Production process of steel wire rope made from stainless steel

A production process and technology for steel wire ropes, applied in the field of steel wire ropes, can solve the problems of high strength and hardness of high carbon steel, difficult to control the wire breakage rate, affecting the use effect, etc., and achieve the effect of low wire breakage rate, simple process and high production efficiency.

Inactive Publication Date: 2019-02-19
江苏恒亿能金属科技有限公司
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Traditional steel wire ropes are usually made of high-carbon steel as raw material. High-carbon steel has high strength and hardness, and the broken wire rate is difficult to control. At the same time, once the compression rate of high-carbon steel is high during processing, the material itself The toughness will decrease, which will affect the subsequent use effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] All features disclosed in this specification, or steps in all methods or processes disclosed, may be combined in any manner, except for mutually exclusive features and / or steps.

[0012] Any feature in this specification, unless specifically stated, can be replaced by other equivalent or alternative features with similar purpose. That is, unless expressly stated otherwise, each feature is one example only of a series of equivalent or similar features.

[0013] Step 1: Pretreatment: place the stainless steel wire rod on the pay-off rack, clean it mechanically, enter the boron-coating equipment for boron-coating treatment after cleaning, and finally enter the drying equipment for drying to obtain the pretreated wire rod;

[0014] Step 2: Drawing: Put the pretreated wire rod in the drawing machine for multiple drawing, and after the drawing is completed, take up the wire to obtain the semi-finished wire rod;

[0015] Step 3: heat treatment: put the drawn semi-finished wir...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a production process, and relates to the field of steel wire ropes, in particular to a production process of a steel wire rope made from stainless steel. The production processof the steel wire rope made from the stainless steel includes the following steps of 1, pre-treatment; 2, drawing; 3, heat treatment; 4, stranding into a rope; 5, quality inspection. The design is reasonable, by means of the production process of the steel wire rope made from the stainless steel, the stainless steel is used as the raw material for processing, the production process is simple in procedure, low in energy consumption, low in wire fracture rate and high in production efficiency, and the steel wire rope is excellent in comprehensive performance.

Description

technical field [0001] The invention relates to the field of steel wire ropes, in particular to a production process for stainless steel wire ropes. Background technique [0002] Traditional steel wire ropes are usually made of high-carbon steel as raw material. High-carbon steel has high strength and hardness, and the broken wire rate is difficult to control. At the same time, once the compression rate of high-carbon steel is high during processing, the material itself The toughness will decrease, which will affect the subsequent use effect. Contents of the invention [0003] In order to solve the problems mentioned above, the present invention provides a galvanized steel wire rope processing technology, the steps of the galvanized steel wire rope processing technology include: [0004] Step 1: Pretreatment: place the stainless steel wire rod on the pay-off rack, clean it mechanically, enter the boron-coating equipment for boron-coating treatment after cleaning, and fina...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D07B1/06D07B5/00B21C1/00C21D9/52C21D9/54
CPCD07B1/066B21C1/00C21D9/525C21D9/54D07B5/005D07B5/006