Flame-retarding dyeing glue solution and flame-retarding paint-free solid wood board applying same
A technology of dyeing glue and solid wood, which is applied in the field of building decoration materials, which can solve the problems of single color tone, easy cracking, and blue stain of the board, and achieve the effect of simple process, accelerated dispersion speed, and accelerated penetration ability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0046] The present invention also provides a preparation method for the above-mentioned flame retardant dyed glue, specifically comprising the following steps:
[0047] The following components are calculated in parts by weight.
[0048] After heating 70-80 parts by weight of thermosetting resin glue, add 2-6 parts by weight of fire retardant, 10-20 parts by weight of color essence, 1.5-3 parts by weight of dispersant, 0.5-2 parts by weight The nano-anion powder solution is stirred evenly, cooled to normal temperature (within 30° C.), and then 6-10 parts by weight of penetrant are added, stirred evenly for later use, and the finished flame-retardant dyed glue is obtained.
[0049] The heating temperature of the above-mentioned thermosetting resin glue is 50° C. to 90° C., heating can prevent the thermosetting resin glue from curing, and facilitate the subsequent thorough mixing of various components.
[0050] The present invention also provides a method for preparing a flame-...
Embodiment 1
[0058] A flame retardant dyeing glue solution, comprising the following components in parts by weight:
[0059] 72 parts of melamine resin glue;
[0060] 8 parts of penetrant;
[0061] 14 parts of color essence;
[0062] 3 parts of fire retardant;
[0063] 1 part of nano anion powder solution;
[0064] 2 parts of dispersant.
[0065] The preparation method of embodiment 1 flame retardant dyeing glue, specifically comprises the following steps:
[0066] The following components are calculated in parts by weight.
[0067] After heating 72 parts of melamine resin glue to 60°C, add 3 parts of fire retardant, 14 parts of color essence, 2 parts of dispersant, and 1 part of nano-anion powder solution in sequence, stir evenly, and cool to 25 After ℃, add 8 parts of penetrating agent, stir evenly for later use, and obtain the finished flame-retardant dyeing glue.
[0068] Application of embodiment 1 flame retardant dyeing glue:
[0069] In this embodiment, the flame-retardant d...
Embodiment 2
[0074] A flame retardant dyeing glue solution, comprising the following components in parts by weight:
[0075] 76 parts of phenolic resin glue;
[0076] 7 parts of penetrant;
[0077] 12 parts of color essence;
[0078] 2 parts of fire retardant;
[0079] 1.5 parts of nano anion powder solution;
[0080] Dispersant 1.5 parts.
[0081] The preparation method of embodiment 2 flame retardant dyeing glue, specifically comprises the following steps:
[0082] The following components are calculated in parts by weight.
[0083] After heating 76 parts of phenolic resin glue to 70°C, add 2 parts of fire retardant, 12 parts of color essence, 1.5 parts of dispersant, and 1.5 parts of nano-anion powder solution, stir evenly, and cool to 27 After ℃, add 7 parts of penetrating agent, stir evenly for later use, and obtain the finished flame-retardant dyeing glue.
[0084] Application of embodiment 2 flame retardant dyeing glue:
[0085] In this embodiment, the flame-retardant dyeing...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap