Preparation method of ceramic white salix integra strips

A white berry and ceramic technology, which is applied in wicker rod peeling, manufacturing tools, mechanical equipment, etc., can solve the problems of poor ornamental and single color, and achieve the effect of enhancing the weaving effect, strong color fixation, and enhancing the effect of dyeing.

Active Publication Date: 2018-11-13
阜南县大喜柳编工艺品有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In our country, there are many willow species that can be used as willow weaving, but at present, willow is generally used as weaving raw material in production. The wicker obtained after peeling willow is generally white, with a single color and poor ornamental value.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A kind of preparation method with ceramic Baiqi willow wicker, comprises the following operation steps:

[0017] (1) After the willow is harvested in autumn, dry it naturally for 5 days, then put the wicker into the soaking solution, boil the soaking solution, continue to decoct for 30 minutes on low heat, take it out, peel the skin, and the soaking solution consists of the following parts by weight Made of ingredients: 5 parts of N-octyldiaminoethylglycine hydrochloride, 10 parts of dipotassium sebacate, 15 parts of sodium ethylenediaminopropanesulfonate, 22 parts of sodium polyacrylate, 350 parts of water ;

[0018] (2) Dry the peeled wicker until the water content is 7%, put it into the color changing solution, soak it for 3 hours, take it out, put it in an oven and dry it until the water content is 12%, and change the color The solution is made of the following components by weight: 11 parts of fumed silica, 1 part of 4,4'-bis(2-sodium styryl)biphenyl, 18 parts of ...

Embodiment 2

[0024] A kind of preparation method with ceramic Baiqi willow wicker, comprises the following operation steps:

[0025] (1) After the willow is harvested in autumn, dry it naturally for 6 days, then put the wicker into the soaking solution, boil the soaking solution, continue to decoct for 35 minutes on low heat, take it out, peel the skin, and the soaking solution consists of the following parts by weight Made of ingredients: 7 parts of N-octyldiaminoethylglycine hydrochloride, 12 parts of dipotassium sebacate, 17 parts of sodium ethylenediaminopropane sulfonate, 24 parts of sodium polyacrylate, 380 parts of water ;

[0026] (2) Dry the peeled wicker until the water content is 8%, put it into the color changing solution, soak it for 3.5 hours, take it out, put it in an oven and dry it until the water content is 14%, and change the color The liquid is made of the following components by weight: 13 parts of fumed silica, 2 parts of 4,4'-bis(2-sodium styryl)biphenyl, 19 parts o...

Embodiment 3

[0032] A kind of preparation method with ceramic Baiqi willow wicker, comprises the following operation steps:

[0033] (1) After the willow is harvested in autumn, dry it naturally for 7 days, then put the willow into the soaking solution, boil the soaking solution, continue to decoct for 40 minutes on low heat, take it out, peel the skin, and the soaking solution consists of the following parts by weight Made of ingredients: 9 parts of N-octyldiaminoethylglycine hydrochloride, 13 parts of dipotassium sebacate, 19 parts of sodium ethylenediaminopropane sulfonate, 26 parts of sodium polyacrylate, 400 parts of water ;

[0034] (2) Dry the peeled wicker until the water content is 9%, put it into the color changing solution, soak it for 4 hours, take it out, put it in an oven and dry it until the water content is 16%, and change the color The solution is made of the following components by weight: 15 parts of fumed silica, 3 parts of 4,4'-bis(2-sodium styryl)biphenyl, 20 parts o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of ceramic white salix integra strips. The preparation method includes the following operation steps that (1) salix integra is subjected to natural dryingtreatment for 5-7 days after being harvested in autumn, then salix integra strips are put into a soaking solution, after the soaking solution is boiled, soft-fire boiling is continued for 30-40 min, and then the salix integra strips are taken out and peeled; (2) when dried till the water content is 7-9%, the peeled salix integra strips are put into a color changing solution, soaked for 3-4 h, thentaken out, and put into a drying oven to be dried till the water content is 12-16%; and (3) a color fixing solution is evenly sprayed on the surfaces of the salix integra strips treated in the step (2), and after 3-4 h, the salix integra strips are put into the drying oven to be dried, so that the ceramic white salix integra strips are obtained. The prepared salix integra strips have the color ofceramic white, so that the texture of manufactured wicker products is effectively improved, and the ornamental value of the products is increased; and meanwhile, the color fixing performance of the ceramic white is high, and a color fading phenomenon is not prone to occurring in the using process.

Description

technical field [0001] The invention belongs to the technical field of wicker treatment, and in particular relates to a method for preparing wicker wicker with ceramics. Background technique [0002] Weaving willow is a kind of willow that produces wicker for weaving raw materials. Various life, handicraft products and small furniture made of wicker are light and beautiful. They are sold in domestic and foreign markets and are important export trade products. In my country, there are many species of willows that can be used as willow weaving, but at present, willow is generally used as weaving raw material in production. The wicker obtained after peeling willow is generally white, with a single color and poor ornamental value. Contents of the invention [0003] In order to solve the above-mentioned technical problems, the present invention provides a preparation method of wicker with ceramic white wolfberry wicker. [0004] The present invention is achieved through the fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B27J3/00B27L3/00B27K9/00B27K5/02B27K5/04C09D15/00
CPCB27J3/00B27K5/02B27K5/04B27K9/002B27L3/00C09D15/00
Inventor 童大喜童小慢朱华云
Owner 阜南县大喜柳编工艺品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap