Disc type brake pad friction surface coating layer, and production method thereof

A friction surface, disc brake technology, applied in coatings, friction linings, mechanical equipment, etc., can solve the problem of small contact area between brake pads and brake disc, affecting product appearance quality and performance, no friction surface, etc. problems, to improve the appearance quality and the stability and safety of brakes, overcome poor contact, and maintain stability

Inactive Publication Date: 2018-11-30
烟台海纳制动技术有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The friction surface of the traditional disc brake pad is not processed by brush coating, and the finished product is directly loaded and used, but there are the following defects and deficiencies: 1. Traditional disc brake pad: there is no coating process on the friction surface, and the product is installed After the car is put on the car, it takes a long time to run in before the friction coefficient can be stable; 2. At the beginning of loading, the contact area between the brake pad and the brake disc is small, the braking torque is small, the braking distance is long, and the safety is poor; 3. The grinding surface There are appearance defects such as tiny pits and grinding scratches, which affect the appearance quality and performance of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Disc type brake pad friction surface coating layer, and production method thereof
  • Disc type brake pad friction surface coating layer, and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A brush coating on the friction surface of a disc brake pad and its production process. The raw materials of the coating include phenolic resin, iron oxide black and aluminum oxide, and the mass percentages are 200:1:100.5 in sequence;

[0040] The production process of the coating is:

[0041] Step 1: Preparation of black glue

[0042] (1) The black glue solution is prepared from PR-55735 phenolic resin and iron oxide black, and the raw materials are prepared according to the ratio (mass percentage) of phenolic resin:iron oxide black=200:1;

[0043] (2) Sprinkle iron oxide black slowly and evenly into the container filled with phenolic resin, and stir for 15 minutes until iron oxide black is fully dissolved;

[0044] (3) After the preparation is completed, the barrel is sealed and sealed for use;

[0045] Step 2: Preparation of coating solution

[0046] (1) The coating liquid is prepared from the black glue solution and alumina in step 1, and prepares raw materials ...

Embodiment 2

[0052] A brush coating on the friction surface of a disc brake pad and its production process. The raw materials of the coating include phenolic resin, iron oxide black and aluminum oxide, and the mass percentages are 200:1:100.5 in sequence;

[0053] The production process of the coating is:

[0054] Step 1: Preparation of black glue

[0055] (1) The black glue solution is prepared from PR-55735 phenolic resin and iron oxide black, and the raw materials are prepared according to the ratio (mass percentage) of phenolic resin:iron oxide black=200:1;

[0056] (2) Sprinkle iron oxide black slowly and evenly into the container filled with phenolic resin, and stir for 10 minutes until iron oxide black is fully dissolved;

[0057] (3) After the preparation is completed, the barrel is sealed and sealed for use;

[0058] Step 2: Preparation of coating solution

[0059] (1) The coating solution is prepared from the black glue solution and alumina in step 1, and the raw materials are...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a disc type brake pad friction surface coating layer, and a production method thereof, and belongs to the technical field of disc type brake pad manufacturing. The disc type brake pad friction surface coating layer is composed of phenolic resin, iron oxide black, and aluminium oxide at a mass ratio of 200:1:100.5. The production method comprises following steps: 1, preparation of a black rubber solution; 2, preparation of a coating solution; 3, coating of the coating solution; and 4, drying. The production method is capable of realizing brake pad surface coating, increasing product initial friction coefficient, and maintaining brake stability; surface coating layer wearing is rapid, the run-in period of the brake pad with a brake disc is shortened, contact area islarge, braking torque is large, braking distance is short, braking safety is improved; appearance defects such as friction surface small pits and grinding scratches are eliminated, product appearancequality and performance are improved, and market share is increased; and the friction surface coating layer technology is suitable for manufacturing of OE high end market products.

Description

technical field [0001] The invention relates to a brush coating on the friction surface of a disc brake pad and a production process, belonging to the technical field of disc brake pad manufacturing. Background technique [0002] The disc brake pad is an important component of the brake system, which is fixed with the tire of the vehicle and cooperates with the caliper to brake the vehicle. The friction surface of the traditional disc brake pad is not processed by brush coating, and the finished product is directly loaded and used, but there are the following defects and deficiencies: 1. Traditional disc brake pad: there is no coating process on the friction surface, and the product is installed After the car is put on the car, it takes a long time to run in before the friction coefficient can be stable; 2. At the beginning of loading, the contact area between the brake pad and the brake disc is small, the braking torque is small, the braking distance is long, and the safety...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D161/06C09D7/61F16D69/02
CPCC08K2003/2227C08K2003/2265C09D7/61C09D161/06F16D69/02F16D2250/0046C08K3/22
Inventor 安述法邵春生
Owner 烟台海纳制动技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap