Damp-proof wall

A technology for wall and composite mother liquor, which is applied in building components, coatings, building insulation materials, etc., can solve the problems of easy fading, easy dirtying, short service life, etc. under long-term light, and achieves increased overall strength and moisture-proof performance. The effect of improving film properties, bonding stability, and compressive shear bond strength

Active Publication Date: 2019-01-04
四川越无限建筑工程有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the construction industry uses paint or paint coating on the interior walls of buildings as a decorative surface layer, which generally has defects such as cracking, falling off, easy corrosion by water, mildew, easy dirt after absorbing dust, easy fading under long-term light, and short service life; In wet weather, the wall surface will return to moisture and even condense water droplets. In addition, the existing plaster has poor thermal insulation performance, is easy to fall off, and has poor bonding force with the wall. The existing wall construction method has poor construction stability, safety and reliability. Poor performance, poor durability and other defects, can not meet the construction needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A moisture-proof wall construction method, comprising the following steps:

[0017] Add ethylene glycol diacrylate, hydroxyethyl methacrylate, 2,4,6-trimethylbenzoyl-diphenylphosphine oxide, and polyvinyl alcohol into the chemical kettle, stir evenly, and pressurize to 0.2-0.3MPa, hold the pressure for 1.5-2 hours to obtain a composite mother liquor; in which ethylene glycol diacrylate, hydroxyethyl methacrylate, 2,4,6-trimethylbenzoyl-diphenylphosphine oxide The molar ratio with polyvinyl alcohol is 1:2:0.5:2.5, the composite mother liquor and microsilica powder, silane-terminated polyether, alkylsulfonic acid phenyl ester, phenylmaleimide-based silicone resin are put into Stir in an internal mixer at 50-60°C for 20-30min and cool naturally to obtain a wall surface interface agent; The mass ratio of imine-based silicone resin is 35:10:6:2:1, and the interface agent is evenly coated on the wall base to form an interface layer. The thickness of the interface layer reach...

Embodiment 2

[0023] A moisture-proof wall construction method, comprising the following steps:

[0024] Add ethylene glycol diacrylate, hydroxyethyl methacrylate, 2,4,6-trimethylbenzoyl-diphenylphosphine oxide, and polyvinyl alcohol into the chemical kettle, stir evenly, and pressurize to 0.2-0.3MPa, hold the pressure for 1.5-2 hours to obtain a composite mother liquor; in which ethylene glycol diacrylate, hydroxyethyl methacrylate, 2,4,6-trimethylbenzoyl-diphenylphosphine oxide The molar ratio with polyvinyl alcohol is 1:3:0.9:2, the composite mother liquor and microsilica powder, silane-terminated polyether, alkyl sulfonic acid phenyl ester, phenylmaleimide-based silicone resin are put into Stir in an internal mixer at 50-60°C for 20-30min and cool naturally to obtain a wall surface interface agent; The mass ratio of imine-based silicone resin is 36:15:5:2:2, and the interface agent is evenly coated on the wall base to form an interface layer. The thickness of the interface layer reache...

Embodiment 3

[0030] A moisture-proof wall construction method, comprising the following steps:

[0031] Add ethylene glycol diacrylate, hydroxyethyl methacrylate, 2,4,6-trimethylbenzoyl-diphenylphosphine oxide, and polyvinyl alcohol into the chemical kettle, stir evenly, and pressurize to 0.2-0.3MPa, hold the pressure for 1.5-2 hours to obtain a composite mother liquor; in which ethylene glycol diacrylate, hydroxyethyl methacrylate, 2,4,6-trimethylbenzoyl-diphenylphosphine oxide And polyvinyl alcohol molar ratio is 1:1.5:0.5:3, described composite mother liquor and microsilica fume, silane-terminated polyether, alkylsulfonic acid phenyl ester, phenylmaleimide base silicone resin are put into Stir in an internal mixer at 50-60°C for 20-30 minutes and cool naturally to obtain a wall interface agent; The mass ratio of imine-based silicone resin is 40:10:9:3:1.5, and the interface agent is evenly coated on the wall base to form an interface layer. The thickness of the interface layer reaches ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a damp-proof wall. A construction method of the damp-proof wall includes the steps: dispensing 150-180 parts of gypsum, 30-50 parts of hollow glass beads, 10-20 parts of ceramsite, 20-30 parts of mica powder, 10-20 parts of silica sol, 10-20 parts of cement, 5-10 parts of sodium silicate, 3-5 parts of dibutyl phthalate, 1-4 parts of sodium pentachlorophenate and 40-70 partsof water; placing the mica powder into a pulverizing mill for pulverizing for 30-60 minutes and enabling average particle size to reach 0.05-0.1mm; uniformly mixing the pulverized mica powder, the hollow glass beads and the ceramsite. By the aid of the hollow glass beads, the ceramsite and the mica powder of plastering mortar, the wall has a better heat retaining property, bonding strength between the mortar and an interface agent is improved by adding the sodium silicate, the dibutyl phthalate and the sodium pentachlorophenate, and the compression and shear bond strength of the wall is greatly improved.

Description

technical field [0001] The invention relates to a moisture-proof wall, which belongs to the field of wall construction. Background technique [0002] At present, the construction industry uses paint or paint coating on the interior walls of buildings as a decorative surface layer, which generally has defects such as cracking, falling off, easy corrosion by water, mildew, easy dirt after absorbing dust, easy fading under long-term light, and short service life; In wet weather, the wall surface will return to moisture and even condense water droplets. In addition, the existing plaster has poor thermal insulation performance, is easy to fall off, and has poor bonding force with the wall. The existing wall construction method has poor construction stability, safety and reliability. Poor performance, poor durability and other defects cannot meet the construction requirements. Therefore, a new technical solution should be provided to solve the above problems. Contents of the in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/06C09D4/02C09D7/61C09D7/63C09D1/00C09D5/34E04B1/64
CPCC08L2205/02C08L2205/03C09D1/00C09D4/06C09D5/34C09D183/08C09D7/61C09D7/63C09D7/65E04B1/644E04F13/02C08L83/04C08K3/36C08K5/42
Inventor 凃义亮
Owner 四川越无限建筑工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com