a tile adhesive

A technology for bonding glue and tiles, applied in the field of chemical building materials, can solve problems such as affecting the aesthetics of soft porcelain paving, lack of soft porcelain adhesive, and weak pasting, etc., and achieves easy construction and operation, firm adhesion, and strong resistance to panning. The effect of alkalinity

Active Publication Date: 2020-05-08
广西里尔新材料有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the process of laying ceramic tiles, adhesives are required, but the existing adhesives for tiles are mainly for laying ceramic tiles, and there are basically no adhesives for soft porcelain
However, because soft porcelain has the characteristics of soft deformability and smooth back, which are different from ceramics, using existing tile adhesives to pave soft porcelain is prone to problems such as weak adhesion and alkali return on the wall, which not only affects the quality of soft porcelain The beauty of paving also has certain safety hazards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • a tile adhesive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A tile adhesive, which is mainly made by mixing and stirring component A and component B at a weight ratio of 4:1; the component A includes the following raw material components in parts by weight: 0.02 parts of simethicone, cellulose 0.2 part of ether, 0.1 part of calcium formate, 50 parts of quartz sand and 20 parts of modified industrial inorganic powder; the B component is an acrylic acid emulsion; the modified industrial inorganic powder includes the following raw material components in parts by weight: 15 parts of bentonite , 5 parts of talcum powder and 1 part of silica lime;

[0022] The preparation method of the modified industrial inorganic powder is as follows: in parts by weight, weigh 15 parts of bentonite, 5 parts of talcum powder and 1 part of silica lime, and pulverize the weighed bentonite, talcum powder and silica lime for 150 Mesh sieve; after mixing bentonite and silica lime, add deionized water and stir evenly to obtain a slurry with a mass concentr...

Embodiment 2

[0025] A tile adhesive, which is mainly made by mixing and stirring component A and component B at a weight ratio of 4:1; the component A includes the following raw material components in parts by weight: 0.03 parts of defoaming agent, cellulose ether 0.4 parts, 0.2 parts of calcium formate, 55 parts of quartz sand and 25 parts of modified industrial inorganic powder; the B component is an acrylic acid emulsion; the modified industrial inorganic powder includes the following raw material components in parts by weight: 18 parts of bentonite, 7 parts of talcum powder and 1.5 parts of silica lime;

[0026] The preparation method of the modified industrial inorganic powder is as follows: in parts by weight, weigh 18 parts of bentonite, 7 parts of talcum powder and 1.5 parts of silica lime, and pulverize the weighed bentonite, talcum powder and silica lime for 150 Mesh sieve; after mixing bentonite and silica lime, add deionized water and stir evenly to obtain a slurry with a mass ...

Embodiment 3

[0029] A tile adhesive, which is mainly made by mixing and stirring component A and component B at a weight ratio of 4:1; the component A includes the following raw material components in parts by weight: 0.04 parts of polysiloxane, cellulose 0.5 part of ether, 0.3 part of calcium formate, 65 parts of quartz sand and 30 parts of modified industrial inorganic powder; the B component is an acrylic acid emulsion; the modified industrial inorganic powder includes the following raw material components in parts by weight: 20 parts of bentonite , 10 parts of talcum powder and 3 parts of silica lime;

[0030]The preparation method of the modified industrial inorganic powder is as follows: in parts by weight, weigh 20 parts of bentonite, 10 parts of talcum powder and 3 parts of silica lime, and pulverize the weighed bentonite, talcum powder and silica lime for 150 parts respectively. Mesh sieve; after mixing bentonite and silica lime, add deionized water and stir evenly to obtain a slu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of chemical building materials, and particularly discloses a ceramic tile adhesive. The ceramic tile adhesive is prepared from mixing and stirring a component A and a component B according to the weight ratio being 4:1; the component A is prepared from, by weight, 0.02-0.04 part of defoaming agent, 0.2-0.5 part of cellulose ether, 0.1-0.3 part of calcium formate, 50-65 parts of silica sand and 20-30 parts of modified industrial inorganic powder; the component B is acrylic emulsion; the modified industrial inorganic powder is prepared from, by weight, 15-20 parts of bentonite, 5-10 parts of talcum powder and 1-3 parts of silicon limestone. The ceramic tile adhesive has the good bonding performance and the impact resistance and can effectively improve the soft ceramic paving firmness degree.

Description

【Technical field】 [0001] The invention relates to the technical field of chemical building materials, in particular to a tile adhesive. 【Background technique】 [0002] With the development of the national economy, people's requirements for architectural beauty are getting higher and higher, and the use of wall decoration materials is becoming more and more common. Among them, soft porcelain is more and more popular because of its strong form of expression. [0003] Soft porcelain is a new type of building decoration material, which uses modified soil as the main raw material, and is a flexible building decoration surface material formed by a special temperature-controlled molding system, baked, and irradiated and cross-linked. [0004] In the process of laying ceramic tiles, adhesives are needed, but the existing tile adhesives are mainly for laying ceramic tiles, and there is basically no special adhesive for soft porcelain. However, because soft porcelain has the characte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More