Making method of standing horse jun porcelain artware

A production method and handicraft technology, applied in decorative arts, clay products, applications, etc., can solve the problems of low yield, difficulty in achieving artistic effects, easy cracking, etc., and achieve high yield, high difficulty in firing, and firm tendon Effect

Inactive Publication Date: 2018-10-02
YUZHOU ZHENGYUJUN KILN CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

like figure 1 The Lima shown here has a bowed head and neck, a strong body, strong tendons, slender and powerful limbs, and a leisurely look. It is a type of utensil with high craftsmanship and difficulty in firing. Adhesion, the enamel formula of the prior art is difficult to achieve immediate artistic effect, and it is easy to crack after cooling out of the kiln, resulting in low yield

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Making method of standing horse jun porcelain artware

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Such as figure 1 Shown, a kind of manufacture method of Lima Jun porcelain handicraft, comprises the following steps:

[0022] Step 1. Carve the model; divide the whole handicraft into multiple parts to carve separately, including horse head 1, horse neck 2, horse body 3, horse buttocks 4, horse front legs 7, horse hind legs 6 and horse tail 5, horse neck 2 directions Bend down, the horse head 1 is downward, the mouth of the horse head 1 is on the side of the left front leg, and it is not glued to the left front leg;

[0023] Step 2, making a mould; making plaster moulds, respectively, from the parts carved in step 1;

[0024] Step 3, selecting pottery clay; the pottery clay includes the following components: 50 parts of kaolin, 5 parts of alkaline earth, 5 parts of quartz stone, 10 parts of sandstone, 10 parts of lead powder, 8 parts of mullite, and 1 part of iron ore;

[0025] Step 4, pulping; the pottery clay in step 3 is first roughly crushed into sand or powder, ...

Embodiment 2

[0033] Such as figure 1 Shown, a kind of manufacture method of Lima Jun porcelain handicraft, comprises the following steps:

[0034] Step 1, engraving the model; divide the whole handicraft into multiple parts to carve respectively, including horse head, horse neck, horse body, horse buttocks, horse front legs, horse hind legs and horse tail, the horse neck is bent downward, and the horse head is Below, the mouth of the horse's head is on the side of the left foreleg;

[0035] Step 2, making a mould; making plaster moulds, respectively, from the parts carved in step 1;

[0036] Step 3, select pottery clay; the pottery clay includes the following components: 65 parts of kaolin, 10 parts of alkaline earth, 5 parts of quartz stone, 8 parts of sandstone, 10 parts of lead powder, 8 parts of mullite, and 2 parts of iron ore;

[0037] Step 4, pulping; the pottery clay in step 3 is first roughly crushed into sand or powder, and then ground to a fineness of 230-250 mesh, mixed with ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a making method of standing horse jun porcelain artware. The method comprises steps as follows: step 1, model carving; step 2, die making; step 3, pottery clay selection; step4, pulping; step 5, slip casting, step 6, drying; step 7, biscuit firing; step 8, glazing; step 9, firing; according to the step 1 of model carving, the overall artware is divided into multiple partsfor respective carving, the multiple parts include horse's head, horse's neck, horse's body, crupper, horse's forelegs, horse's hind legs and horsetail, the horse's neck bends downwards, the horse's head is downward, and the mouth of the horse's head is located on one side of the left foreleg; according to the step 6 of drying, the finished green body is dried at the temperature of 25-120 DEG C, and water content of the dried green body is lower than 3%; according to the step 7 of biscuit firing, the green body is placed in a biscuit firing kiln and fired for 5-6 h at the temperature of 900-1000 DEG C. The binding property of the green body and glaze is good, the finished product rate of jun porcelain is high, and the vessel shape and the color of the artware can further represent creativity and artistic effect of the work.

Description

technical field [0001] The invention relates to the field of Jun porcelain crafts, in particular to a method for making Lima Jun porcelain handicrafts. Background technique [0002] Jun Porcelain is known as the first of my country's "Five Famous Porcelains". It is a specialty of Yuzhou City, Henan Province. , out of the kiln and other unique features, which cannot be achieved and compared with other ceramic handicrafts. Such as figure 1 The Lima shown here has a bowed head and neck, a strong body, strong tendons, slender and powerful limbs, and a leisurely look. It is a type of utensil with high craftsmanship and difficulty in firing. Adhesion, the enamel formula of the prior art is difficult to achieve an immediate artistic effect, and it is very easy to crack after cooling out of the kiln, and the yield is low. Contents of the invention [0003] In view of this, the present invention provides a method for making Lima Jun porcelain handicraft, which has good base-glaze...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B33/04C04B33/13C04B33/16C04B33/24C04B33/28C04B41/89C04B41/86C03C8/00B44C3/04
CPCC04B33/04B44C3/04C03C8/00C04B33/13C04B33/16C04B33/24C04B33/28C04B41/009C04B41/52C04B41/86C04B41/89C04B2235/3272C04B2235/3418C04B2235/3463C04B41/504C04B41/4539C04B41/5022
Inventor 王现锋
Owner YUZHOU ZHENGYUJUN KILN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap