A concrete external curing agent

A curing agent and concrete technology, which is applied in the field of building materials, can solve the problems of inability to further improve concrete performance, ecological environment pollution, poor stability, etc., and achieve the effects of improving hardness and elasticity, increasing specific surface area, and strengthening stability.

Active Publication Date: 2021-06-22
浙江研翔新材料有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem mainly solved by the present invention is: in view of the poor stability of the traditional concrete external curing agent in the storage process, resulting in the inability to further improve the performance of the concrete after curing, and the problem that the ecological environment is easily polluted after use, a concrete curing agent is provided. External curing agent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A concrete external curing agent

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0032] In parts by weight, take 8 parts of β-sitosterol, 8 parts of phospholipids, 40 parts of water, 50 parts of vegetable oil, 15 parts of dry oil, 6 parts of polyallylamine, 0.3 part of defoamer, 8 parts of calcium bicarbonate , first pour the vegetable oil into the No. 1 beaker, and then move the No. 1 beaker into a digital speed measuring and constant temperature magnetic stirrer. At a temperature of 85 ° C and a speed of 500 r / min, stir and preheat for 30 minutes, and then add β-glucose Pour the sterols and phospholipids into the No. 2 beaker, stir and mix with a glass rod for 30 minutes, and then pour the materials in the No. 2 beaker into the No. 1 beaker under constant temperature stirring, then add dry oil into the No. 1 beaker, and continue to keep the temperature constant Stir and mix for 60 minutes to obtain the oil phase; mix water and polyallylamine into No. 3 beaker, stir and mix with a glass rod for 30 minutes, add calcium bicarbonate to No. 3 beaker, and then ...

example 2

[0034]In parts by weight, take 40 parts of water, 50 parts of vegetable oil, 15 parts of dry oil, 6 parts of polyallylamine, 0.3 part of defoamer, 8 parts of calcium bicarbonate, and pour the vegetable oil into No. 1 beaker. And move the No. 1 beaker into the digital display speed measuring constant temperature magnetic stirrer, under the condition of the temperature of 85 ℃ and the rotation speed of 500r / min, stir and preheat for 30 minutes, then add dry oil into the No. 1 beaker, and continue to stir and mix at constant temperature for 60 minutes , to obtain the oil phase; mix water and polyallylamine into No. 3 beaker, stir and mix with a glass rod for 30 minutes, add calcium bicarbonate into No. 3 beaker, and then move No. , at a temperature of 80°C and a rotation speed of 600r / min, stir and preheat at a constant temperature for 30 minutes to obtain the water phase; then transfer the water phase to a mixer, and at a temperature of 85°C and a stirring speed of 800r / min Next...

example 3

[0036] In parts by weight, take 8 parts of β-sitosterol, 8 parts of phospholipids, 40 parts of water, 50 parts of vegetable oil, 6 parts of polyallylamine, 0.3 part of defoamer, 8 parts of calcium bicarbonate, and pour the vegetable oil into Put the No. 1 beaker into the digital display speed measuring constant temperature magnetic stirrer, under the condition of temperature 85 ℃ and rotation speed 500r / min, stir and preheat for 30min, then pour β-sitosterol and phospholipid into 2 In the No. beaker, stir and mix with a glass rod for 30 minutes, under constant temperature stirring, pour the material in the No. In the No. 3 beaker, stir and mix with a glass rod for 30 minutes, then add calcium bicarbonate into the No. 3 beaker, and then move the No. 3 beaker into a digital speed measuring constant temperature magnetic stirrer, at a temperature of 80 ° C and a speed of 600 r / min. , stirring at constant temperature and preheating for 30 minutes to obtain the water phase; then tra...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a concrete external curing agent, which belongs to the technical field of building materials. The external curing agent for concrete developed by the present invention is mainly composed of β-sitosterol, phospholipid, water, vegetable oil, drying oil, polyallylamine, defoamer and calcium bicarbonate, and after first stirring and mixing the β-sitosterol and phospholipid , pour into the preheated vegetable oil, then add dry oil to obtain an oil phase; stir and mix water and polyallylamine, then add calcium bicarbonate, preheat to obtain a water phase; Add the oil phase to the water phase. After the oil phase is added, add the defoamer, continue stirring and mixing at a constant temperature for 40-60 minutes, discharge, and fill to obtain the concrete external curing agent. The product developed by the invention has good storage stability, can significantly improve the performance of the concrete after curing, and does not cause secondary pollution to the environment after use.

Description

technical field [0001] The invention discloses a concrete external curing agent, which belongs to the technical field of building materials. Background technique [0002] Concrete is one of the most widely used building materials in construction projects. Its performance depends not only on the composition and ratio of raw materials, but also on later maintenance. If the concrete is not maintained in time after construction, its internal moisture will pass through the system. The capillary pores evaporate to the outside world, resulting in insufficient hydration of the cementitious material and reduction of hydration products, which in turn causes the performance of concrete to decline. Therefore, curing is crucial to the development of concrete properties and must be taken seriously. [0003] Traditional concrete curing methods mainly include water curing, steam curing, landfill curing and plastic film covering, etc. This kind of curing method is time-consuming, laborious,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B40/04
CPCC04B40/04
Inventor 林正脉许玉
Owner 浙江研翔新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More