A fire-proof and breakdown-resistant film capacitor

A thin-film capacitor and breakdown-resistant technology, which is applied in the direction of thin-film/thick-film capacitors, laminated capacitors, fixed capacitor dielectrics, etc., can solve the problems of limited application range and poor voltage breakdown resistance, and achieve enhanced breakdown resistance. Effect of improving bond energy and improving high temperature resistance

Active Publication Date: 2018-12-18
GUANGDONG FENGMING ELECTRONICS TECH
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the metallized polypropylene film is widely used in the market to be wound into a capacitor core, but the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A fire-proof and breakdown-resistant film capacitor
  • A fire-proof and breakdown-resistant film capacitor

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0018] Example 1

[0019] A fire-resistant and breakdown-resistant film capacitor uses a composite film made of macromolecular copolymer-modified polypropylene masterbatch as the dielectric of the film capacitor.

[0020] Further, the preparation method of the macromolecular copolymer modified polypropylene master batch is:

[0021] Weigh in parts by weight 120 parts of trans-2-butene, 30 parts of acrylonitrile, 120 parts of diethyl fumarate, 1250 parts of deionized water, 10 parts of emulsifier, 5 parts of nano-bentonite dispersion, and 0.03 parts of activator Add 1.2 parts of initiator to the reaction kettle, stir at 1500r / min for 2 hours, then continue to feed nitrogen gas for 20 minutes, then heat to 35 ° C, keep the temperature for 10 minutes, then add 1.2 parts of initiator, after stirring evenly, keep in a 35 ° C water bath for insulation Under the reaction for 10 hours, then discharging, purifying the reaction product, drying to constant weight, that is, the macromole...

Example Embodiment

[0031] Example 2

[0032] A fire-resistant and breakdown-resistant film capacitor uses a composite film made of macromolecular copolymer-modified polypropylene masterbatch as the dielectric of the film capacitor.

[0033] Further, the preparation method of the macromolecular copolymer modified polypropylene master batch is:

[0034] Weigh 150 parts of trans-2-butene, 50 parts of acrylonitrile, 160 parts of diethyl fumarate, 1300 parts of deionized water, 12 parts of emulsifier, 7 parts of nano-bentonite dispersion, and 0.08 parts of activator by weight. Add 1.5 parts of initiator to the reaction kettle, stir at 1500r / min for 3 hours, then continue to feed nitrogen gas for 20 minutes, then heat to 35 °C, keep the temperature for 10 minutes, then add 1.5 parts of initiator, stir evenly, and keep in a 35 °C water bath for insulation Under the reaction for 12 hours, then discharging, purifying the reaction product, drying to constant weight, that is, the macromolecular copolymer;...

Example Embodiment

[0044] Example 3

[0045] A fire-resistant and breakdown-resistant film capacitor uses a composite film made of macromolecular copolymer-modified polypropylene masterbatch as the dielectric of the film capacitor.

[0046] Further, the preparation method of the macromolecular copolymer modified polypropylene master batch is:

[0047] Weigh in parts by weight 130 parts of trans-2-butene, 40 parts of acrylonitrile, 150 parts of diethyl fumarate, 1270 parts of deionized water, 11 parts of emulsifier, 6 parts of nano-bentonite dispersion, and 0.05 parts of activator Add 1.4 parts of initiator to the reaction kettle, stir at 1500 r / min for 2.3 hours, then continue to feed nitrogen gas for 20 minutes, then heat to 35 °C, keep the temperature for 10 minutes, then add 1.4 parts of initiator, stir evenly, and keep in a 35 °C water bath for insulation Under the reaction for 11 hours, then discharging, purifying the reaction product, drying to constant weight, that is, the macromolecular...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a fire-proof and breakdown-resistant film capacitor and relates to the technical field of film capacitors, comprises a composite film made of a macromolecular copolymer modified polypropylene master batch as a dielectric of a film capacitor, A composite film made of macromolecular copolymer modified polypropylene masterbatch is used as dielectric of film capacitor, Throughthe modification of polypropylene film, The tensile properties of the polypropylene film were improved remarkably, especially the macromolecular copolymer was used to modify the polypropylene masterbatch, which greatly improved the molecular structure of the composite film, increased the bond energy between the molecules, greatly improved its high temperature resistance, reduced the loss coefficient, and achieved remarkable economic benefits.

Description

technical field [0001] The invention belongs to the technical field of film capacitors, and in particular relates to a fireproof and breakdown resistant film capacitor. Background technique [0002] Capacitors are widely used in integrated circuits. They are suitable for chips and lead circuits that require DC blocking and RF bypass. They can also be used as tuning components in filters, oscillators and matching networks. At present, the metallized polypropylene film is mostly used in the market to be wound into a capacitor core, but the simple polypropylene film capacitor has poor voltage breakdown resistance, which greatly limits its application range. Contents of the invention [0003] The object of the present invention is to provide a fireproof and breakdown resistant film capacitor aiming at the existing problems. [0004] The present invention is achieved through the following technical solutions: [0005] A fire-proof and breakdown-resistant film capacitor, the c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01G4/18H01G4/33C08F210/08C08F220/44C08F222/14C08J3/22
CPCC08F210/08C08F222/14C08J3/226C08J2423/12C08J2423/20C08J2435/02H01G4/18H01G4/33C08F220/44
Inventor 徐培培
Owner GUANGDONG FENGMING ELECTRONICS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap