An adhesive and soft porcelain technology, which is applied in the field of chemical building materials, can solve the problems of affecting the beauty of soft porcelain paving, lack of soft porcelain binder, and weak pasting. The effect of pantothenic ability

Active Publication Date: 2020-05-08
广西里尔新材料有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the process of tile laying, it is necessary to use adhesives, and the existing tile adhesives are mainly for laying ceramic tiles, and there are basically no special adhesives for soft porcelain
However, because soft porcelain has the characteristics of soft deformability and smooth back, which are different from ceramics, using existing tile adhesives to pave soft porcelain is prone to problems such as weak adhesion and alkali return on the wall, which not only affects the quality of soft porcelain The beauty of paving also has certain safety hazards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A special binder for soft porcelain

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A special binder for soft porcelain, which is mainly made by mixing and stirring component A and component B at a weight ratio of 4:1; the component A includes the following raw material components in parts by weight: 0.02 parts of defoaming agent, fiber 0.2 part of plain ether, 0.1 part of calcium formate, 50 parts of quartz sand and 25 parts of modified industrial inorganic powder; the B component is an acrylic acid emulsion; the modified industrial inorganic powder includes the following raw material components in parts by weight: calcium carbonate 10 parts, 5 parts of talcum powder and 0.5 part of kaolin;

[0021] The modified industrial inorganic powder is prepared by the following method: in parts by weight, 10 parts of calcium carbonate, 5 parts of talcum powder and 0.5 part of kaolin are weighed, and the weighed calcium carbonate, talcum powder and kaolin are respectively pulverized to the 150 mesh sieve; mix and stir the pulverized calcium carbonate and deioniz...

Embodiment 2

[0027] A special binder for soft porcelain, which is mainly made by mixing and stirring component A and component B at a weight ratio of 4:1; the component A includes the following raw material components in parts by weight: 0.03 parts of defoaming agent, fiber 0.3 part of plain ether, 0.2 part of calcium formate, 60 parts of quartz sand and 32 parts of modified industrial inorganic powder; the B component is an acrylic acid emulsion; the modified industrial inorganic powder includes the following raw material components in parts by weight: calcium carbonate 12 parts, 7 parts of talcum powder and 1.2 parts of kaolin;

[0028] The modified industrial inorganic powder is prepared by the following method: in parts by weight, 12 parts of calcium carbonate, 7 parts of talcum powder and 1.2 parts of kaolin are weighed, and the weighed calcium carbonate, talcum powder and kaolin are respectively pulverized to the 150-mesh sieve; mix and stir the pulverized calcium carbonate and deion...

Embodiment 3

[0034]A special binder for soft porcelain, which is mainly made by mixing and stirring component A and component B at a weight ratio of 4:1; the component A includes the following raw material components in parts by weight: 0.04 parts of defoaming agent, fiber 0.5 part of plain ether, 0.3 part of calcium formate, 65 parts of quartz sand and 35 parts of modified industrial inorganic powder; the B component is an acrylic acid emulsion; the modified industrial inorganic powder includes the following raw material components in parts by weight: calcium carbonate 15 parts, 8 parts of talcum powder and 1.5 parts of kaolin;

[0035] The modified industrial inorganic powder is prepared by the following method: in parts by weight, weigh 15 parts of calcium carbonate, 8 parts of talcum powder and 1.5 parts of kaolin, and pulverize the weighed calcium carbonate, talcum powder and kaolin to the 150 mesh sieve; mix and stir the pulverized calcium carbonate and deionized water at a weight ra...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of chemical building materials and in particular discloses a special ceramic adhesive which is mainly prepared from a component A and a component B in a weight ratio of 4:1 through mixing and stirring, wherein the component A comprises the following raw material components in parts by weight: 0.02-0.04 part of a defoaming agent, 0.2-0.5 part of cellulose ether, 0.1-0.3 part of calcium formate, 50-65 parts of quartz sand and 25-35 parts of modified industrial inorganic powder; the component B is an acrylic emulsion. The special ceramic adhesive disclosed by the invention has good adhesion properties and temperature resistance, is wide in base surface applicability and good in anti-whiskering property, and is capable of effectively improving the solidness of soft ceramic pasting.

Description

【Technical field】 [0001] The invention relates to the technical field of chemical building materials, in particular to a special binder for soft porcelain. 【Background technique】 [0002] Soft porcelain is a new type of building decoration material. It uses modified soil as the main raw material, and is a flexible building decoration surface material formed by a special temperature-controlled molding system, baked, and irradiated. With strong expressive force, it can not only realistically express the color and texture of existing materials such as stone, ceramics, wood, leather, knitting, metal plate, weaving, etc., but also create personalized forms of expression according to individual design requirements. [0003] In the process of laying ceramic tiles, adhesives are needed, but the existing tile adhesives are mainly for laying ceramic tiles, and there is basically no special adhesive for soft porcelain. However, because soft porcelain has the characteristics of soft de...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B26/28
CPCC04B26/285C04B2111/00637C04B2201/50C04B2103/50C04B24/04C04B14/06C04B14/28C04B14/042C04B14/106C04B24/2641
Inventor 邹先强
Owner 广西里尔新材料有限公司