Fettling material for converter and preparation method thereof

A technology for repairing charge and converter, which is applied to the field of repair charge for converter and its preparation, can solve the problems of long hardening time, poor adhesion of converter working lining, low service life of cast iron converter, etc., and achieves short hardening time and economic benefits. Considerable, improve the effect of furnace age

Inactive Publication Date: 2019-01-25
海城利尔麦格西塔材料有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there is no repairing material suitable for the converter iron melting process. The existing repairing materials take a long time to ha...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fettling material for converter and preparation method thereof
  • Fettling material for converter and preparation method thereof
  • Fettling material for converter and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] The specific embodiment of the present invention will be further described below, but it is not used to limit the scope of the present invention:

[0020] The following 6 examples are listed as specific descriptions of the raw materials used in the specific embodiments of the present invention, and the specific contents are shown in Table 1.

[0021] Table 1: A list of ingredients for a converter repair charge from Embodiment 1 to Embodiment 6 (unit: parts by weight)

[0022]

[0023] A kind of preparation method of repairing material for converter, specifically comprises the following steps:

[0024] (1) Raw material crushing, sieving, and fine grinding: crush, sieve, and finely grind mid-grade magnesia to separate 8-3mm and 3-1mm mid-grade magnesia; crush and sieve spinel sand Separation and fine grinding, to separate spinel sand with two particle levels of 0~1mm and ≤0.088mm;

[0025] (2) batching: take raw material by formula described in table 1;

[0026] (3)...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of fireproof materials and in particular relates to a fettling material for a converter and a reparation method thereof. The fettling material is preparedfrom the following raw materials in parts by weight: 30 to 60 parts of middle-grade magnesite, 30 to 60 parts of spinel sand, 10 to 20 parts of a binding agent, 2 to 5 parts of an additive and 6 to 10parts of a wetting agent. The fettling material can be adaptive to a utilization environment with the slag basicity, which is controlled to be 0.5 to 1.0, of an iron-melting converter very well. Thelow-temperature sintering performance of the fettling material is greatly improved and the fettling material is applicable to a low-temperature utilization condition of the iron-melting converter. Thefettling material can meet the requirements of good self-flowing performance, thermal-state strength, corrosion resistance and thermal vibration resistance, and also has the advantages of short curing, capability of shortening the stopping and maintenance time of the converter and capability of improving the working efficiency; meanwhile, the fettling material is stuck with a working liner of theconverter well and does not fall off in a utilization process. The furnace age of the iron-melting converter is greatly prolonged and the economic benefits are considerable.

Description

technical field [0001] The invention relates to the technical field of refractory materials, in particular to a repair charge for a converter and a preparation method thereof. Background technique [0002] With the arrival of winter, the north began to enter the heating period. In order to protect the environment, most blast furnaces in steel mills entered the stage of staggered peak production. The main process of converter iron melting is roughly as follows: put 50t of molten iron, scrap steel, slagging agent, and heat replenishing agent into the furnace three times, blow oxygen for about 10 minutes each time, and smelt for about 70 minutes each time. The tapping temperature is 1300-1400 ° C. At present, the basicity of the slag is controlled at 0.5-1.0, the content of MgO in the slag is 6-10%, TFe8-12%, C3-5%, and whether the iron converter is stopped or started depends on the demand for molten iron in the steel plant. [0003] At present, there is no repairing material ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/043C04B35/622C21C5/44
CPCC04B35/043C04B35/622C04B2235/3206C04B2235/3222C04B2235/3418C04B2235/405C04B2235/428C04B2235/5208C04B2235/9692C21C5/44
Inventor 曹贺张义先董会彬王新杰陈东明袁青峰金钊
Owner 海城利尔麦格西塔材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap