Environmentally friendly diatom mud wall material and preparation method thereof

A diatom mud and wall material technology, applied in the field of interior decoration coatings, can solve the problems of diatom mud wall materials, such as easy to drop powder, low strength, and not resistant to dirt, achieve good adsorption and degradation functions, improve water repellency, reduce The effect of surface cracks

Inactive Publication Date: 2018-09-25
杨显武
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a kind of environmental protection diatom ooze wall material and preparation method thereof, the preparation process of this diatom ooze wall material is easy to operate, the produced diatom ooze wall materi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0025] Example 1

[0026] An environmentally friendly diatom mud wall material, mainly made of the following raw materials by weight: 50 parts by weight of diatomaceous earth, 10 parts of nano-titanium dioxide, 10 parts of heavy calcium, 5 parts of wollastonite powder, 5 parts of quartz powder, 4 parts of attapulgite powder Parts, 4 parts of gray calcium powder, 4 parts of graphene, 3 parts of propyl gallate, 2 parts of anion powder, 2 parts of sodium hexametaphosphate dispersant, 5 parts of surface modifier, 5 parts of mildew and antibacterial agent, inorganic aluminum 2 parts of salt water resistant agent and 5 parts of binder;

[0027] The surface modifier is made by mixing sodium lauryl sulfate, sodium palmitoylglycinate and stearic acid in a mass ratio of 2:2:1;

[0028] The anti-mold and antibacterial agent is prepared by the following method: Wash 40 parts of aloe vera, 20 parts of cloves, 15 parts of Eucalyptus urophylla and 5 parts of vanilla, pulverize, pass through a 100-...

Example Embodiment

[0038] Example 2

[0039] An environmentally friendly diatom mud wall material, mainly made of the following raw materials by weight: 75 parts by weight of diatomaceous earth, 13 parts of nano-titanium dioxide, 12 parts of heavy calcium, 9 parts of wollastonite powder, 8 parts of quartz powder, 8 parts of attapulgite powder Parts, 8 parts of gray calcium powder, 6 parts of graphene, 7 parts of propyl gallate, 7 parts of anion powder, 15 parts of acrylic ammonium salt dispersant, 9 parts of surface modifier, 10 parts of mildew and antibacterial agent, urea-formaldehyde resin water-resistant agent 7 parts and 8 parts binder; of which,

[0040] The surface modifier is made by mixing sodium lauryl sulfate, sodium palmitoylglycinate and stearic acid in a mass ratio of 2:2:1;

[0041] The anti-mildew and antibacterial agent is prepared by the following method: Wash 50 parts of aloe vera, 35 parts of cloves, 25 parts of Eucalyptus grandis and 15 parts of vanilla, pulverize, pass through a ...

Example Embodiment

[0051] Example 3

[0052] An environmentally friendly diatom mud wall material, which is mainly made of the following raw materials by weight: 70 parts by weight of diatomaceous earth, 12 parts of nano-titanium dioxide, 11 parts of heavy calcium, 8 parts of wollastonite powder, 7 parts of quartz powder, 7 parts of attapulgite powder Parts, 6 parts of gray calcium powder, 5.5 parts of graphene, 6 parts of propyl gallate, 6 parts of anion powder, 10 parts of dispersant composed of ammonium acrylate and styrene acrylic copolymer, 8 parts of surface modifier, anti 9 parts of mildew antibacterial agent, 6 parts of inorganic aluminum salt water-resistant agent and 7 parts of binder;

[0053] The surface modifier is made by mixing sodium lauryl sulfate, sodium palmitoylglycinate and stearic acid in a mass ratio of 2:2:1;

[0054] The anti-mold and antibacterial agent is prepared by the following method: wash 48 parts of aloe vera, 34 parts of cloves, 24 parts of Eucalyptus urophylla and 14...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Particle sizeaaaaaaaaaa
Finenessaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of indoor decoration coating, and relates to an environmentally friendly diatom mud wall material. The material is mainly prepared from, by weight, 50-75 parts of diatomite, 10-13 parts of nanometer titanium dioxide, 10-12 parts of ground calcium carbonate, 5-9 parts of wollastonite powder, 5-8 parts of quartz powder, 4-8 parts of attapulgite powder, 4-8 parts ofsierozem powder, 4-6 parts of graphene, 3-7 parts of propyl gallate, 2-7 parts of negative ion powder, 2-15 parts of a dispersant, 5-9 parts of a surface modifier, 5-10 parts of a mildew-proof antibacterial agent, 2-7 parts of a water resistant agent and 5-8 parts of a binder. The preparation process of the diatom mud wall material is simple, and the diatom mud wall material produced has better mildew-proof and antibacterial properties and excellent strength, flexibility and crack resistance, and overcomes technical problems including easy powder falling, easy cracking, low strength and no stain resistance of diatom mud wall materials.

Description

technical field [0001] The invention belongs to the field of interior decoration coatings, and in particular relates to an environment-friendly diatom mud wall material and a preparation method thereof. Background technique [0002] The main component of diatom mud is diatomaceous earth, and the main component of diatomaceous earth is diatoms. Diatoms are the first single-celled algal organisms that appeared on the earth. They live in seawater or lake water, and their shapes are extremely small. The main component of diatom mud is protein, which is rich in a variety of beneficial minerals and has a soft texture. Use an electron microscope to observe diatom mud. Diatom mineral is a micron-scale porous material. There are countless tiny holes on the surface of the particles, which are regularly and neatly arranged in circles and needles, with a porosity of more than 90. The number of micropores is thousands of times more than that of charcoal. This molecular sieve structure...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/14C04B111/20C04B111/34
CPCC04B28/14C04B2111/00017C04B2111/00025C04B2111/00482C04B2111/2092C04B2111/343C04B2201/10C04B2201/50C04B14/08C04B14/305C04B14/28C04B14/043C04B14/06C04B14/102C04B22/064C04B14/024C04B24/045C04B24/16C04B24/085C04B18/248C04B24/2623C04B24/38C04B24/123C04B22/16C04B22/08C04B2103/0068C04B24/04C04B24/302C04B24/26
Inventor 杨显武
Owner 杨显武
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap