Barium aluminate cement-based radiation shielding concrete and preparation method thereof

A barium aluminate and concrete technology, applied in the field of concrete, can solve the problems of land occupation, waste of resources, pollution of the environment, etc., and achieve the effect of saving material costs, reducing consumption, and good radiation protection performance

Inactive Publication Date: 2019-01-18
成都宏基建材股份有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The annual discharge of copper slag in my country is huge, and most of them are in the state of accumulation and storage. At present, the stock of copper slag in my country has already exceeded 50 million tons, which not only occupies land, pollutes the environment, but also causes a huge waste of resources.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Barium aluminate cement-based radiation shielding concrete and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A barium aluminate cement-based anti-radiation concrete, which is composed of the following materials: 325 parts of cement, 1000 parts of fine aggregate, 1300 parts of coarse aggregate, 18 parts of neutron absorber, 0.5 part of water reducer, 150 parts of water, and parts by weight.

[0035] Among them, the cement is selected from barium aluminate cement, provided by Zhengzhou Kanghui Refractories Co., Ltd., and its performance test results are as follows: the specific surface area is 366m 2 kg -1 , initial setting time 106min, final setting time 127min, 1-day compressive strength 76.3MPa, 3-day compressive strength 80.1MPa, Al 2 o 3 The content is 55.46%, the BaO content is 37.45%, the CaO content is 7.32%, and other properties meet the requirements.

[0036] Among them, the fine aggregate is selected from the water-quenched copper slag after mechanical treatment, and the mechanical treatment method is as follows: first, the water-quenched copper slag is crushed in ...

Embodiment 2

[0045] A barium aluminate cement-based radiation-proof concrete, consisting of the following materials: 310 parts of cement, 1000 parts of fine aggregate, 1300 parts of coarse aggregate, 18 parts of neutron absorber, 0.5 part of water reducing agent, 148 parts of water, and parts by weight.

[0046] Among them, the cement is selected from barium aluminate cement, provided by Zhengzhou Kanghui Refractories Co., Ltd., and its performance test results are as follows: the specific surface area is 366m 2 kg -1 , initial setting time 106min, final setting time 127min, 1-day compressive strength 76.3MPa, 3-day compressive strength 80.1MPa, Al 2 o 3 The content is 55.46%, the BaO content is 37.45%, the CaO content is 7.32%, and other properties meet the requirements.

[0047] Among them, the fine aggregate is selected from the water-quenched copper slag after mechanical treatment, and the mechanical treatment method is as follows: first, the water-quenched copper slag is crushed in...

Embodiment 3

[0056] A barium aluminate cement-based radiation-proof concrete, consisting of the following materials: 340 parts of cement, 1000 parts of fine aggregate, 1300 parts of coarse aggregate, 18 parts of neutron absorber, 0.5 part of water reducing agent, 152 parts of water, and parts by weight.

[0057] Among them, the cement is selected from barium aluminate cement, provided by Zhengzhou Kanghui Refractories Co., Ltd., and its performance test results are as follows: the specific surface area is 366m 2 kg -1 , initial setting time 106min, final setting time 127min, 1-day compressive strength 76.3MPa, 3-day compressive strength 80.1MPa, Al 2 o 3 The content is 55.46%, the BaO content is 37.45%, the CaO content is 7.32%, and other properties meet the requirements.

[0058]Among them, the fine aggregate is selected from the water-quenched copper slag after mechanical treatment, and the mechanical treatment method is as follows: first, the water-quenched copper slag is crushed in ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
curing timeaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of concrete, and particularly discloses barium aluminate cement-based radiation shielding concrete and a preparation method thereof. The concrete is prepared from the following materials in parts by weight: 300 to 350 parts of cement, 900 to 1200 parts of fine aggregate, 1200 to 1500 parts of coarse aggregate, 10 to 20 parts of neutron absorbent, 0.4 to 0.6 partof a water reduction agent, and 140 to 160 parts of water. The prepared barium aluminate cement-based radiation shielding concrete has the characteristics that the strength requirement of C40 concreteis met, the segregation is avoided, the collapsing degree and extendibility are good, the volume weight is 2900 to 2950kg.m<3>, and the volume weight requirements of the radiation shielding concreteare met; the working property is excellent, the anti-radiation property is good, the cost is low, the fire-refractory property is realized, and the like; the problems of easiness in segregation, poorhomogenizing property, poor construction property and the like in the traditional radiation shielding concrete, and the problem of application difficulty in fire-resistant environments are solved.

Description

technical field [0001] The invention belongs to the field of concrete, and specifically discloses a barium aluminate cement-based radiation-proof concrete and a preparation method thereof. Background technique [0002] Radiation exists throughout the universe and can be divided into natural radiation and artificial radiation. Natural radiation mainly comes from cosmic rays, etc. Artificial radiation mainly comes from α, β, γ, X and neutron streams and other rays produced in the process of applying nuclear technology in nuclear power, military, education, medical treatment, scientific research and other fields. After being exposed to these rays for a long time, it is easy to induce cancer, leukemia, thyroid dysfunction, infertility, birth defects and other diseases, and it is also easy to induce gene mutations in other animals or plants. In order to prevent radiation from harming human beings, when building buildings with radiation sources, it is generally necessary to insta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/06
CPCC04B28/06C04B2111/00431C04B2111/00862C04B18/144C04B14/14C04B14/36C04B2103/302
Inventor 肖超黄俊廖俊
Owner 成都宏基建材股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products