Firework display pattern glaze and preparation method thereof

A technique of patterned glaze and calcite, applied in the field of glaze, can solve the problems of firing ritual patterned glaze, etc., and achieve the effect of high fluidity and enhanced fluidity

Inactive Publication Date: 2018-10-09
禹州市土魂钧瓷有限公司
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the existing flower glazes are presented in the form of flowers, but few people are able to burn the ceremony pattern glaze.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A ritual pattern glaze, which is prepared from the following raw materials in parts by weight: 30-40 parts of feldspar, 12-15 parts of white feldspar, 8-10 parts of calcite, 7-8 parts of quartz, and 20-30 parts of frit , 5-8 parts of copper ore, 6-10 parts of zinc oxide, and 1-4 parts of copper oxide.

[0022] The preparation method of above-mentioned ceremony pattern glaze, comprises the following steps:

[0023] (1) Preparation of glaze slurry: Add appropriate amount of water to mix the above raw materials, and ball mill to obtain glaze slurry with a mass concentration of 50-52%;

[0024] (2) Glazing: immerse the bisque-fired body into the glaze slurry prepared in step (1) for a while, take it out for a while, immerse it again for a while, take it out, use the water absorption of the body to make the glaze slurry adhere to the surface of the body, and dry , and then brush the glaze slurry 2-3 times;

[0025] (3) Firing, the firing temperature is 1290-1310°C;

[002...

Embodiment 2

[0033] A ritual pattern glaze, which is prepared from the following raw materials in parts by weight: 35 parts of feldspar, 13.5 parts of white feldspar, 9 parts of calcite, 7.5 parts of quartz, 25 parts of frit, 6.5 parts of copper ore, 8 parts of zinc oxide Parts, 2.5 parts of copper oxide.

[0034] The preparation method of above-mentioned ceremony pattern glaze, comprises the following steps:

[0035] (1) Preparation of glaze slurry: Add appropriate amount of water to mix the above raw materials, and ball mill to obtain glaze slurry with a mass concentration of 51%;

[0036] (2) Glazing: immerse the bisque-fired body into the glaze slurry prepared in step (1) for a while, take it out for a while, immerse it again for a while, take it out, use the water absorption of the body to make the glaze slurry adhere to the surface of the body, and dry , and then brush the glaze slurry 2-3 times;

[0037] (3) Firing, the firing temperature is 1300°C.

[0038] The firing process sp...

Embodiment 3

[0045] A ceremony pattern glaze, which is prepared from the following raw materials in parts by weight: 34 parts of feldspar, 14 parts of white feldspar, 8 parts of calcite, 7 parts of quartz, 26 parts of frit, 6.5 parts of copper ore, 8 parts of zinc oxide Parts, 2.5 parts of copper oxide.

[0046] The preparation method of above-mentioned ceremony pattern glaze, comprises the following steps:

[0047] (1) Preparation of glaze slurry: Add appropriate amount of water to mix the above raw materials, and ball mill to obtain glaze slurry with a mass concentration of 51%;

[0048](2) Glazing: immerse the bisque-fired body into the glaze slurry prepared in step (1) for a while, take it out for a while, immerse it again for a while, take it out, use the water absorption of the body to make the glaze slurry adhere to the surface of the body, and dry , and then brush the glaze slurry 2-3 times;

[0049] (3) Firing, the firing temperature is 1290°C.

[0050] The firing process speci...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides firework display pattern glaze and a preparation method thereof. The firework display pattern glaze is prepared from the following raw materials in parts by weight: 30-40 partsof melilite, 12-15 parts of chesterlite, 8-10 parts of calcite, 7-8 parts of quartz, 20-30 parts of frits, 5-8 parts of copper ores, 6-10 parts of zinc oxide and 1-4 parts of copper oxide. According to the firework display pattern glaze and the preparation method thereof, through the regulation and the control of the content of the frits in the glaze and the atmosphere in the firing process, and in combination with the other glaze materials, the fired firework display pattern glaze is high in fluidity, a glaze surface can show high-density spots in the firework state in the flowing process, and no defects such as glaze flowing, smoking and cracking exist.

Description

technical field [0001] The invention relates to the technical field of glazes, in particular to a ritual pattern glaze and a preparation method thereof. Background technique [0002] Jun porcelain is one of the five famous porcelains of the Song Dynasty in my country. It is famous for its unique kiln transformation art. The unique national treasure porcelain in Shenhou Town, Zhouzhou City, with its simple shape, exquisite craftsmanship, and complex glaze matching, can achieve the magical kiln transformation of "one color in the kiln, and a variety of colors in the kiln". Fish and other infinitely changing graphic colors and wonderful charm, known as the first of China's "Five Famous Porcelains". After the founding of New China, Jun porcelain has developed rapidly, especially since the reform and opening up, the production technology and level of Jun porcelain have been improved epoch-makingly, and Jun porcelain has continuously appeared in the world as national gifts. [000...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/14
CPCC03C8/14
Inventor 王志勇
Owner 禹州市土魂钧瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com