Strengthened type nanometer WC/AlSi10Mg composite powder and additive manufacturing technology

A composite material and additive manufacturing technology, which is applied in the field of additive manufacturing, can solve problems such as inappropriateness, and achieve the effects of good sphericity, uniform growth, and good application prospects

Inactive Publication Date: 2019-03-08
NANCHANG UNIV
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the modern industry is increasingly looking for lightweight materials with high strength and stiffn...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Strengthened type nanometer WC/AlSi10Mg composite powder and additive manufacturing technology
  • Strengthened type nanometer WC/AlSi10Mg composite powder and additive manufacturing technology
  • Strengthened type nanometer WC/AlSi10Mg composite powder and additive manufacturing technology

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032] All features disclosed in this specification, or steps in all methods or processes disclosed, may be combined in any manner, except for mutually exclusive features and / or steps.

[0033] Any feature disclosed in this specification (including any appended claims, abstract and drawings), unless expressly stated otherwise, may be replaced by alternative features which are equivalent or serve a similar purpose. That is, unless expressly stated otherwise, each feature is one example only of a series of equivalent or similar features.

[0034] The present invention will be described in further detail below in conjunction with the examples, but the implementation of the present invention is not limited thereto.

[0035] The technical solution of the present invention will be further described below through specific embodiments.

[0036] The embodiment provides a kind of reinforced nano-WC / AlSi10Mg composite material powder and additive manufacturing process:

[0037] Add 0.1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses strengthened type nanometer WC/AlSi10Mg composite powder and an additive manufacturing technology and belongs to the technical field of additive manufacturing. The additive manufacturing technology comprises the following steps of adding 0.1 percent of nanometer WC in AlSi10Mg powder, performing mixing on the two powders for 20min with a GH-17 type three-dimensional motionefficient mixer, and then performing drying for 10h with a vacuum drying tank to obtain the strengthened type nanometer WC/AlSi10Mg composite powder. The composite powder has the characteristics of better mobility, high sphericity degree, high printing stability and the like; and by melting and solidifying the composite powder with laser, the plasticity of AlSi10Mg alloy is improved while the strength of the AlSi10Mg is improved.

Description

technical field [0001] The invention relates to the technical field of additive manufacturing, and more specifically relates to enhanced nano-WC / AlSi10Mg composite material powder and an additive manufacturing process. Background technique [0002] AlSi10Mg alloy has the advantages of low density, good corrosion resistance and high specific strength, which make it widely used in aerospace, automobile and heat exchange equipment. AlSi10Mg alloy parts produced by SLM have close to full density and have excellent mechanical properties compared with materials produced by conventional casting processes. However, modern industry is increasingly looking for lightweight materials with high strength and stiffness, and traditional processing materials are far from suitable for current and future SLM industrial applications. Therefore, there is a need to find a novel composite material for industrial applications. Particle-reinforced aluminum matrix composites can be widely used in v...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F1/00B22F3/105B33Y70/00B33Y10/00C22C21/02C22C32/00
CPCB22F1/0003C22C21/02C22C32/0052B33Y10/00B33Y70/00B22F10/00B22F10/32B22F10/34B22F10/366B22F10/36B22F10/38B22F10/28Y02P10/25
Inventor 叶寒黄俊强张坚强孙旭朱晋姝刘勇
Owner NANCHANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap