A method for improving flame retardancy and mechanical properties of polyethylene/nylon 6 blends

A technology of polyethylene and blends, which is applied in the field of polymer composite material preparation, can solve the problems that flame retardancy and compatibilization efficiency cannot be taken into account at the same time, and achieve the goal of improving application value, flame retardancy and mechanical properties Effect

Active Publication Date: 2021-02-09
HENAN UNIV OF SCI & TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical purpose of the present invention is to prepare a polyethylene / nylon 6 blend with excellent flame retardancy, high compatibilization efficiency, and significantly improved mechanical properties of the finished material by adding the blending sequence of raw materials and improving the processing and preparation process to solve the technical problem that the flame retardancy and compatibilization efficiency of polyethylene / nylon 6 blends in the prior art cannot be taken into account at the same time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for improving flame retardancy and mechanical properties of polyethylene/nylon 6 blends
  • A method for improving flame retardancy and mechanical properties of polyethylene/nylon 6 blends
  • A method for improving flame retardancy and mechanical properties of polyethylene/nylon 6 blends

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] The polyethylene / nylon 6 blend of present embodiment adopts following method to make:

[0039]Weigh a certain amount of linear low density polyethylene (LLDPE), nylon 6 (PA6), PE-g-MAH (solubilizer), ammonium polyphosphate (APP), pentaerythritol according to the ratio of 62:16:2:16:4 (PER), within the temperature range of 220~240°C, the twin-screw extruder is used to melt the mixed material to prepare the corresponding blend, and it is molded in the corresponding molding processing equipment at the temperature range of 220~240°C. Preparation of products. The mechanical properties and flame retardant properties tested are shown in Table 1.

Embodiment 2

[0041] The polyethylene / nylon 6 blend of present embodiment adopts following method to make:

[0042] Weigh a certain amount of linear low density polyethylene (LLDPE), nylon 6 (PA6), PE-g-MAH (solubilizer), ammonium polyphosphate (APP), pentaerythritol according to the ratio of 59:15:5:16:4 (PER), within the temperature range of 220~240°C, the twin-screw extruder is used to melt the mixed material to prepare the corresponding blend, and it is molded in the corresponding molding processing equipment at the temperature range of 220~240°C. Preparation of products. The mechanical properties and flame retardant properties tested are shown in Table 1.

Embodiment 3

[0044] The polyethylene / nylon 6 blend of present embodiment adopts following method to make:

[0045] Weigh a certain amount of linear low density polyethylene (LLDPE), nylon 6 (PA6), PE-g-MAH (solubilizer), ammonium polyphosphate (APP), pentaerythritol according to the ratio of 56:17:8:16:4 (PER), within the temperature range of 220~240°C, the twin-screw extruder is used to melt the mixed material to prepare the corresponding blend, and it is molded in the corresponding molding processing equipment at the temperature range of 220~240°C. Preparation of products. The mechanical properties and flame retardant properties tested are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A method for improving the flame retardancy and mechanical properties of polyethylene / nylon 6 blends, the method adopts a two-step step-by-step melt blending method, which can control the uniform distribution of intumescent flame retardants in polyethylene / nylon 6 blends In the nylon 6 phase domain in the blend, the flame retardant performance of the blend is greatly improved. Compared with the one-step processing method in the prior art, the limiting oxygen index of the polyethylene / nylon 6 blend prepared by the step-by-step processing method of the present invention can be improved by 15.6%-21.5%, and the resistance of the blend The combustion level can not be raised to above V-1 level by vertical combustion, thus greatly improving its application value. The technical problem that the flame retardancy and compatibilization efficiency of the polyethylene / nylon 6 blend cannot be simultaneously considered in the prior art is solved.

Description

technical field [0001] The invention relates to the technical field of preparation of polymer composite materials, in particular to a method for improving the flame retardancy and mechanical properties of polyethylene / nylon 6 blends. Background technique [0002] Blending different types of polymer materials to prepare polymer alloys is a common means to improve the properties of polymer materials. Blending a small amount of nylon 6 with polyethylene can improve the defects of polyethylene such as poor heat resistance, easy creep at high temperature, and low mechanical strength. However, due to the poor compatibility between polyethylene and nylon 6, it is necessary to add a certain amount of solubilizer to improve the compatibility of the two, so as to achieve the purpose of utilizing the properties of nylon modified polyethylene. [0003] Both polyethylene and nylon 6 are flammable polymer materials. When heated at high temperature, they will degrade into low molecular we...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/08C08L77/02C08L51/06C08K3/32C08K5/053
CPCC08K2003/323C08L23/0815C08L2201/02C08L2205/03C08L2205/08C08L77/02C08L51/06C08K3/32C08K5/053
Inventor 陆昶高喜平黄新辉赵盼张帅姚大虎赫玉欣曹成林田训宇
Owner HENAN UNIV OF SCI & TECH