003/2241C08K2003/2296C08L33/00C08K13/02C08K3/22C08K5/41C08K3/36C08K3/346C08K3/04
Inventor 王和山王厚国王和东黄义朝黄开仁施保兵李洪陈发东殷芳荣
Owner ANHUI KAILIN ADVANCED MATERIAL CO LTD