Production technology of doris three-layer lattice fabric

A production process and fabric technology, applied to multi-strand fabrics, fabrics, textiles, etc., can solve the problems of poor weft insertion, lower loom efficiency, easy weft stop and return of looms, etc., to improve loom efficiency and soft luster , the color has the effect of natural beauty

Inactive Publication Date: 2019-02-19
JIANGSU DESHUN TEXTILES
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a production process of Dori three-layer lattice fabric, which has the advantages of high loom efficiency, and solves the problem of using two kinds of raw materials with different linear densities as weft yarns in the production process, and the difference between warp and weft yarn interweaving points is easy. The problems caused by poor weft insertion, easy weft stop and return of the loom reduce the efficiency of the loom

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production technology of doris three-layer lattice fabric
  • Production technology of doris three-layer lattice fabric
  • Production technology of doris three-layer lattice fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A production process of a multi-layered three-layer lattice fabric, comprising the following process steps: winding → double twisting → section warping → drafting → temperature and humidity control → weaving, wherein:

[0033] a. Winding: Use the SGD168 type winding machine, set the winding weight to 0.7kg, the winding time to 63 minutes, and the curling force to 42CN to wind;

[0034] b. Two-for-one twisting: use the YB310G two-for-one twister, set the spindle speed to 11000r / min, increase the expansion force beads to 0.9*2 grains, and perform two-for-one twisting with a wrap angle of 360°; control the speed of rewinding and moving the screw at 7.5s, The tension is controlled at 16CN;

[0035] c. Sectional warping: set the speed of the large drum at 250m / min, the inverted axis at 60m / min, control the warping tension at 15g, and control the tension at the inverted axis at 1.5kg, and warp according to 587 grains*36 strips;

[0036] d. Wearing: See the method of wearing ...

Embodiment 2

[0040] A production process of a multi-layered three-layer lattice fabric, comprising the following process steps: winding → double twisting → section warping → drafting → temperature and humidity control → weaving, wherein:

[0041] a. Winding: Use the SGD168 type winding machine, set the winding weight to 0.7kg, the winding time to 63 minutes, and the curling force to 42CN to wind;

[0042] b. Two-for-one twisting: use the YB310G two-for-one twister, set the spindle speed to 11000r / min, increase the expansion force beads to 0.9*2 grains, and perform two-for-one twisting with a wrap angle of 360°; control the speed of rewinding and moving the screw at 7.5s, The tension is controlled at 16CN;

[0043] c. Sectional warping: set the speed of the large drum at 250m / min, the inverted axis at 60m / min, control the warping tension at 15g, and control the tension at the inverted axis at 1.5kg, and warp according to 587 grains*36 strips;

[0044] d. Wearing: See the method of wearing ...

Embodiment 3

[0048] A production process of a multi-layered three-layer lattice fabric, comprising the following process steps: winding → double twisting → section warping → drafting → temperature and humidity control → weaving, wherein:

[0049]a. Winding: Use the SGD168 type winding machine, set the winding weight to 0.7kg, the winding time to 63 minutes, and the curling force to 42CN to wind;

[0050] b. Two-for-one twisting: use the YB310G two-for-one twister, set the spindle speed to 11000r / min, increase the expansion force beads to 0.9*2 grains, and perform two-for-one twisting with a wrap angle of 360°; control the speed of rewinding and moving the screw at 7.5s, The tension is controlled at 16CN;

[0051] c. Sectional warping: set the speed of the large drum at 250m / min, the inverted axis at 60m / min, control the warping tension at 15g, and control the tension at the inverted axis at 1.5kg, and warp according to 587 grains*36 strips;

[0052] d. Wearing: See the method of wearing ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a production technology of doris three-layer lattice fabric. The production technology comprises the steps of warp treatment and weaving, wherein during weaving, the temperature of a weaving workshop is 25-26 DEG C, the humidity is 65-70%, the loom speed is 400 r / min, the height of a rear beam is 4 cm, the angle is 73 degrees, the loom tension of an upper weaving shaft is 600-670 kg*g, the loom tension of a lower weaving shaft is 250-300 kg*g, a single No.30 water pump, two No.90 sprinkler bodies and two No.40 nozzles are provided, the water outlet angle is 85-90 degrees, the water ending angle is 190-200 degrees, the angle between the water and waste side yarn is 220-230 degrees, the angle between the yarn and the waste side yarn is 240-255 degrees, the touch anglebetween the yarn and a reed is 280-295 degrees, and the heald leveling angle is 345 degrees. According to the production technology, on the basis of digesting, absorbing and improving equipment, attention is paid to solving the problems that since two raw materials with different linear densities are adopted for making weft, weft insertion is unsmooth due to differences in interweaving points ofthe warp and weft, and a loom easily stops weft making and pulls back; through the optimization of the weaving technology, the efficiency of the loom is improved, and the novel fabric which is good indyeing performance, soft in luster, and natural and attractive in color is developed.

Description

technical field [0001] The invention relates to the technical field of textile fabric production, in particular to a production process of a dori three-layer grid fabric. Background technique [0002] With the improvement of people's living standards, in addition to clothing fabrics, there are more and more requirements for textile fabrics used in interior decoration. Consumers' requirements are the market, and products that can meet consumer requirements can occupy the market. The fabric style of curved yarn double-layer lattice fabric is relatively simple, and the poor shading performance and fabric coloring are the defects of this kind of product. The design idea of ​​2050 Dori three-layer lattice fabric is based on the traditional double-layer lattice fabric. Polyester cationic yarn is used as the core yarn , using changing warp and weft interweaving methods, so that the surface weave, middle weave and inner weave of the fabric show different product styles, using curved...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D11/00D03D21/00
CPCD03D11/00D03D21/00
Inventor 吴国良茹秋利郭建洋吴保虎张浩杨照飞金丰郭海艳倪琪
Owner JIANGSU DESHUN TEXTILES