Seal rubber mat capable of preventing salt corrosion and preparation method thereof

A technology for sealing rubber pads and anti-salt, applied in the field of sealing rubber pads, can solve the problems of device sealing effect, device corrosion, and device sealing deterioration, etc., and achieve the effects of prolonging service life, improving fluidity and saving costs.

Inactive Publication Date: 2018-08-28
SHANDONG LIANXING ENERGY GRP CO LTD
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The main function of the sealing pad applied to the equipment is to seal between the components on the equipment and reduce the wear and tear of the components on the equipment. When the equipment is in a humid environment, the salt dissolved in water will affect the sealing pad on the equipment. Corrosion, corrosion causes crystallized salts to adhere to the surface of the sealing rubber pad, rough surface of the sealing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A salt-corrosion-resistant sealing rubber pad, comprising the following components in parts by weight: 80 parts of silicone rubber, 20 parts of fluororubber, 1.5 parts of anti-aging agent DNP, 2 parts of anti-aging agent CMA, 30 parts of white carbon black, calcium carbonate 5 parts, 2 parts of iron oxalate, 1 part of accelerator NOBS, 0.5 parts of accelerator DPTH, 2 parts of tert-butyl perbenzoate, 1 part of benzoyl peroxide, and 0.5 parts of epoxy resin.

[0017] The preparation method of the above-mentioned anti-salt corrosion sealing rubber pad, the steps are as follows:

[0018] (1) Cut the dried fluororubber into pieces with a size range of 10-20kg, put them into the internal mixer for plasticizing, and the temperature for plasticizing is 130°C to obtain plasticized rubber, park for 22 hours, and set aside;

[0019] (2) Put the plasticized rubber into the open mill, and put in the silicone rubber, start rolling to make the fluororubber and silicone rubber mix eve...

Embodiment 2

[0029] An anti-salt corrosion sealing rubber pad, comprising the following components in parts by weight: 75 parts of silicone rubber, 25 parts of fluororubber, 1 part of anti-aging agent DNP, 1.5 parts of anti-aging agent CMA, 20 parts of white carbon black, calcium carbonate 3 parts, 1 part of iron oxalate, 0.7 parts of accelerator NOBS, 0.3 parts of accelerator DPTH, 1.5 parts of tert-butyl perbenzoate, 0.5 parts of benzoyl peroxide, and 0.3 parts of epoxy resin.

[0030] The preparation method of the above-mentioned anti-salt corrosion sealing rubber pad, the steps are as follows:

[0031] (1) Cut the dried fluororubber into pieces with a size range of 10-20kg, put them into the internal mixer for plasticizing, and the temperature for plasticizing is 120°C to obtain plasticized rubber, park it for 20 hours, and set aside;

[0032] (2) Put the plasticized rubber into the open mill, and put in the silicone rubber, start rolling to make the fluororubber and silicone rubber mi...

Embodiment 3

[0036] An anti-salt corrosion sealing rubber pad, comprising the following components in parts by weight: 85 parts of silicone rubber, 25 parts of fluororubber, 2 parts of anti-aging agent DNP, 2.5 parts of anti-aging agent CMA, 40 parts of white carbon black, calcium carbonate 7 parts, 3 parts of iron oxalate, 1.3 parts of accelerator NOBS, 0.7 parts of accelerator DPTH, 2.5 parts of tert-butyl perbenzoate, 1.5 parts of benzoyl peroxide, and 0.7 parts of epoxy resin.

[0037] The preparation method of the above-mentioned anti-salt corrosion sealing rubber pad, the steps are as follows:

[0038] (1) Cut the dried fluororubber into pieces with a size range of 10-20kg, put them into the internal mixer for plasticizing, and the temperature for plasticizing is 140°C to obtain plasticized rubber, park for 24 hours, and set aside;

[0039] (2) Put the plasticized rubber into the open mill, and put in the silicone rubber, start rolling to make the fluororubber and silicone rubber mix...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a seal rubber mat capable of preventing salt corrosion. The seal rubber mat is made from silicone rubber, fluororubber, an anti-aging agent DNP, an anti-aging agent CMA, white carbon black, calcium carbonate, iron oxalate, an accelerator NOBS, an accelerator DPTH, t-butyl perbenzoate, benzoyl peroxide and epoxy resin. The preparation method comprises the steps that (1) the fluororubber is subjected to plastication; (2) after the plastication, the fluororubber is mixed with the silicone rubber and other components in an open mill for mixing; (3) the rubber compound is subjected to remilling; (4) extrusion forming and vulcanization are carried out, and the seal rubber mat is obtained. The seal rubber mat has the advantages of smooth surfaces, strong resistance to corrosion and long service life, simple preparation process, reasonable components and safe production during the preparing process.

Description

technical field [0001] The invention relates to the technical field of sealing rubber pads, in particular to a salt corrosion-resistant sealing rubber pad and a preparation method thereof. Background technique [0002] The main function of the sealing pad applied to the equipment is to seal between the components on the equipment and reduce the wear and tear of the components on the equipment. When the equipment is in a humid environment, the salt dissolved in water will affect the sealing pad on the equipment. Corrosion, corrosion causes crystallized salts to adhere to the surface of the sealing rubber pad, rough surface of the sealing rubber pad, etc. These conditions will not only affect the sealing between the devices, but also cause wear on the device itself during the vibration of the equipment and corrosion. In addition, the rough surface of the sealing rubber pad leads to poor sealing between devices. Therefore, how to provide a sealing rubber pad with a smooth surfa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L83/04C08L27/12C08K13/02C08K3/36C08K3/26C08K5/098C08K5/14B29B7/72
CPCB29B7/728C08K2003/265C08L83/04C08L2205/03C08L27/12C08K13/02C08K3/36C08K3/26C08K5/098C08K5/14
Inventor 车春玲
Owner SHANDONG LIANXING ENERGY GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap