Preparation method of viviparus shell vase

A field snail shell and vase technology, applied in clay products, applications, household appliances, etc., can solve problems such as environmental pollution, and achieve the effect of high whiteness and fine porcelain.

Inactive Publication Date: 2018-10-02
刘春环
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] As the waste after people use snails, the snail shells are discarded in large quantities, causing pollution to the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Wash 35 parts of snail shells, use hard objects to crack them, and then grind them with a grinder; pass 20 parts of clay, 28 parts of sodium potassium feldspar, and 25 parts of quartz through a 200-mesh sieve, and mix the raw materials with an appropriate amount of water. Harmonize into a uniform clay body; press the clay body into a ring shape, and dry it at 300-400℃; after drying, place it at 0-5℃ for 1-2 hours, glaze at room temperature and then put it into a kiln to make a vase.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a viviparus shell vase. The method comprises the following steps of screening, mixing, blank making, drying, glazing, firing and the like. The viviparusshell vase is fine in porcelain, high in whiteness, good in semi-transparency and bright in picture and has dual value of application and art.

Description

Technical field [0001] The invention belongs to the field of ceramic preparation, and particularly relates to a preparation method of a snail shell vase. Background technique [0002] The snail shells are discarded in large quantities as waste after people use the snails, causing pollution to the environment. The main component of the snail shell is calcium carbonate. In addition, it also contains the shell matrix (ie, conchiolin), magnesium, iron, calcium phosphate, silicate, and oxides. The waste can be used to make the escar shell vase. Summary of the invention [0003] The purpose of the present invention is to provide a method for preparing a snail shell vase, which includes the following steps. [0004] (1) Grind 35-50 parts of escargot shell, and mix the snail shell powder with 18-25 parts of clay, 25-30 parts of sodium potassium feldspar, 18- [0005] 28 pieces of quartz pass through 200 mesh sieve for use; [0006] (2) Mix the raw materials with an appropriate amount of wate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/132C04B33/13C04B33/34C04B33/24
CPCC04B33/13C04B33/132C04B33/24C04B33/34C04B2235/3418C04B2235/3472Y02P40/60
Inventor 刘春环
Owner 刘春环
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com