Wear-resistant corrosion-resistant stainless steel cup material and preparation method thereof

A stainless steel and corrosion-resistant technology, applied in the field of wear-resistant and corrosion-resistant stainless steel cup materials and their preparation, can solve the problems of multi-price, expensive cobalt elements, and high production costs, and achieve high hardenability, fine grain size, and hardness. Effect

Inactive Publication Date: 2018-12-14
合肥久新不锈钢厨具有限公司
View PDF2 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The cobalt-based alloy designed in this invention has excellent corrosion resistance and wear resistance, and its average hardness value reaches about 48HRC, but this alloy contains more expensive cobalt elements, and the production cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wear-resistant corrosion-resistant stainless steel cup material and preparation method thereof
  • Wear-resistant corrosion-resistant stainless steel cup material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] The wear-resistant and corrosion-resistant stainless steel cup material of the present embodiment is made up of the chemical composition of following mass percent: C0.35%, Si 0.75%, Mn 0.80%, Cr 5.50%, Cu 0.55%, Mo 0.18%, V 0.20% , Co 0.02%, Nb 0.03%, Ti 0.02%, Ce 0.01%, Yb 0.0010%, B 0.0010%, the balance is Fe and unavoidable impurities.

[0052] Wherein, in weight percentage, the total content of the impurities is ≤0.1%, wherein, P≤0.015%, S≤0.008%, H≤0.003%, O≤0.001%.

[0053] The present invention also provides a preparation method for the above-mentioned wear-resistant and corrosion-resistant stainless steel cup material, comprising the following steps:

[0054] S1: First put the raw materials of C, Si, Mn, Cr, Cu, and B into the electric furnace for melting, and the melting temperature is 1570°C;

[0055] S2: Add 0.5% desulfurizer to the molten steel in step S1, remove the slag, then take the molten steel for testing, and adjust the components of the molten steel...

Embodiment 2

[0072] The wear-resistant and corrosion-resistant stainless steel cup material of the present embodiment is made up of the chemical composition of following mass percent: C0.55%, Si 1.15%, Mn 1.20%, Cr 8.50%, Cu 0.85%, Mo 0.38%, V 0.40% , Co 0.06%, Nb 0.05%, Ti 0.04%, Ce 0.03%, Yb 0.0040%, B 0.0035%, the balance is Fe and unavoidable impurities.

[0073] Wherein, in weight percentage, the total content of the impurities is ≤0.1%, wherein, P≤0.015%, S≤0.008%, H≤0.003%, O≤0.001%.

[0074] The present invention also provides a preparation method for the above-mentioned wear-resistant and corrosion-resistant stainless steel cup material, comprising the following steps:

[0075] S1: first put the raw materials of C, Si, Mn, Cr, Cu and B into the electric furnace for melting, and the melting temperature is 1630°C;

[0076] S2: Add 0.5% desulfurizer to the molten steel in step S1, remove the slag, then take the molten steel for testing, and adjust the components of the molten steel ...

Embodiment 3

[0093] The wear-resistant and corrosion-resistant stainless steel cup material of the present embodiment, it is made up of the chemical composition of following mass percent: C0.45%, Si 0.95%, Mn 1.00%, Cr 7.00%, Cu 0.70%, Mo 0.28%, V 0.20- 0.40%, Co0.04%, Nb 0.04%, Ti 0.03%, Ce 0.02%, Yb0.0025%, B 0.0020%, P≤0.02%, S≤0.02%, the balance is Fe and unavoidable impurities.

[0094] Wherein, in weight percentage, the total content of the impurities is ≤0.1%, wherein, P≤0.015%, S≤0.008%, H≤0.003%, O≤0.001%.

[0095] The present invention also provides a preparation method for the above-mentioned wear-resistant and corrosion-resistant stainless steel cup material, comprising the following steps:

[0096] S1: first put the raw materials of C, Si, Mn, Cr, Cu and B into the electric furnace and melt them, and the melting temperature is 1600°C;

[0097] S2: Add 0.5% desulfurizer to the molten steel in step S1, remove the slag, then take the molten steel for testing, and adjust the comp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wear-resistant corrosion-resistant stainless steel cup material. The material comprises the following chemical components of, by mass, 0.35-0.55% of C, 0.75-1.15% of Si, 0.80-1.20% of Mn, 5.50-8.50% of Cr, 0.55-0.85% of Cu, 0.18-0.38% of Mo, 0.20-0.40% of V, 0.20-0.06% of Co, 0.03-0.05% of Nb, 0.02-0.04% of Ti, 0.01-0.03% of Ce, 0.0010-0.0040% of Yb, 0.0010-0.0035% of B,the balance Fe and inevitable impurities. The stainless steel cup material has relatively high wear resistance and high corrosion resistance, low in cost, good in antibacterial performance, strength,hardness and heat resistance and excellent in comprehensive performance.

Description

technical field [0001] The invention relates to the technical field of stainless steel cup materials, in particular to a wear-resistant and corrosion-resistant stainless steel cup material and a preparation method thereof. Background technique [0002] With the rapid development of the metallurgical industry and the improvement of daily life standards, the use of stainless steel has greatly increased, and a large number of beautiful and durable stainless steel products have entered the field of civilian consumption. Among them, the use of stainless steel in utensils and kitchen supplies accounts for the vast majority. most. Stainless steel refers to steel resistant to weak corrosive media such as air, steam, water, and chemically corrosive media such as acid, alkali, and salt. It is also called stainless acid-resistant steel. In practical applications, the steel resistant to weak corrosion medium is often called stainless steel, and the steel resistant to chemical medium co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/20C22C38/22C22C38/24C22C38/30C22C38/26C22C38/28C22C38/32C21D8/02C22C33/04C21D1/18
CPCC22C38/02C21D1/18C21D8/0205C21D8/0226C21D8/0247C22C33/04C22C38/005C22C38/04C22C38/20C22C38/22C22C38/24C22C38/26C22C38/28C22C38/30C22C38/32
Inventor 辛松
Owner 合肥久新不锈钢厨具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com