Formula of pulp for producing paper straws

A pulp and straw technology, applied in natural cellulose pulp/paper, paper, papermaking and other directions, can solve the problems of unsatisfactory paper straw production technology, low strength of paper straws, affecting use, etc., to improve the utilization rate, dry High tensile strength and resource saving effect

Inactive Publication Date: 2019-02-22
浙江华丰纸业科技有限公司
View PDF7 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the production technology of paper straws in the prior art is not satisfactory, and the produced paper straws have low strength and are easy to soften after soaking in water, which directly affects people's use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Formula of pulp for producing paper straws
  • Formula of pulp for producing paper straws
  • Formula of pulp for producing paper straws

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Embodiment 1: A formula for producing pulp for paper straws, which is formed by mixing softwood pulp, hardwood pulp, recycled paper pulp and additives.

[0017] Additives include wet strength agents and sizing agents.

[0018] The additives also include defoamers, and the addition ratio is 0.5% of the total mass.

[0019] The ratio of softwood pulp, hardwood pulp and recycled paper pulp is 20:50:10.

[0020] wet strength agent wet strength agent Polyamide The polyepichlorohydrin resin is prepared, and the addition ratio is 3% of the total mass, and the sizing agent is alkyl ketene dimer, and the addition ratio is 2% of the total mass.

[0021] Wet strength agent consists of 10% of Polyamide The polyepichlorohydrin resin is mixed with 90% water, the stirring time is 10 minutes, and the stirring speed is 100rmp.

[0022] The softwood pulp is disintegrated by a pulper for 10 minutes, and the beating degree is 70°SR.

[0023] The hardwood pulp is disintegrated by a pul...

Embodiment 2

[0028] Embodiment 2: A formula for producing pulp for paper straws, which is formed by mixing softwood pulp, hardwood pulp, recycled paper pulp and additives.

[0029] Additives include wet strength agents and sizing agents.

[0030] The additives also include defoamers, and the addition ratio is 0.5% of the total mass.

[0031] The ratio of softwood pulp, hardwood pulp and recycled paper pulp is 40:80:20.

[0032] wet strength agent wet strength agent Polyamide The polyepichlorohydrin resin is prepared, and the addition ratio is 3% of the total mass, and the sizing agent is alkyl ketene dimer, and the addition ratio is 2% of the total mass.

[0033] Wet strength agent consists of 30% of Polyamide The polyepichlorohydrin resin is mixed with 70% water, the stirring time is 10 minutes, and the stirring speed is 100rmp.

[0034] The softwood pulp is disintegrated by a pulper for 5 minutes, and the beating is circulated, and the beating degree is 50°SR.

[0035] The hardwood ...

Embodiment 3

[0040] Embodiment 3: A formula for producing pulp for paper straws, which is formed by mixing softwood pulp, hardwood pulp, recycled paper pulp and additives.

[0041] Additives include wet strength agents and sizing agents.

[0042] The additives also include defoamers, and the addition ratio is 0.5% of the total mass.

[0043] The ratio of softwood pulp, hardwood pulp and recycled paper pulp is 40:80:20.

[0044] wet strength agent wet strength agent Polyamide The polyepichlorohydrin resin is prepared, and the addition ratio is 3% of the total mass, and the sizing agent is alkylketene dimer, and the addition ratio is 3% of the total mass.

[0045] Wet strength agent consists of 25% of Polyamide The polyepichlorohydrin resin is mixed with 75% water, the stirring time is 10 minutes, and the stirring speed is 150rmp.

[0046] The softwood pulp is disintegrated by a pulper for 8 minutes, and the beating is circulated, and the beating degree is 65°SR.

[0047] The hardwood p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a formula of pulp for producing paper straws. The pulp is prepared by mixing softwood pulp, hardwood pulp, recycled paper pulp and additives. Paper straws prepared from the pulphave high dry tensile strength and large dry elongation rate, has the wet tensile strength of 1Kn / m or more and wet elongation rate of 4 percent or more, cannot be softened if being soaked in water for half an hour or more, is environment-friendly, and can greatly meet the requirement of people for daily use.

Description

Technical field: [0001] The invention relates to the field of paper production, in particular to a formula for producing pulp for paper straws. Background technique: [0002] Nowadays, people's awareness of environmental protection is getting higher and higher, and the small plastic straws are difficult to be grasped by garbage disposers and then recycled. Therefore, the final fate of most plastic straws is to fall into landfills or float in on the ocean. Plastic straws that enter the waters are often eaten by sea turtles, seabirds, fish and other animals, causing the tragedies we have seen before. The plastic straws that continue to float on the sea will gradually break down, forming a large number of microplastic particles with a diameter of less than 5 mm. These toxic and harmful microplastic particles will also accumulate through the food chain and may eventually enter the human body, threatening human health. [0003] But the production technology of paper straw in t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H11/00D21H11/14D21H15/10D21H17/17D21H17/55D21H21/12D21H21/16D21H21/20
CPCD21H11/00D21H11/14D21H15/10D21H17/17D21H17/55D21H21/12D21H21/16D21H21/20
Inventor 周家俊邹小峰刘敏刘言林少鸣杨晓林包红慧
Owner 浙江华丰纸业科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com