Method for preparing novel casting composite binder

A composite adhesive, a new type of technology, applied in the direction of casting molding equipment, casting molds, cores, etc., can solve the problems of low core yield, low dry tensile strength, poor bonding effect, etc., to achieve excellent product performance, The effect of high dry tensile strength and short roasting time

Inactive Publication Date: 2013-10-02
江苏中丽新材料有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the existing casting composite adhesives are usually made of synthetic grease, but the adhesives using the above method have poor performance, low dry tensile strength, poor bonding effect, and low core yield.
At the same time, the existing adhesives are prone to a large amount of smoke and toxic odor during the drying and pouring process, causing environmental pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] The preparation method of novel foundry composite adhesive comprises the following steps:

[0012] (1) Mix and stir 20 parts of epoxy resin, 10 parts of fatty acid ester and 30 parts of water in parts by weight, heat up to 80°C, and hold for 1 hour;

[0013] (2) Add 5 parts by weight of hydrochloric acid and 10 parts of methanol to the mixed material in the step (1), stir evenly, and cool to 50°C, holding time for 0.5 hours;

[0014] (3) Add 10 parts by weight of talcum powder to the mixed material in the step (2), stir evenly, and then cool naturally to obtain the product.

Embodiment 2

[0016] The preparation method of novel foundry composite adhesive comprises the following steps:

[0017] (1) Mix and stir 30 parts of epoxy resin, 15 parts of fatty acid ester and 40 parts of water in parts by weight, heat up to 85°C, and hold for 1.5 hours;

[0018] (2) Add 8 parts by weight of hydrochloric acid and 15 parts of methanol to the mixed material in the step (1), stir evenly, and cool to 60°C, holding time for 0.8 hours;

[0019] (3) Add 20 parts by weight of talcum powder to the mixed material in the step (2) and stir evenly, then cool naturally to obtain the finished product.

Embodiment 3

[0021] The preparation method of novel foundry composite adhesive comprises the following steps:

[0022] (1) Mix and stir 40 parts of epoxy resin, 20 parts of fatty acid ester and 50 parts of water in parts by weight, heat up to 90°C, and hold for 2 hours;

[0023] (2) Add 10 parts by weight of hydrochloric acid and 20 parts of methanol to the mixed material in the step (1), stir evenly, and cool to 70°C, holding time for 1 hour;

[0024] (3) Add 30 parts by weight of talcum powder to the mixed material in the step (2) and stir evenly, then cool naturally to obtain the product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of composite binders and particularly relates to a method for preparing a novel casting composite binder. The method comprises the following steps of: (1) mixing and stirring 20-40 parts (by weight) of epoxy resin, 10-20 parts (by weight) of fatty acid ester and 30-50 parts (by weight) of water, heating up to the temperature of 80-90 DEG C, and carrying out heat preservation for 1-2 hours; and (2) adding 5-10 parts (by weight) of hydrochloric acid and 10-20 parts (by weight) of methanol to the mixture obtained in the step (1), uniformly stirring, cooling down to the temperature of 50-70 DEG C, and carrying out heat preservation for 0.5-1 hours. The product of the method is excellent in performance, high in dry tensile strength and can be universally used in a manner of replacing compound fatty oil in the prior art; firstly, after wet core sand using the product is released, in the process of drying and moving, a geometric switch does not change, and the yield of cores can be increased to 98% compared with that of the prior art; secondly, the core drying temperature is low, the roasting time is short, energy sources are saved, the scattering performance after pouring is good, and the sand removal is very easy; and finally, the reduction of environmental pollution and improvement on work environment are facilitated.

Description

technical field [0001] The invention relates to the technical field of composite adhesives, in particular to a preparation method of a novel foundry composite adhesive. Background technique [0002] At present, the existing casting composite adhesives are usually made of synthetic grease, but the adhesives using the above method have poor performance, low dry tensile strength, poor bonding effect, and low core yield. At the same time, the existing adhesives are prone to produce a large amount of smoke and toxic smell during the drying and pouring process, causing environmental pollution. Contents of the invention [0003] The purpose of the present invention is to provide a preparation method of a new casting composite adhesive with excellent performance, high dry tensile strength, high core yield, non-toxic, tasteless and beneficial to improve the working environment. [0004] In order to solve the existing problems of the background technology, the present invention ado...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22C1/24B22C1/22
Inventor 胡浩
Owner 江苏中丽新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products