Self-luminous glaze and preparation method thereof

A self-luminous and glaze technology, applied in the field of ceramic glaze, can solve the problems that the ceramic decoration technology stays within the scope of traditional limitations, cannot provide novel ceramic art styles, and does not have luminescent function, etc., and achieves a scientific, reasonable and easy preparation method. Implementation, high yield effect

Pending Publication Date: 2021-09-21
刘梁锋
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the traditional Longquan celadon is generally monochrome glaze, which does not have the function of luminescence, and the color surface is relatively single. With the change of modern aesthetic concepts, the traditional ceramic glaze can no longer provide a novel ceramic style, making the ceramic decoration technology stay within the traditional limitations. In the range

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A self-luminous glaze according to the present invention is made of the following raw materials: 10g of luminous powder, 10g of kaolin, 40g of porcelain stone, 15g of purple gold clay, 5g of feldspar, and 5g of talc.

[0028] In practical application, the preparation method of the self-luminous glaze according to the present invention comprises the following steps:

[0029] Step 1. According to the above ratio, weigh luminous powder, kaolin, porcelain stone, purple gold clay, feldspar, and talc;

[0030] Step 2, pulverizing the above-mentioned raw materials, and bisque firing the pulverized raw materials, the temperature during biscuit firing is 900°-1100°;

[0031] Step 3, mixing and finely grinding the raw materials after bisque firing, and after fine grinding, water milling again on the principle after fine grinding;

[0032] Step 4, using a sieve to sieve the raw materials processed by the water mill, the fineness of the sieve is 200 mesh, and after sieving, stirri...

Embodiment 2

[0039] A self-luminous glaze according to the present invention is made of the following raw materials: 45g of luminous powder, 30g of kaolin, 42g of porcelain stone, 25g of purple gold clay, 15g of feldspar, and 8g of talc.

[0040] In practical application, the preparation method of the self-luminous glaze according to the present invention comprises the following steps:

[0041] Step 1. According to the above ratio, weigh luminous powder, kaolin, porcelain stone, purple gold clay, feldspar, and talc;

[0042] Step 2, pulverizing the above-mentioned raw materials, and bisque firing the pulverized raw materials, the temperature during biscuit firing is 900°-1100°;

[0043] Step 3, mixing and finely grinding the raw materials after bisque firing, and after fine grinding, water milling again on the principle after fine grinding;

[0044] Step 4, using a sieve to sieve the raw materials processed by the water mill, the fineness of the sieve is 200 mesh, and after sieving, stirr...

Embodiment 3

[0051] A self-luminous glaze according to the present invention is made of the following raw materials: 90g of luminous powder, 70g of kaolin, 45g of porcelain stone, 35g of purple gold clay, 25g of feldspar, and 15g of talc.

[0052] In practical application, the preparation method of the self-luminous glaze according to the present invention comprises the following steps:

[0053] Step 1. According to the above ratio, weigh luminous powder, kaolin, porcelain stone, purple gold clay, feldspar, and talc;

[0054] Step 2, pulverizing the above-mentioned raw materials, and bisque firing the pulverized raw materials, the temperature during biscuit firing is 900°-1100°;

[0055] Step 3, mixing and finely grinding the raw materials after bisque firing, and after fine grinding, water milling again on the principle after fine grinding;

[0056] Step 4, using a sieve to sieve the raw materials processed by the water mill, the fineness of the sieve is 200 mesh, and after sieving, stir...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a self-luminous glaze and a preparation method thereof. The self-luminous glaze is prepared from the following raw materials in percentage: 10-90% of noctilucent powder, 10-70% of kaolin, 40-45% of chinastone, 15-35% of Zijin clay, 5-25% of feldspar and 5-15% of talc. The self-luminous glaze has the beneficial effects that the prepared celadon takes the high-temperature celeste glaze as a primary color, the noctilucent powder layer is fused to achieve the noctilucent and jade texture effects, and the celadon is good in thermal stability and wide in adaptability. In addition, the preparation method provided by the invention is scientific, reasonable and easy to implement, and the obtained celadon self-luminous glaze product is high in yield and good in porcelain quality.

Description

technical field [0001] The invention relates to the technical field of ceramic glazes, in particular to a self-luminous glaze and a preparation method thereof. Background technique [0002] Celadon is famous for its delicate porcelain quality, bright and smooth lines, dignified and simple shape, pure and colorful color, and is known as the "flower of porcelain". Celadon is known as the "Flower of Porcelain" that is "green as jade, bright as a mirror, and sound like a chime". It is rich in varieties and colorful in glaze. The glaze is a colorless or colored glassy thin layer covering the surface of ceramic products. It is made of mineral raw materials and chemical raw materials in a certain proportion, and then ground to make a glaze slurry, which is applied to the surface of the body and calcined at a certain temperature. made. It can increase the mechanical strength, thermal stability and dielectric strength of the product, and it also has the characteristics of beautifyi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00C04B41/86
CPCC03C8/00C04B41/86C04B41/5022C04B41/4539C04B41/4572C04B41/4543C04B41/0072
Inventor 刘梁锋陈永荣李光树刘辉平朱承清
Owner 刘梁锋
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap